Fire barrier coating and fire barrier plywood
Assignee: INTERNATIONAL BARRIER TECHNOLOGY Inc
•
Filing: 1987-04-24
•
Granted: 1989-04-04
•
Expires: 2007-04-24
Abstract
Abstract A novel, non-combustible thin coating, applied as an air-setting paint, is used to form a coherent fire-barrier on or between susceptible wood or plastic substrates, or other substances. Consisting of a paint-like slurry of three separate but compatible and mutually synergistic co-bonding systems, viz. magnesium "oxychloride" cement, plus high alumina mono-calcium aluminate cement, plus colloidal silica dispersed in dimethyl formamide (DMF), and utilizing an aqueous solution of magnesium chloride as the common hydrating fluid for the two cements, the coating retains its structural integrity through prolonged exposure to flame temperatures of 2000° F. The coating takes advantage of its brilliant whiteness to act as a thermal radiation reflector for the high radiation component of most flames. Used alone, or in combination with structural reinforcing geotextiles, such as non-woven spunbonded polyester fabric, or woven and non-woven fiberglass or other natural or synthetic fabrics to form a laminate, the coating, while serving only transitorily as a heat barrier, effectively prevents the ignition of and flame spread of fire on the coated substrate. When placed between substrates at the partial sacrifice of the surface directly exposed to flame, it protects the back-substrate, and thus maintains structural integrity, as well as preventing the spread of flame to adjacent areas. The coating thus acts as a "fire-barrier" for which there are numerous applications.
Inventors
- 👤 Harold Ellis
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 01:44
CPC Classifications
C; C04; C04B; C04B28/00; C04B28/02; C04B28/30; C04B41/00; C04B41/009; C04B41/45; C04B41/50; C04B41/5076; C04B41/509; C09; C09D; C09D5/00; C09D5/18; Y; Y10; Y10S; Y10S428/00; Y10S428/92; Y10S428/921; Y10T; Y10T442/00; Y10T442/20; Y10T442/2041; Y10T442/2049; Y10T442/2057; Y10T442/2074; Y10T442/2631; Y10T442/2926; Y10T442/2992
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
88 words
A fire resistant composition comprising a hardened, substantially uniform dispersion of: (A) a binder component comprising a substantially uniform mixture of (1) heat activated MgO, and (2) high-alumina calcium aluminate cement comprising 70% to 80% Al 2 O 3 cured with; (B) a gauging component in about a stoichiometric amount sufficient to react with said binder component, wherein the gauging component is derived from an aqueous solution of M g Cl 2 or M g SO 4 having a specific gravity of about 26° to about 32° Baume.
Claim 2
Dependent Claim
88 words
A fire resistant composition comprising a hardened, substantially uniform dispersion of: (A) a binder component comprising a substantially uniform mixture of (1) heat activated MgO, and (2) high-alumina calcium aluminate cement comprising 70% to 80% Al 2 O 3 cured with; (B) a gauging component in about a stoichiometric amount sufficient to react with said binder component, wherein the gauging component is derived from an aqueous solution of M g Cl 2 or M g SO 4 having a specific gravity of about 26° to about 32° Baume.
Claim 3
Dependent Claim
14 words
Composition according to claim 1 in which the binder component includes TiO 2 .
Claim 4
Dependent Claim
16 words
Composition according to claim 1 in which the binder component includes alumina trihydrate as a filler.
Claim 5
Dependent Claim
15 words
Composition according to claim 1 in which the binder component includes vermiculite as a filler.
Claim 6
Dependent Claim
16 words
Composition according to claim 1 in which the binder component includes silica flour as a filler.
Claim 7
Dependent Claim
44 words
Composition according to claim 1 in which the gauging component includes a colloidal dispersion of colloidal silica in dimethyl formamide, said component serving also as a co-binder cement along with M g O and M g Cl 2 cement and high-alumina calcium aluminate cement.
Claim 8
Dependent Claim
16 words
A solid substrate having a coating thereon, wherein the coating comprises the composition of claim 1.
Claim 9
Dependent Claim
12 words
Coated substrate according to claim 7 wherein the substrate is laminated plywood.
Claim 10
Dependent Claim
12 words
Coated substrate according to claim 7 wherein the substrate is wood panelling.
