Abstract
Abstract An analytical technique for controlling the curing process of fiber-reinforced composite materials that are formed using thermosetting resins. The technique is the percent gel method and involves development of a time-to-gel equation as a function of temperature. From this equation a rate-of-gel equation is then determined, and a percent gel is calculated which is the product of rate-of-gel times time. Percent gel accounting is used to control the proper pressure application point in an autoclave cure process to achieve desired properties in a production composite part.
Inventors
- 👤 Charles N. Webster
- 👤 Robert O. Scott
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 12:13
CPC Classifications
G; G01; G01N; G01N33/00; G01N33/44; G01N33/442; B; B29; B29C; B29C35/00; B29C35/02; B29C35/0288; B29C37/00; B29C2037/90; B29C2037/903; G01N2203/00; G01N2203/0058; G01N2203/0092; Y; Y10; Y10S; Y10S264/00; Y10S264/59
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
235 words
The method of monitoring and controlling the curing process of fiber-reinforced thermosetting resin composite materials in order to establish after cure, predetermined composite characteristics of strength, thickness, resin content and a porosity, which are uniform from one article to the next despite variations in the percent gel, or state of gelation, of the different articles, due to their different histories of temperature and time-at-temperature prior to a heating phase comprising the steps of; (a) determining the percent gel already existing in a particular batch of composite material at some point in time; (b) accumulating and accounting for additional percent gel due to the temperature and time-at-temperature of all intervening steps, including a fabrication steps, said intervening steps being those subsequent to determination of the initial percent gel and prior to the heating phase; (c) calculating, on the basis of steps (a) and (b) and the desired product characteristics, the percent gel remaining to be accomplished prior to a pressure increasing step which is to be conducted, at least in part, simultaneously with the heating phase; (d) initiating the heating phase; (e) controlling the temperature and time-at-temperature during the heating phase to accomplish the desired percent gel prior to initiation of the pressure increasing step; (f) initiating the pressure increasing step at the desired percent gel; (g) controlling the temperature and time-at-temperature during the remainder of the heating phase to accomplish 100% percent gel, complete gelation.
Claim 2
Independent Claim
235 words
The method of monitoring and controlling the curing process of fiber-reinforced thermosetting resin composite materials in order to establish after cure, predetermined composite characteristics of strength, thickness, resin content and a porosity, which are uniform from one article to the next despite variations in the percent gel, or state of gelation, of the different articles, due to their different histories of temperature and time-at-temperature prior to a heating phase comprising the steps of; (a) determining the percent gel already existing in a particular batch of composite material at some point in time; (b) accumulating and accounting for additional percent gel due to the temperature and time-at-temperature of all intervening steps, including a fabrication steps, said intervening steps being those subsequent to determination of the initial percent gel and prior to the heating phase; (c) calculating, on the basis of steps (a) and (b) and the desired product characteristics, the percent gel remaining to be accomplished prior to a pressure increasing step which is to be conducted, at least in part, simultaneously with the heating phase; (d) initiating the heating phase; (e) controlling the temperature and time-at-temperature during the heating phase to accomplish the desired percent gel prior to initiation of the pressure increasing step; (f) initiating the pressure increasing step at the desired percent gel; (g) controlling the temperature and time-at-temperature during the remainder of the heating phase to accomplish 100% percent gel, complete gelation.
Claim 3
Dependent Claim
20 words
The method of claim 1 wherein the fiber is selected from the group consisting of glass, boron, graphite and carbon.
Claim 4
Dependent Claim
19 words
The method of claim 2 wherein the resin is selected from the group consisting of epoxy, phenolic, and polyimide.
Claim 5
Dependent Claim
51 words
The method of claim 2 wherein the resin is selected from the group consisting of thermosetting resins whose B-stage advancement rate can be characterized in the form: r.sub.g =K EXP (-E/RT) where: r g =Rate-of-gel, % per minute K=Specific Reactivity, % per minute E=Activation Energy, BTU/lb-mole R=Gas Constant, BTU/lb-mole-R T=Temperature, °R
Claim 6
Dependent Claim
35 words
The method of claim 3 wherein the pressure increasing step and the heating phase are conducted while the resin is within the B-stage intermediate reaction state where the resin softens and is plastic while hot.
Claim 7
Dependent Claim
42 words
The method of claim 1 where the percent gel remaining to be accomplished is determined by use of a time-to-gel equation in the form: 0=2.486×10.sup.-12 EXP (20586/T) where 0 is the time-to-gel in minutes and T is the absolute temperature in °R.
Claim 8
Dependent Claim
16 words
The method of claim 6 wherein the material is graphite fabric impregnated with a phenolic resin.
Claim 9
Dependent Claim
32 words
The method of claim 7 wherein the time-to-gel for the resin is as follows: ______________________________________
Temperature °F.
Time-To-Gel
______________________________________
40 3.6 Years
70 128 Days
175 298 Minutes
250 10 Minutes
______________________________________
Claim 10
Dependent Claim
50 words
The method of claim 6 where the time-to-gel equation is developed by preparing a series of samples of the resin impregnated fabric and heating them at a constant temperature for varying lengths of time, and pressing each sample in order to establish resin squeeze-out beyond the boundary of the fabric.
Claim 11
Dependent Claim
29 words
The method of claim 6 where the time-to-gel equation is developed by preparing a series of samples of the resin impregnated fabric and measuring time-to-gel using constant-temperature Rheology methods.
Claim 12
Dependent Claim
104 words
The method of claim 1 wherein the pressure increasing step and the heating phase are performed within an autoclave having temperature and time control such that the autoclave control allows for differing stages of pre-autoclave advancement of the resin composite under cure by subtracting the amount of percent gel accumulated prior to the heating phase from the percent gel desired at initiation of pressure increasing step in order to determine the percent gel to be added in by the autoclave prior to the pressure increasing step, and the percent gel to be added in by the autoclave during the remainder of the heating phase.
Claim 13
Dependent Claim
145 words
The method of claim 1 wherein the pressure increasing step and the heating phase are performed within an autoclave having an autoclave control system and wherein the autoclave control system is fully automated and includes input parameters of accumulated percent gel prior to the autoclave run, the desired percent gel when the autoclave pressure is raised, the time-temperature profile and the autoclave pressure profile, and the process further includes the steps of measuring the autoclave pressure, autoclave temperature, and the temperature of the production part during the autoclave cycle, providing elasped time for calculating the percent gel and for loop control logic calculations, employing the percent gel calculations in the pressure control logic and in the temperature control logic of the control system, and employing the production part temperature control logic to signal completion of the heating phase and the completion of the autoclave cycle.
References Cited (Backward Citations)
US3049410A
Cited
US3413836A
Cited
US3718721A
Cited
US4022555A
Cited
US4344142A
Cited
US4140050A
Cited
US4312212A
Cited
US4382052A
Cited
US4542466A
Cited
US4455268A
Cited
US4515545A
Cited
US4589072A
Cited
US4371483A
Cited
US4494408A
Cited
US4517146A
Cited
US4551807A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-03-06 | 1992-09-05 | 1993-03-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-03-06 | 1996-09-05 | 1997-03-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-03-06 | 2000-09-05 | 2001-03-07 | $7700.00 | Window Closed / Lapsed |