Method of manufacturing chromium-doped beryllium aluminate laser rod and lasers incorporating the rods therein
Assignee: Laser Energetics Inc
•
Filing: 1988-02-26
•
Granted: 1989-02-28
•
Expires: 2008-02-26
Abstract
Abstract The invention relates to an improved method of making a beryllium aluminate laser rod wherein a crystal is grown by the Czochraslshi technique by core drilling and grinding. The improvement resides in heat treating the rod to release mechanical stresses induced in the single crystal rod by the griding operation to improve its optical properties. The invention also resides in a rod manufactured in this manner and to a laser employing such a rod.
Inventors
- 👤 Donald J. Harter
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 18:03
CPC Classifications
H; H01; H01S; H01S3/00; H01S3/14; H01S3/16; C; C30; C30B; C30B15/00; C30B29/00; C30B29/10; C30B29/16; C30B29/20; H01S3/1601; H01S3/162; H01S3/1623; H01S3/163; H01S3/1631; H01S3/1633
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
115 words
In a method of making solid state laser rods for use in a solid state laser, the method comprising the steps of preparing a single crystal of beryllium aluminate having a chromium doping concentration effective to permit lasing of said crystal, said crystal being prepared by the Czochralski technique from stoichiometric melt, and thereafter core drilling and grinding said crystal into a laser rod, the improvement wherein said rod is further treated by heating in a furnace at a temperature, within the range of about 800° C. to about 1500° C. to release stress induced on its crystal structure by grinding whereby the wavefront distortion of a light beam propagating throughout the rod is reduced.
Claim 2
Dependent Claim
115 words
In a method of making solid state laser rods for use in a solid state laser, the method comprising the steps of preparing a single crystal of beryllium aluminate having a chromium doping concentration effective to permit lasing of said crystal, said crystal being prepared by the Czochralski technique from stoichiometric melt, and thereafter core drilling and grinding said crystal into a laser rod, the improvement wherein said rod is further treated by heating in a furnace at a temperature, within the range of about 800° C. to about 1500° C. to release stress induced on its crystal structure by grinding whereby the wavefront distortion of a light beam propagating throughout the rod is reduced.
Claim 3
Dependent Claim
29 words
A method as in claim 1 wherein said treatment is conducted in an air atmosphere, and further comprising the step of polishing said laser rod after said heat treatment.
Claim 4
Dependent Claim
17 words
A method as in claim 2 wherein said temperature is about 1300° C. to about 1500° C.
Claim 5
Dependent Claim
17 words
A method as in claim 3 wherein said temperature is about 1350° C. to about 1400° C.
Claim 6
Dependent Claim
72 words
A method as in claim 2 wherein said heat treatment is conducted by heating said rod from room temperature to said temperature range at a temperature rate of increase effective to avoid thermal shocking the rod, thereafter the rod is held at said temperature to cause said release of stress to occur and the rod is then cooled to room temperature at a rate effective to ensure uniform cooling of the rod.
Claim 7
Dependent Claim
23 words
A method as in claim 1 wherein said laser rod is first polished, and thereafter said treatment is conducted in an inert atmosphere.
Claim 8
Dependent Claim
12 words
A method as in claim 6 wherein said inert atmosphere is nitrogen.
Claim 9
Dependent Claim
16 words
A method as in claim 7 wherein said temperature is about 1300° to about 1500° C.
Claim 10
Dependent Claim
17 words
A method as in claim 8 wherein said temperature is about 1,350° C. to about 1500° C.
Claim 11
Dependent Claim
73 words
A method as in claim 6 wherein said heat treatment is conducted by heating said rod from room temperature to said temperature range at a temperature rate of increase effective to avoid thermal shocking the rod, thereafter the rod is held at said temperature range to cause said release of stress to occur and the rod is then cooled to room temperature at a rate effective to ensure uniform cooling of the rod.
Claim 12
Dependent Claim
68 words
A broadly wavelength-tunable laser comprising: (a) a laser rod made in accordance with claim 1: (b) means for exciting said laser rod to emit coherent radiation: (c) tuning means for tuning said coherent radiation in a spectral range from red to infrared: and (d) mirrors forming an optical resonator, said resonator enclosing the laser medium and tuning means and adapted for maintaining laser oscillation between the two mirrors.
Claim 13
Dependent Claim
20 words
The laser of claim 11 in which the tuning means is a birefringent filter rotatably mounted within the optical resonator.
Claim 14
Dependent Claim
23 words
The laser of claim 11 in which the tuning means is a prism and at least one of the mirrors is pivotably mounted.
Claim 15
Dependent Claim
20 words
The laser of claim 11 in which the tuning means is an optical grating rotatably mounted within the optical resonator.
Claim 16
Dependent Claim
22 words
The laser of claim 11 in which the tuning means is a multilayer dielectric coated filter rotatably mounted within the optical resonator.
Claim 17
Dependent Claim
28 words
The laser of claim 11 in which the means for exciting said laser medium comprises a pulsed incoherent light source emitting at wavelengths shorter than about 700 nm.
Claim 18
Dependent Claim
15 words
The laser of claim 16 in which the light source comprises a xenon flash lamp.
Claim 19
Dependent Claim
28 words
The laser of claim 11 in which the means for exciting said laser medium comprises a continuous incoherent light source emitting at wavelengths shorter than about 700 nm.
Claim 20
Dependent Claim
12 words
The laser of claim 11 further comprising means for Q-switching said laser.
Claim 21
Dependent Claim
16 words
The laser of claim 19 in which the Q-switching means comprise a Pockels cell and polarizer.
References Cited (Backward Citations)
US3866142A
Cited
US3997853A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-02-28 | 1992-08-29 | 1993-02-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-02-28 | 1996-08-29 | 1997-02-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-02-28 | 2000-08-29 | 2001-02-28 | $7700.00 | Window Closed / Lapsed |