Sulfide thin film formed from stabilized metallo-organic solution
Assignee: Motors Liquidation Co
•
Filing: 1988-05-02
•
Granted: 1989-03-14
•
Expires: 2008-05-02
Abstract
Abstract A metal sulfide thin film, such as a zinc sulfide thin film, is formed by thermal decomposition of a metal mercaptide or other suitable metallo-organic compound having a metal-to-sulfur bond. To produce the film, the metallo-organic compound is applied to a substrate in a solution that also contains a sulfur to facilitate dissolution of the compound and enhance stability of the solution. It is also found that sulfur addition reduces carbon contamination of the product sulfide thin film.
Inventors
- 👤 Adolph L. Micheli
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 20:45
CPC Classifications
C; C23; C23C; C23C18/00; C23C18/02; C23C18/12; C23C18/1204; C23C18/125; C23C18/1275
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
82 words
A method for producing a metal sulfide thin film comprising applying onto a substrate a stabilized solution comprising a thermally decomposable metallo-organic compound and elemental sulfur dissolved in a vaporizable solvent, said metallo-organic compound selected from the group consisting of mercaptides and thiocarboxylates evaporating the solvent to a deposit comprising the metallo-organic compound and the sulfur, and heating the deposit while exposed to an inert atmosphere to a temperature sufficient to decompose the metallo-organic compound to form a metal sulfide thin film.
Claim 2
Independent Claim
82 words
A method for producing a metal sulfide thin film comprising applying onto a substrate a stabilized solution comprising a thermally decomposable metallo-organic compound and elemental sulfur dissolved in a vaporizable solvent, said metallo-organic compound selected from the group consisting of mercaptides and thiocarboxylates evaporating the solvent to a deposit comprising the metallo-organic compound and the sulfur, and heating the deposit while exposed to an inert atmosphere to a temperature sufficient to decompose the metallo-organic compound to form a metal sulfide thin film.
Claim 3
Independent Claim
120 words
A method for forming a metal sulfide thin film on a substrate comprising applying onto the substrate a solution comprising a thermally decomposable metal mercaptide compound and elemental sulfur dissolved in pyridine solvent, said sulfur being added in an amount effective to increase solubility of the metal mercaptide and form a stable solution, evaporating the solvent to form a deposit comprising the metal mercaptide and the sulfur, and heating the deposit while exposed to a nonoxidizing atmosphere to a temperature sufficient to decompose the metal mercaptide compound to form a metal sulfide thin film, whereupon sulfur reacts with carbon derived by said thermal decomposition to form vaporizable carbon sulfur compounds, thereby reducing carbon contamination of the metal sulfide thin film.
Claim 4
Independent Claim
120 words
A method for forming a metal sulfide thin film on a substrate comprising applying onto the substrate a solution comprising a thermally decomposable metal mercaptide compound and elemental sulfur dissolved in pyridine solvent, said sulfur being added in an amount effective to increase solubility of the metal mercaptide and form a stable solution, evaporating the solvent to form a deposit comprising the metal mercaptide and the sulfur, and heating the deposit while exposed to a nonoxidizing atmosphere to a temperature sufficient to decompose the metal mercaptide compound to form a metal sulfide thin film, whereupon sulfur reacts with carbon derived by said thermal decomposition to form vaporizable carbon sulfur compounds, thereby reducing carbon contamination of the metal sulfide thin film.
Claim 5
Dependent Claim
30 words
The method of claim 2 wherein the metal mercaptide compound is a zinc mercaptide compound and said heating decomposes the zinc mercaptide compound to form a zinc sulfide thin film.
Claim 6
Dependent Claim
25 words
The method of claim 2 wherein the solution contains sulfur in an amount up to about one percent by weight of the metal mercaptide compound.
Claim 7
Dependent Claim
50 words
A stable solution comprising a metallo-organic compound dissolved in a solvent, said metallo-organic compound selected from the group consisting of mercaptides and thiocarboxylates comprising elemental sulfur dissolved in said solvent in an amount effective to increase solubility of said metallo-organic compound in said solution and to form a stable solution.
Claim 8
Dependent Claim
50 words
A stable solution comprising a metallo-organic compound dissolved in a solvent, said metallo-organic compound selected from the group consisting of mercaptides and thiocarboxylates comprising elemental sulfur dissolved in said solvent in an amount effective to increase solubility of said metallo-organic compound in said solution and to form a stable solution.
Claim 9
Dependent Claim
43 words
A stable solution comprising a metal mercaptide compound dissolved in pyridine solvent and further comprising elemental sulfur dissolved in said pyridine solvent in an amount effective to increase solubility of said metal mercaptide compound in said solution and to form a stable solution.
Claim 10
Dependent Claim
43 words
A stable solution comprising a metal mercaptide compound dissolved in pyridine solvent and further comprising elemental sulfur dissolved in said pyridine solvent in an amount effective to increase solubility of said metal mercaptide compound in said solution and to form a stable solution.
Claim 11
Dependent Claim
15 words
The solution of claim 6 wherein the metal mercaptide compound is a zinc mercaptide compound.
Claim 12
Dependent Claim
25 words
The solution of claim 6 wherein the solution comprises sulfur in an amount less than one percent by weight of the dissolved metal mercaptide compound.
Claim 13
Dependent Claim
27 words
The solution of claim 6 wherein the solution comprises sulfur in an amount between about 0.3 and 1.0 percent by weight of the dissolved metal mercaptide compound.
References Cited (Backward Citations)
JPS62146276A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-03-13 | 1992-09-12 | 1993-03-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-03-13 | 1996-09-12 | 1997-03-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-03-13 | 2000-09-12 | 2001-03-14 | $7700.00 | Window Closed / Lapsed |