Abstract A hybrid composite material is constructed from woven reinforced fabrics of Kevlar 49 and biaxially reinforced fibers of graphite and E-Glass bonded together with a thermosetting adhesive, for the application of custom orthotics. The material is designed with the idea of introducing different fibers at different locations of the orthotic in order to take advantage of the unique properties of each reinforcing fibers. The resulting material creates a hybrid composite that exhibits a balance of properties, in both the longitudinal and transverse directions, unavailable with any single reinforcing fibers. A method of orthotic manufacturing involves a hand lay-up and forming procedure. The constructed composite material is formed and pressed on a prescribed cast, then allowed to cure under pressure. The post-cured material is stripped from the cast, then cut and ground and finally finished to the required orthotic. The produced orthotic combines the desired feature of a thin section with excellent combination of properties relevant to custom orthotics. Such properties include light weight, high strength and modulus, excellent resistance to impact, fatigue, and creep, and outstanding ability to damp vibrations.
A method of forming a custom orthotic device comprising the steps of: (a) cutting selected fiber fabrics and release fabrics to a predetermined size; (b) preparing a prescribed plaster cast; (c) layering the selected fiber and release fabrics to form a lay-up in a predetermined order including a thermosetting adhesive between the layers of fiber fabrics, said fiber fabrics including graphite fibers oriented downwardly as the fabrics are layered; (d) rolling the lay-up with a roller to gently diffuse the adhesive between the layers; (e) forming the lay-up on the cast with graphite fibers adjacent the cast and extending coaxially with the longitudinal axis of the cast, then stretching a first fabric substantially over the entire surface of the cast and securing the first fabric to sustain substantially uniform pressure to the lay-up on the cast, and finally stretching a second fabric substantially over the first fabric at an arch area of the surface of the cast and securing the second fabric to sustain substantially uniform pressure to the lay-up on the cast; (f) pressing the lay-up with finger pressure to conform to the cast; (g) curing the lay-up for a predetermined period of time; (h) removing the cured lay-up from the cast; (i) trimming excess lay-up material from the cured lay-up to a predetermined shape; and (j) grinding edge surfaces of the trimmed lay-up to prescribed finished dimensions to form the orthotic device.
Claim 2
Independent Claim
234 words
A method of forming a custom orthotic device comprising the steps of: (a) cutting selected fiber fabrics and release fabrics to a predetermined size; (b) preparing a prescribed plaster cast; (c) layering the selected fiber and release fabrics to form a lay-up in a predetermined order including a thermosetting adhesive between the layers of fiber fabrics, said fiber fabrics including graphite fibers oriented downwardly as the fabrics are layered; (d) rolling the lay-up with a roller to gently diffuse the adhesive between the layers; (e) forming the lay-up on the cast with graphite fibers adjacent the cast and extending coaxially with the longitudinal axis of the cast, then stretching a first fabric substantially over the entire surface of the cast and securing the first fabric to sustain substantially uniform pressure to the lay-up on the cast, and finally stretching a second fabric substantially over the first fabric at an arch area of the surface of the cast and securing the second fabric to sustain substantially uniform pressure to the lay-up on the cast; (f) pressing the lay-up with finger pressure to conform to the cast; (g) curing the lay-up for a predetermined period of time; (h) removing the cured lay-up from the cast; (i) trimming excess lay-up material from the cured lay-up to a predetermined shape; and (j) grinding edge surfaces of the trimmed lay-up to prescribed finished dimensions to form the orthotic device.
Claim 3
Dependent Claim
16 words
The method claim 1 wherein the lay-up is cured at room temperature for about twenty-four hours.
Claim 4
Dependent Claim
19 words
The method of claim 1 wherein the lay-up is cured at about 110 degrees C. for about eight hours.
Claim 5
Dependent Claim
21 words
The method of claim 1 including the step of: attaching a heel post to a heel portion of the orthotic device.