US4808675A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Moisture permeable film for lamination to a textile material
Assignee: Honeywell International Inc
•
Filing: 1986-12-22
•
Granted: 1989-02-28
•
Expires: 2006-12-22
Abstract
Abstract This invention is a water-resistant film for lamination to a textile material, and the flexible, laminated product produced therewith. The film has a permeability of at least 0.0008 metric perm-cm. at 20 DEG C. and 65 percent relative humidity and of at least 0.0006 metric perm-cm. at 30 DEG C. and 50 percent relative humidity. The film is formed from a block copolymer having a number average molecular weight of from about 15,000 to about 35,000. The block copolymer contains polymer segments prepared by the amination of a polyether formed by treating a polyethylene glycol with an alkylene oxide of three or more carbon atoms. The product is a laminant of a layer of the described film and a layer of a textile material, and is useful in the formation of water-resistant, moisture permeable articles such as garments, tarpaulins, tents, and the like.
Inventors
- 👤 Ian C. Twilley
- 👤 Robert A. Lofquist
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 22:16
CPC Classifications
B; B32; B32B; B32B27/00; B32B27/12; B32B27/28; B32B27/285; B32B27/34; B32B5/00; B32B5/18; C; C08; C08G; C08G69/00; C08G69/40; C08J; C08J5/00; C08J5/18; D; D06; D06N; D06N3/00; D06N3/12; D06N3/125; B32B2307/00; B32B2307/70; B32B2307/724; B32B2307/73; B32B2371/00; B32B2377/00; B32B2437/00; C08J2371/00; C08J2371/02; C08J2377/00; Y; Y10; Y10S; Y10S525/00; Y10S525/926; Y10T; Y10T428/00; Y10T428/249921; Y10T428/249953; Y10T428/249978; Y10T428/24998; Y10T428/249982; Y10T442/00; Y10T442/30; Y10T442/3854; Y10T442/3894
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
99 words
A water-resistant film for lamination to a textile material, said film having a permeability of at least 0.0008 metric perm-cm. when tested at 20° C. and 65 percent relative humidity and of at least 0.0006 metric perm-cm. when tested at 30° C. and 50 percent relative humidity, said film being formed from a block copolyether amide having a number average molecular weight of from about 15,000 to about 35,000 and containing polymer segments, said segments being prepared by the amination of a polyether formed by treating a polyethylene glycol with an alkylene oxide having at least three carbon atoms.
Claim 2
Dependent Claim
99 words
A water-resistant film for lamination to a textile material, said film having a permeability of at least 0.0008 metric perm-cm. when tested at 20° C. and 65 percent relative humidity and of at least 0.0006 metric perm-cm. when tested at 30° C. and 50 percent relative humidity, said film being formed from a block copolyether amide having a number average molecular weight of from about 15,000 to about 35,000 and containing polymer segments, said segments being prepared by the amination of a polyether formed by treating a polyethylene glycol with an alkylene oxide having at least three carbon atoms.
Claim 3
Dependent Claim
142 words
The film of claim 1 wherein the polymer segments have the following structure: A. a polyether segment consisting predominantly of ##STR7## where c is at least 1, (a+c) is at least 1 but less than 5.5 and b is at least 10 but less than 90; B. a polyamide segment consisting of at least one of the following: ##STR8## where R 1 , R 2 and R 3 are each selected from the same or different alkylene or substituted alkylene moieties of from 4 to 11 carbons and difunctional aromatic moieties; wherein the concentration of segment A in the copolyether amide is from about 5 to about 50 percent by weight of copolyether amide, and a phenolic antioxidant is used in the copolyether amide where the ratio of antioxidant to polyether segment is greater than 0.01 but less than 0.1 by weight.
Claim 4
Dependent Claim
26 words
The film of claim 2 wherein the concentration of segment A in the copolyether amide is about 10 to 25 percent by weight of copolyether amide.
Claim 5
Dependent Claim
12 words
The film of claim 3 wherein a carboxylic acid is also present.
Claim 6
Dependent Claim
22 words
The film of claim 4 wherein segment A (a+c) is about 3 to 4, and b is between about 20 and 75.
Claim 7
Dependent Claim
13 words
The film of claim 5 wherein b is between about 40 and 50.
Claim 8
Dependent Claim
21 words
The film of claim 6 wherein the polyamide segment B is B.1. and R 1 is (CH 2 ) 5 .
Claim 9
Dependent Claim
12 words
The film of claim 7 wherein the carboxylic acid is terephthalic acid.
Claim 10
Dependent Claim
26 words
The film of claim 7 wherein the carboxylic acid is selected from the group consisting of terephthalic, adipic, azelaic, isophthalic, dodecanedioic, sebacic and naphthalene dicarboxylic acid.
Claim 11
Dependent Claim
47 words
The film of claim 8 wherein said film is nonoriented and wherein the permeability is at least 0.0010 metric perm-cm. when tested at 20° C. and 65 percent relative humidity and is at least 0.0008 metric perm-cm. when tested at 30° C. and 50 percent relative humidity.
Claim 12
Dependent Claim
163 words
The film of claim 2 wherein the polymer segments have the following structure: A. a polyether segment consisting of from about 5 to about 10 percent by weight of ##STR9## and from about 95 percent to 90 percent by weight of ##STR10## where c is at least 1, (a+c) is at least 1 but less than 5.5 and b is at least 10 but less than 90; B. a polyamide segment consisting of at least one of the following: ##STR11## where R 1 , R 2 and R 3 are each selected from the same or different alkylene or substituted alkylene moieties of from 4 to 11 carbons and difunctional aromatic moieties; wherein the concentration of segment A in the copolyether amide is from about 5 to about 50 percent by weight of copolyether amide, and a phenolic antioxidant is used in the copolyether amide where the ratio of antioxidant to polyether segment is greater than 0.01 but less than 0.1 by weight.
Claim 13
Dependent Claim
28 words
The film of claim 11 wherein the concentration of segment A in the copolyether amide is from about 10 to about 25 percent by weight of copolyether amide.
Claim 14
Dependent Claim
46 words
The film of claim 12 wherein said film is nonoriented and wherein the permeability is at least 0.0010 metric perm-cm. when tested at 20° C. and 65 percent relative humidity and at least 0.0008 metric perm-cm. when tested at 30° C. and 50 percent relative humidity.
Claim 15
Dependent Claim
29 words
The film of claim 12 wherein said copolymer has from about 5 to 35 per 10 6 grams ends terminated by a hindered phenol antioxidant, said antioxidant being tetrakis[methylene(3,5-di-t-butyl-4-hydroxyhydrocinnamate)]methane.
References Cited (Backward Citations)
GB1108811A
Cited
US3473956A
Cited
US3632666A
Cited
US3639502A
Cited
US3953566A
Cited
US4194041A
Cited
US4468505A
Cited
US4443511A
Cited
US4493870A
Cited
US4493870B1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-02-28 | 1992-08-29 | 1993-02-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-02-28 | 1996-08-29 | 1997-02-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-02-28 | 2000-08-29 | 2001-02-28 | $7700.00 | Window Closed / Lapsed |