Process for producing toner through suspension polymerization
Assignee: Canon Inc
•
Filing: 1988-02-12
•
Granted: 1989-03-28
•
Expires: 2008-02-12
Abstract
Abstract A toner for developing electrostatic latent images is produced by a process comprising the steps of: (a) stirring at least water, hardly water-soluble inorganic fine powder and a specific compound thereby to prepare an aqueous dispersion medium; (b) adding a polymerizable monomer composition comprising at least a polymerizable monomer and a polymerization initiator to the aqueous dispersion medium; (c) forming particles of the polymerizable monomer composition in the aquoeus dispersion medium; (d) subjecting the particles of the polymerizable monomer composition to suspension polymerization, thereby to produce toner particles; and (e) removing the hardly water-soluble inorganic fine powder attached to the surfaces of the toner particles by an aqueous alkaline or acidic solution.
Inventors
- 👤 Yoshihiko Hyosu
- 👤 Takeshi Ikeda
- 👤 Hitoshi Kanda
- 👤 Hiromi Mori
- 👤 Hiroaki Kawakami
- 👤 Kuniko Kobayashi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 14:46
CPC Classifications
G; G03; G03G; G03G9/00; G03G9/08; G03G9/0802; G03G9/0804; G03G9/0806; G03G9/0815; G03G9/087; G03G9/08702
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
131 words
A process for producing a toner through suspension polymerization, comprising: (a) stirring at least water, hardly water-soluble inorganic fine powder and a compound selected from the group consisting of a silane coupling agent, a titanate-type coupling agent, an aluminate-type coupling agent, a zircoaluminate-type coupling agent and hydrolysis products thereof, thereby to prepare an aqueous dispersion medium; (b) adding a polymerizable monomer composition comprising at least a polymerizable monomer and a polymerization initiator to the aqueous dispersion medium; (c) forming particles of the polymerizable monomer composition in the aqueous dispersion medium; (d) subjecting the particles of the polymerizable monomer composition to suspension polymerization, thereby to produce toner particles; and (e) removing the hardly water-soluble inorganic fine powder attached to the surfaces of the toner particles by an aqueous alkaline or acidic solution.
Claim 2
Dependent Claim
131 words
A process for producing a toner through suspension polymerization, comprising: (a) stirring at least water, hardly water-soluble inorganic fine powder and a compound selected from the group consisting of a silane coupling agent, a titanate-type coupling agent, an aluminate-type coupling agent, a zircoaluminate-type coupling agent and hydrolysis products thereof, thereby to prepare an aqueous dispersion medium; (b) adding a polymerizable monomer composition comprising at least a polymerizable monomer and a polymerization initiator to the aqueous dispersion medium; (c) forming particles of the polymerizable monomer composition in the aqueous dispersion medium; (d) subjecting the particles of the polymerizable monomer composition to suspension polymerization, thereby to produce toner particles; and (e) removing the hardly water-soluble inorganic fine powder attached to the surfaces of the toner particles by an aqueous alkaline or acidic solution.
Claim 3
Dependent Claim
42 words
A process according to claim 1, wherein the hardly water-soluble inorganic fine powder is added to water and stirred, and then said compound is added to the water cotaining the inorganic fine powder and stirred, thereby to prepare the aqueous dispersion medium.
Claim 4
Dependent Claim
32 words
A process according to claim 1, wherein said hydrolysis product is prepared by mixing the silane coupling agent, the titanate-type coupling agent, the aluminate-type coupling agent or zircoaluminate-type coupling agent, with water.
Claim 5
Dependent Claim
19 words
A process according to claim 1, wherein said compound is the silane coupling agent or the hydrolysis product thereof.
Claim 6
Dependent Claim
19 words
A process according to claim 4, wherein said compound is a nitrogen-containing silane coupling agent having an alkoxy group.
