Method of eliminating core distortion in diffusion bonded and uperplastically formed structures
Assignee: Boeing North American Inc
•
Filing: 1983-05-07
•
Granted: 1989-03-14
•
Expires: 2003-05-07
Abstract
Abstract Method for eliminating core distortion in diffusion bonded and superplastically formed structures or panels, wherein metal blanks or workpieces of metal, capable of diffusion bonding and superplastic forming such as a titanium alloy, preferably in the form of thin sheets of the order of 0.030 inch thick or less, are placed in contact with each other in a tooling apparatus or die, the sheets are joined at selected areas by diffusion bonding and are then expanded superplastically to form a desired panel or a truss core panel structure. In such method, the metal sheets are diffusion bonded at certain preselected areas under pressure and at elevated temperature, and the unbonded areas of the sheets are then expanded by superplastic forming into contact with the walls of the tool or die cavity, at elevated temperature e.g., 1600-1650° F. and an internal gas pressure e.g., about 300 psi, to form the desired panel. Following superplastic forming and cooling, the thin cell walls of the core panel are often distorted or crushed. As a feature of the invention, following superplastic forming and release of the internal gas pressure, and during cooling of the panel and while the metal panel is still at a temperature where the metal remains flexible or plastic, e.g., 1200°-1400° F., a low internal differential gas pressure, e.g., of about 3-7 psi, is introduced into the interior of the panel, expanding the panel out to its original form against the tool or die as a restraint, and straightening the thin core cell walls of the panel which were distorted following superplastic forming.
Inventors
- 👤 Charles Dowling
- 👤 Roger S. Raymond
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 17:20
CPC Classifications
B; B21; B21D; B21D26/00; B21D26/02; B21D26/053; B21D26/055; B23; B23K; B23K20/00; B23K20/22; B23K20/233
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
152 words
A method for eliminating core distortion in the production of core panels formed from metal workpieces of a metal capable of diffusion bonding and superplastic forming, the core of said panels being thin and subject to distortion following superplastic forming, which comprises: diffusion bonding said metal workpieces at preselected areas in a die, expanding the unbonded areas of said workpieces by superplastic forming at elevated temperature and pressure into contact with the walls of said die, and forming a core panel, and following release of said pressure after superplastic forming and during cooling and distortion of said panel in said die, introducing a low differential pressure into the interior of said core panel to expand said panel to its original form, said low internal differential pressure being introduced into said core panel while the metal of said panel is still at a sufficiently elevated temperature so that said metal is still flexible.
Claim 2
Independent Claim
152 words
A method for eliminating core distortion in the production of core panels formed from metal workpieces of a metal capable of diffusion bonding and superplastic forming, the core of said panels being thin and subject to distortion following superplastic forming, which comprises: diffusion bonding said metal workpieces at preselected areas in a die, expanding the unbonded areas of said workpieces by superplastic forming at elevated temperature and pressure into contact with the walls of said die, and forming a core panel, and following release of said pressure after superplastic forming and during cooling and distortion of said panel in said die, introducing a low differential pressure into the interior of said core panel to expand said panel to its original form, said low internal differential pressure being introduced into said core panel while the metal of said panel is still at a sufficiently elevated temperature so that said metal is still flexible.
Claim 3
Dependent Claim
11 words
The method of claim 1, said metal being a titanium alloy.
Claim 4
Independent Claim
157 words
A method for eliminating core distortion in the production of core panels having a thin core and formed from a plurality of metal workpieces of a metal capable of diffusion bonding and superplastic forming, which comprises: diffusion bonding said workpieces at preselected areas in a die, expanding the unbonded areas of said workpieces by superplastic forming at elevated temperatures and pressure into contact with the walls of said die, and forming a core panel, releasing said pressure and cooling said core panel, resulting in distorted core cell walls, and following release of said pressure and during cooling of said panel in said die, and while the metal of said panel remains at a sufficiently elevated temperature so that said metal is still flexible, introducing a low internal differential pressure into said core panel to expand said panel to its original form against the restraint of said die, and straightening the distorted core cell walls of said panel.
Claim 5
Independent Claim
157 words
A method for eliminating core distortion in the production of core panels having a thin core and formed from a plurality of metal workpieces of a metal capable of diffusion bonding and superplastic forming, which comprises: diffusion bonding said workpieces at preselected areas in a die, expanding the unbonded areas of said workpieces by superplastic forming at elevated temperatures and pressure into contact with the walls of said die, and forming a core panel, releasing said pressure and cooling said core panel, resulting in distorted core cell walls, and following release of said pressure and during cooling of said panel in said die, and while the metal of said panel remains at a sufficiently elevated temperature so that said metal is still flexible, introducing a low internal differential pressure into said core panel to expand said panel to its original form against the restraint of said die, and straightening the distorted core cell walls of said panel.
Claim 6
Dependent Claim
27 words
The method of claim 3, including releasing said low internal differential pressure following said expansion of said panel to its original form, and further cooling said panel.
Claim 7
Dependent Claim
18 words
The method of claim 3, the core wall thickness of said panel being about 0.030 inch or less.
Claim 8
Dependent Claim
11 words
The method of claim 5, said metal being a titanium alloy.
Claim 9
Dependent Claim
18 words
The method of claim 3, said low internal differential pressure ranging from about 3 to about 10 psi.
Claim 10
Dependent Claim
18 words
The method of claim 7, said low internal differential pressure ranging from about 3 to about 7 psi.
