In situ process for producing a composite containing refractory material
Assignee: Drexel University
•
Filing: 1986-01-23
•
Granted: 1989-02-28
•
Expires: 2006-01-23
Abstract
Abstract An in situ process is provided for producing a composite comprising a refractory material dispersed in a solid matrix. A molten composition comprising a matrix liquid, and at least one refractory carbide-forming component are provided, and a gas is introduced into the molten composition. A reactive component is also provided for reaction with the refractory material-forming component. The refractory material-forming component and reactive component react to form a refractory material dispersed in the matrix liquid, and the liquid composite is cooled to form a solid composite material. In one embodiment, the reactive component is a carbonaceous component in the form of a component of the gas, a solid in the gas or the molten composition, or both. The carbonaceous component is provided for reaction with a refractory carbide-forming component to yield a refractory carbide. In a preferred embodiment, the matrix liquid is molten aluminum and the refractory carbide-forming component is tantalum. In other embodiments, refractory borides or refractory nitrides are formed in situ in the matrix liquid.
Inventors
- 👤 Michael J. Koczak
- 👤 K. Sharvan Kumar
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 12:10
CPC Classifications
C; C22; C22C; C22C1/00; C22C1/10; C22C1/1036; C22C1/1047; C22C1/1052; C22C32/00; C22C32/0047; C22C32/0052
Claims Analysis
Total Claims: 44
Claim 1
Independent Claim
119 words
An in situ process for producing a composite with improved homogeneity comprising a refractory material dispersed in a matrix, the process comprising providing a molten composition comprising a matrix liquid; providing at least one refractory material-forming component selected from the group consisting of refractory boride-forming components and refractory carbide-forming components in the molten composition; introducing a gas into the molten composition; providing a reactive component selected from the group consisting of boron containing components and carbonaceous components for reaction with the refractory material-forming component; whereby the refractory material-forming component reacts with the reactive component in the matrix liquid to form a refractory material dispersed in the matrix liquid; and cooling the liquid composite to form a solid composite material.
Claim 2
Dependent Claim
119 words
An in situ process for producing a composite with improved homogeneity comprising a refractory material dispersed in a matrix, the process comprising providing a molten composition comprising a matrix liquid; providing at least one refractory material-forming component selected from the group consisting of refractory boride-forming components and refractory carbide-forming components in the molten composition; introducing a gas into the molten composition; providing a reactive component selected from the group consisting of boron containing components and carbonaceous components for reaction with the refractory material-forming component; whereby the refractory material-forming component reacts with the reactive component in the matrix liquid to form a refractory material dispersed in the matrix liquid; and cooling the liquid composite to form a solid composite material.
Claim 3
Dependent Claim
19 words
A process according to claim 1 wherein the gas is introduced into the molten composition under an inert atmosphere.
Claim 4
Dependent Claim
35 words
A process according to claim 1 comprising melting a mixture of a matrix solid and a solid refractory material-forming component to provide the molten composition which comprises the matrix liquid and the refractory material-forming component.
Claim 5
Dependent Claim
33 words
A process according to claim 1 additionally comprising melting a matrix solid to provide a matrix liquid, and subsequently adding the refractory material-forming component to the matrix liquid to provide the molten composition.
Claim 6
Dependent Claim
31 words
A process according to claim 1 wherein the carbonaceous component comprises a carbonaceous solid and wherein the carbonaceous solid is dispersed in the gas which is introduced into the molten composition.
Claim 7
Dependent Claim
13 words
A process according to claim 1 wherein the gas comprises the carbonaceous component.
Claim 8
Dependent Claim
15 words
A process according to claim 6 wherein the gas additionally comprises an inert carrier gas.
Claim 9
Dependent Claim
13 words
A process according to claim 7 wherein the inert carrier gas is argon.
Claim 10
Dependent Claim
21 words
A process according to claim 6 wherein the carbonaceous component is selected from carbon monoxide, carbon dioxide, mixtures thereof, and methane.
Claim 11
Dependent Claim
46 words
A process according to claim 1 for producing a composite of aluminum and a finely dispersed particulate of a refractory carbide, the composite being substantially free of aluminum carbide, wherein the molten composition comprises molten aluminum and the refractory material-forming component comprises a refractory carbide-forming material.
Claim 12
Dependent Claim
12 words
The process of claim 10 wherein the refractory carbide-forming component comprises tantalum.
Claim 13
Dependent Claim
17 words
The process of claim 10 wherein the carbonaceous component is a gaseous mixture of argon and methane.