Claim 7
Dependent Claim
26 words
A process according to claim 5, wherein the silane coupling agent comprises a compound selected from the group consisting of γ-(2-aminoethyl)aminopropyltrimethoxysilane, γ-(2-aminoethyl)aminopropylmethyldimethoxysilane, octadecyldimethyl[3-(trimethoxysilyl)propyl]ammonium chloride, and γ-aminopropyltriethoxysilane.
Claim 8
Dependent Claim
26 words
A process according to claim 1, wherein the hardly water-soluble inorganic fine powder has a solubility of 100 mg or less in 100 g of water.
Claim 9
Dependent Claim
26 words
A process according to claim 7, wherein the hardly water-soluble inorganic fine powder has a solubility of 50 mg or less in 100 g of water.
Claim 10
Dependent Claim
54 words
A process according to claim 8, wherein the hardly water-soluble inorganic fine powder comprises an inorganic compound selected from the group consisting of barium carbonate (BaCO 3 ), calcium carbonate (CaCO 3 ), calcium phosphate (Ca 3 (PO 4 ) 2 ), colloidal silica, aluminum oxide (Al 2 O 3 ), and titanium oxide.
Claim 11
Dependent Claim
29 words
A process according to claim 1, wherein the aqueous dispersion medium is used in an amount of 200-1000 wt. parts, per 100 wt. parts of the polymerizable monomer composition.
Claim 12
Dependent Claim
36 words
A process according to claim 1, wherein the hardly water-soluble inorganic fine powder is added to the aqueous dispersion medium in an amount of 1-20 wt. %, based on the weight of the polymerizable monomer composition.
Claim 13
Dependent Claim
36 words
A process according to claim 11, wherein the hardly water-soluble inorganic fine powder is added to the aqueous dispersion medium in an amount of 3-10 wt. %, based on the weight of the polymerizable monomer composition.
Claim 14
Dependent Claim
14 words
A process according to claim 1, wherein the polymerizable monomer comprises a vinyl monomer.
Claim 15
Dependent Claim
16 words
A process according to claim 13, wherein the polymerizable monomer comprises styrene or a styrene derivative.
Claim 16
Dependent Claim
26 words
A process according to claim 13, wherein the polymerizable monomer comprises a mixture of styrene and an alkyl acrylate, an alkyl methacrylate, or an alkyl maleate.
Claim 17
Dependent Claim
21 words
A process according to claim 1, wherein the aqueous dispersion medium is stirred by means of a high shearing force stirrer.
Claim 18
Dependent Claim
23 words
A process according to claim 1, wherein the polymerizable monomer composition comprises a polymerizable monomer, colorant or magnetic powder, and a polymerization initiator.
Claim 19
Dependent Claim
51 words
A process according to claim 1, wherein colloidal silica is mixed with water to prepare a silica dispersion, a silane coupling agent diluted with water is added to the silica dispersion and stirred to prepare an aqueous dispersion medium, and a Broensted acid is further added to the aqueous dispersion medium.
Claim 20
Dependent Claim
13 words
A process according to claim 18, wherein the Broensted acid comprises hydrochloric acid.
Claim 21
Dependent Claim
79 words
A process according to claim 18, wherein the aqueous dispersion medium is mixed with a polymerizable monomer composition which comprses a polymerizable monomer, colorant or magnetic powder, a polymerization initiator, and an anionic polymer, an anionic copolymer or cyclized rubber, by means of a high shearing force stirrer; the resultant mixture is subjected to suspension polymerization to prepare toner particles; and the colloidal silica attached to the surfaces of the toner particles is removed by an aqueous alkaline solution.
Claim 22
Dependent Claim
22 words
A process according to claim 20, wherein the aqueous alkaline solution is prepared by adding sodium hydroxide to the aqueous dispersion medium.
Claim 23
Dependent Claim
29 words
A process according to claim 21, wherein the sodium hydroxide is used in an amount of more than 1 to 3.5 equivalents, per 1 equivalent of the colloidal silica.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-03-27 | 1992-09-26 | 1993-03-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-03-27 | 1996-09-26 | 1997-03-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-03-27 | 2000-09-26 | 2001-03-28 | $7700.00 | Window Closed / Lapsed |