Claim 11
Dependent Claim
14 words
Coated substrate according to claim 7 wherein the substrate is comprised of compressed fiberglass.
Claim 12
Dependent Claim
14 words
Coated substrate according to claim 7 wherein the substrate is comprised of woven fiberglass.
Claim 13
Dependent Claim
22 words
Coated substrate according to claim 7 wherein the substrate is a non-woven spunbonded polyester fabric or a woven or non-woven fiberglass fabric.
Claim 14
Dependent Claim
23 words
Coated substrate according to claim 12 in which said fabric has opposing sides and each side of said fabric has said coating thereon.
Claim 15
Independent Claim
138 words
A method of making a fire resistant composition comprising: (A) preparing a substantially dry, powdered binder component comprising (1) heat activated M g O, and (2) high-alumina calcium aluminate cement comprising 70% to 80% Al 2 O 3 ; (B) preparing a gauging component comprising an aqueous solution of M g Cl 2 or M g SO 4 , wherein the aqueous solution has a specific gravity of about 26° to about 32° Baume; (C) gradually adding said binder component to said gauging component with mixing to substantially uniformly disperse said binder component in said gauging component to form a slurry; and (D) reacting the gauging component with the binder component to permit the slurry to set into a hard monolithic refractory; wherein said gauging component is employed in about a stoichiometric amount relative to said binder component.
Claim 16
Independent Claim
138 words
A method of making a fire resistant composition comprising: (A) preparing a substantially dry, powdered binder component comprising (1) heat activated M g O, and (2) high-alumina calcium aluminate cement comprising 70% to 80% Al 2 O 3 ; (B) preparing a gauging component comprising an aqueous solution of M g Cl 2 or M g SO 4 , wherein the aqueous solution has a specific gravity of about 26° to about 32° Baume; (C) gradually adding said binder component to said gauging component with mixing to substantially uniformly disperse said binder component in said gauging component to form a slurry; and (D) reacting the gauging component with the binder component to permit the slurry to set into a hard monolithic refractory; wherein said gauging component is employed in about a stoichiometric amount relative to said binder component.
Claim 17
Dependent Claim
20 words
Method according to claim 14 wherein said binder component contains silica flour and titanium dioxide as substantially dry powdered fillers.
Claim 18
Dependent Claim
26 words
Method according to claim 14 wherein the gauging component is reacted with the binder component for a time sufficient to form a hardened, fire resistant composition.
Claim 19
Dependent Claim
37 words
Method according to claim 14 wherein said binder component contains a filler selected from the group consisting of sand, gravel, crushed rock, silica flour, pumice, vermiculite, volcanic ash, perlite, wood shavings, sugarcane bagasse, asbestos, and mineral fibers.
Claim 20
Dependent Claim
17 words
Method according to claim 14 wherein said binder component contains alumina trihydrate as a fire retardant filler.
Claim 21
Dependent Claim
17 words
Method according to claim 14 wherein said binder component contains expanded vermiculite as a fire retardant filler.
Claim 22
Dependent Claim
21 words
Method according to claim 14 in which a colloidal dispersion of silica in dimethyl formamide is added to said aqueous solution.
Claim 23
Dependent Claim
57 words
Method according to claim 20 comprising slowly adding a sodium tetradecyl sulphate anionic surfactant to said aqueous solution, gradually adding said colloidal silica dispersion to the resulting surfactant-containing solution to form an opalescent dispersion, and then gradually adding said binder component to said opalescent dispersion with mixing to substantially completely wet particles of said powdered binder component.
References Cited (Backward Citations)
US3811992A
Cited
US3745031A
Cited
US3778304A
Cited
US3963849A
Cited
CA957455A
Cited
US4097422A
Cited
US3956538A
Cited
US4088804A
Cited
US4159302A
Cited
GB1561271A
Cited
US4255483A
Cited
US4312674A
Cited
US4315967A
Cited
US4462831A
Cited
US4410366A
Cited
US4572862A
Cited
US4661398A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-04-03 | 1992-10-03 | 1993-04-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-04-03 | 1996-10-03 | 1997-04-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-04-03 | 2000-10-03 | 2001-04-04 | $7700.00 | Window Closed / Lapsed |