Claim 14
Dependent Claim
20 words
The process of claim 10 wherein the refractory carbide-forming component additionally comprises solid tantalum aluminide dispersed in the molten aluminum.
Claim 15
Dependent Claim
15 words
A process according to claim 1 wherein the matrix liquid comprises a molten ceramic material.
Claim 16
Dependent Claim
25 words
A process according to claim 1 wherein refractory carbide-forming component comprises a transition metal selected from niobium, tantalum, titanium, zirconium, hafnium, molybdenum, vanadium and tungsten.
Claim 17
Dependent Claim
25 words
A process according to claim 15 wherein at least a part of the total amount of the transition metal is dissolved in the matrix liquid.
Claim 18
Dependent Claim
39 words
A process according to claim 16 wherein the matrix liquid comprises a metallic element and the matrix liquid contains a second phase comprising an intermetallic compound of the metallic element of the matrix liquid and the refractory carbide-forming component.
Claim 19
Dependent Claim
17 words
A process according to claim 1 wherein the refractory carbide-forming component is selected from boron and silicon.
Claim 20
Dependent Claim
30 words
A process according to claim 1 wherein molten composition additionally comprises elemental carbon and the gas is an inert gas introduced into the molten composition to agitate the molten composition.
Claim 21
Dependent Claim
31 words
A process according to claim 19 wherein the refractory carbide-forming component and the elemental carbon are provided in the molten composition in substantially the same amounts on an equivalent weight basis.
Claim 22
Dependent Claim
30 words
A process according to claim 20 wherein the matrix liquid is molten aluminum; the refractory carbide-forming component is selected from tantalum, titanium and niobium; and the inert gas is argon.
Claim 23
Dependent Claim
21 words
A process according to claim 1 wherein the gas comprises a carbonaceous component and the molten composition additionally comprises elemental carbon.
Claim 24
Dependent Claim
26 words
process according to claim 22 wherein the amount of elemental carbon is greater than the amount of the refractory carbide-forming component on an equivalent weight basis.
Claim 25
Dependent Claim
16 words
A composite material produced by the process of claim 1 wherein said matrix is a metal.
Claim 26
Dependent Claim
38 words
A process according to claim 1 wherein the matrix liquid includes a liquid metal which reacts with the reactive component to form a product having a Gibbs free energy of formation greater than about -10 kilocalories per mole.
Claim 27
Dependent Claim
18 words
A process according to claim 25 wherein the liquid metal comprises a molten alloy of nickel and copper.
Claim 28
Dependent Claim
16 words
A composite material produced by the process of claim 2 wherein said matrix is a metal.
Claim 29
Dependent Claim
16 words
A composite material produced by the process of claim 3 wherein said matrix is a metal.
Claim 30
Dependent Claim
16 words
A composite material produced by the process of claim 5 wherein said matrix is a metal.
Claim 31
Dependent Claim
16 words
A composite material produced by the process of claim 5 wherein said matrix is a metal.
Claim 32
Dependent Claim
16 words
A composite material produced by the process of claim 6 wherein said matrix is a metal.
Claim 33
Dependent Claim
16 words
A composite material produced by the process of claim 9 wherein said matrix is a metal.
Claim 34
Dependent Claim
10 words
A composite material produced by the process of claim 10.
Claim 35
Dependent Claim
10 words
A composite material produced by the process of claim 11.
Claim 36
Dependent Claim
10 words
A composite material produced by the process of claim 12.
Claim 37
Dependent Claim
10 words
A composite material produced by the process of claim 26.
Claim 38
Dependent Claim
16 words
A composite material produced by the process of claim 14 wherein said matrix is a metal.
Claim 39
Dependent Claim
16 words
A composite material produced by the process of claim 15 wherein said matrix is a metal.
Claim 40
Dependent Claim
10 words
A composite material produced by the process of claim 23.
Claim 41
Dependent Claim
10 words
A composite material produced by the process of claim 21.
Claim 42
Dependent Claim
16 words
A composite material produced by the process of claim 22 wherein said matrix is a metal.
Claim 43
Dependent Claim
10 words
A composite material produced by the process of claim 13.
Claim 44
Dependent Claim
16 words
A composite material produced by the process of claim 19 wherein said matrix is a metal.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-02-28 | 1992-08-29 | 1993-02-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-02-28 | 1996-08-29 | 1997-02-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-02-28 | 2000-08-29 | 2001-02-28 | $7700.00 | Window Closed / Lapsed |