Abstract The present invention relates to metallurgy of non-ferrous metals and alloys and, more particularly, to a process for producing an aluminium-silicon alloy with a content of silicon of 2 to 22% by mass. The process comprises charging crystalline silicon onto the sole of a reverberatory furnace so that the charged crystalline silicon has a cone shape, casting liquid aluminium into the furnace bath at 780°-820° C. and agitation of the resulting aluminium-silicon melt by means of a shaped jet of the same melt; the melt jet is directed into the base of the cone of the charged crystalline silicon at a speed of the jet along the axis thereof of from 0.5 to 0.8 m/s; simultaneously with the beginning of agitation the melt temperature in the furnace bath is lowered to 670°-750° C. and agitation of the melt is effected at this temperature. The alloy can be used in the automobile industry, tractor manufacture in the production of consumer goods.
Inventors
👤 Vadim P. Ivchenkov
👤 Nikolai A. Kaluzhsky
👤 Eduard A. Isidorov
👤 Viktor G. Sirotenko
👤 Viktor S. Shusterov
👤 Gennady A. Pakhomov
👤 Fedor K. Teplyakov
👤 Oleg S. Khromovskikh
Bibliographic Details
Application Number—
JurisdictionUS
Data Sourcegoogle_patents
Last Synchronized2026-10-23 20:47
CPC Classifications
C; C22; C22C; C22C1/00; C22C1/02; C22C1/026
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
108 words
A process for producing an aluminum-silicon alloy with a content of silicon of 2-22% by mass comprising charging crystalline silicon onto the sole of a reverberatory furnace, the charged crystalline silicon having a cone shape; casting liquid aluminium onto the sole of said reverberatory furnace to form a molten bath with the silicon at a temperature of from 780° to 820° C.; agitating the resulting aluminum-silicon melt by a shaped jet of the same melt, said melt jet being directed into the base of the cone of the charged crystalline silicon; and casting the resultant melt into a mold to produce an aluminum-silicon alloy in a solid state.
Claim 2
Dependent Claim
108 words
A process for producing an aluminum-silicon alloy with a content of silicon of 2-22% by mass comprising charging crystalline silicon onto the sole of a reverberatory furnace, the charged crystalline silicon having a cone shape; casting liquid aluminium onto the sole of said reverberatory furnace to form a molten bath with the silicon at a temperature of from 780° to 820° C.; agitating the resulting aluminum-silicon melt by a shaped jet of the same melt, said melt jet being directed into the base of the cone of the charged crystalline silicon; and casting the resultant melt into a mold to produce an aluminum-silicon alloy in a solid state.
Claim 3
Dependent Claim
25 words
A process according to claim 1, wherein the melt jet speed along its axis is maintained within the range of from 0.5 to 0.8 m/s.
Claim 4
Dependent Claim
34 words
A process according to claim 1, wherein, simultaneously with the beginning of agitation, the melt temperature in the furnace bath is lowered to 670°-750° C. and the melt agitation is effected at this temperature.