Claim 11
Dependent Claim
26 words
The method of claim 3, said metal panel being at a temperature of about 1000° F. or above during said introduction of said low internal pressure.
Claim 12
Dependent Claim
26 words
The method of claim 9, the temperature of said metal panel during introduction of said low internal pressure ranging from about 1200° to about 1400° F.
Claim 13
Dependent Claim
81 words
In the method for the production of a core structure having a thin core, from metal blanks of a metal by diffusion bonding and superplastic forming in a die, the core of said core structure being subject to distortion following superplastic forming, the improvement which comprises pressurizing said core structure internally with a low differential pressure after superplastic forming and during cooling of said core structure, to thereby expand said core structure into contact with said die and eliminate core distortion.
Claim 14
Dependent Claim
81 words
In the method for the production of a core structure having a thin core, from metal blanks of a metal by diffusion bonding and superplastic forming in a die, the core of said core structure being subject to distortion following superplastic forming, the improvement which comprises pressurizing said core structure internally with a low differential pressure after superplastic forming and during cooling of said core structure, to thereby expand said core structure into contact with said die and eliminate core distortion.
Claim 15
Dependent Claim
52 words
The improvement of claim 11, said core structure being internally pressurized by a gas at a temperature at which the metal of said core structure remains flexible to permit said expansion of said panel, and including releasing said internal pressure following said expansion, and further cooling said core structure to ambient temperature.
Claim 16
Dependent Claim
39 words
The improvement of claim 12, the core wall thickness of said core structure being about 0.030 inch or less, and said core structure being cooled to a temperature above about 1000° F. prior to pressurizing said core structure internally.
Claim 17
Dependent Claim
11 words
The improvement of claim 12, said metal being a titanium alloy.
Claim 18
Dependent Claim
11 words
The improvement of claim 13, said metal being a titanium alloy.
Claim 19
Dependent Claim
38 words
The improvement of claim 12, said metal being a titanium alloy, the core wall thickness of said core structure being about 0.030 inch or less, and said low differential pressure ranging from about 3 to about 7 psi.
Claim 20
Dependent Claim
27 words
The improvement of claim 16, said core structure being cooled to a temperature of about 1200 to about 1400° F. prior to pressurizing said core structure internally.
Claim 21
Independent Claim
214 words
A method for eliminating core distortion in the production of a truss core panel of a titanium alloy having a core wall of a thickness of about 0.030 inch or less, by diffusion bonding and superplastic forming which comprises: diffusion bonding at least two sheets of a titanium alloy, at least one of said sheets having a thickness of about 0.030 inch or less, at preselected areas in a die at temperature ranging from about 1450° F. to about 1850° F. and at pressure of about 150 to about 600 psi, expanding the unbonded areas of said titanium alloy sheets by superplastic forming at elevated temperatures of about 1600° to about 1700° F. and at a pressure of about 200 to about 400 psi, into contact with the walls of said die and forming a truss core panel, releasing the pressure following superplastic forming, and cooling said truss core to a temperature of about 1200° to about 1400° F., resulting in core wall distortion, and introducing an inert gas at a differential pressure of about 3 to about 7 psi internally into said truss core panel to expand said panel to its original form into contact with the walls of said die, to thereby eliminate said core wall distortion of said truss core panel.
Claim 22
Independent Claim
214 words
A method for eliminating core distortion in the production of a truss core panel of a titanium alloy having a core wall of a thickness of about 0.030 inch or less, by diffusion bonding and superplastic forming which comprises: diffusion bonding at least two sheets of a titanium alloy, at least one of said sheets having a thickness of about 0.030 inch or less, at preselected areas in a die at temperature ranging from about 1450° F. to about 1850° F. and at pressure of about 150 to about 600 psi, expanding the unbonded areas of said titanium alloy sheets by superplastic forming at elevated temperatures of about 1600° to about 1700° F. and at a pressure of about 200 to about 400 psi, into contact with the walls of said die and forming a truss core panel, releasing the pressure following superplastic forming, and cooling said truss core to a temperature of about 1200° to about 1400° F., resulting in core wall distortion, and introducing an inert gas at a differential pressure of about 3 to about 7 psi internally into said truss core panel to expand said panel to its original form into contact with the walls of said die, to thereby eliminate said core wall distortion of said truss core panel.
Claim 23
Dependent Claim
36 words
The method of claim 18, said truss core panel being formed from three sheets of said titanium alloy in contact with each other, the interior core sheet having a thickness of about 0.030 inch or less,
Claim 24
Dependent Claim
58 words
The method of claim 19, said cooling of said truss core panel following superplastic forming being carried out down to a temperature of about 1300° to about 1400° F., and said inert gas then being introduced internally into said truss core panel at a differential pressure of about 3 psi for about 30 minutes to about 1 hour.
Claim 25
Dependent Claim
26 words
The method of claim 18, including releasing the internal pressure in said truss core panel, and further cooling said truss core panel to about ambient temperature.
References Cited (Backward Citations)
US3011254A
Cited
US3812230A
Cited
US3861847A
Cited
US3825641A
Cited
US3936920A
Cited
US4104394A
Cited
US4406393A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-03-13 | 1992-09-12 | 1993-03-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-03-13 | 1996-09-12 | 1997-03-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-03-13 | 2000-09-12 | 2001-03-14 | $7700.00 | Window Closed / Lapsed |