US4808361A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for forming an in-mold coated fiber reinforced part
Assignee: Aerojet Rocketdyne Holdings Inc
•
Filing: 1987-03-16
•
Granted: 1989-02-28
•
Expires: 2007-03-16
Abstract
Abstract A method of making a fiber reinforced part by compression molding under heat and pressure a glass fiber reinforced thermosetting resin composition at an initial high pressure for a short period of time and then substantially reducing the pressure for a longer period of time to form an almost cured FRP part at which time there is applied to the exterior or outer surface of the FRP part an in-mold coating composition and heat and pressure are continued to cure the in-mold coating composition and to complete the cure of the FRP part. During the molding process the temperature gradient across, or the temperature non-uniformities of, the molding or working surfaces of the mold halves is less than about 5° C.
Inventors
- 👤 Jose' M. Castro
- 👤 Elliott J. Straus
- 👤 Henry Shanoski
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 22:40
CPC Classifications
B; B29; B29C; B29C43/00; B29C43/02; B29C43/14; B29C37/00; B29C37/0025; B29C37/0028; B29C70/00; B29C70/04; B29C70/28; B29C70/40; B29C70/42; B29C70/46; B29K; B29K2105/00; B29K2105/24; B29K2105/243; Y; Y10; Y10S; Y10S264/00; Y10S264/59; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31551; Y10T428/31565; Y10T428/31573; Y10T428/31576
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
249 words
In a method of forming an in-mold coated fiber reinforced part in a heated compression mold having two parts forming a cavity for molding, said method comprising placing a curable glass fiber reinforced thermosetting resin composition on one of said heated halves of said mold and applying heat and pressure to form a glass-fiber reinforced part, applying a thermosetting in-mold coating composition to at least one surface of said part and applying heat and pressure to said coated part, and removing said coated fiber reinforced part from the mold, the improvement comprising: (1) forming a glass fiber reinforced part by closing the mold with a pressure sufficient to force the glass fiber reinforced thermosetting resin composition to flow between the mold parts to conform to the configuration defined by the closed mold at a pressure of from about 820 to about 1200 psi for from about 5 to about 12 seconds and subsequently reducing the pressure to from about 80 to about 330 psi for from about 30 to about 100 seconds to effect about 90% cure of said composition, all at a temperature of from about 147° to about 151° C., (2) applying a thermosetting in-mold coating composition on the outer surface of the fiber reinforced part and applying pressure and completing the cure of said fiber reinforced part, and (3) maintaining the difference in temperature between non-uniformities across the molding surfaces of said mold halves at less than about 5° C. during the molding and curing steps.
Claim 2
Dependent Claim
249 words
In a method of forming an in-mold coated fiber reinforced part in a heated compression mold having two parts forming a cavity for molding, said method comprising placing a curable glass fiber reinforced thermosetting resin composition on one of said heated halves of said mold and applying heat and pressure to form a glass-fiber reinforced part, applying a thermosetting in-mold coating composition to at least one surface of said part and applying heat and pressure to said coated part, and removing said coated fiber reinforced part from the mold, the improvement comprising: (1) forming a glass fiber reinforced part by closing the mold with a pressure sufficient to force the glass fiber reinforced thermosetting resin composition to flow between the mold parts to conform to the configuration defined by the closed mold at a pressure of from about 820 to about 1200 psi for from about 5 to about 12 seconds and subsequently reducing the pressure to from about 80 to about 330 psi for from about 30 to about 100 seconds to effect about 90% cure of said composition, all at a temperature of from about 147° to about 151° C., (2) applying a thermosetting in-mold coating composition on the outer surface of the fiber reinforced part and applying pressure and completing the cure of said fiber reinforced part, and (3) maintaining the difference in temperature between non-uniformities across the molding surfaces of said mold halves at less than about 5° C. during the molding and curing steps.
Claim 3
Independent Claim
232 words
The method which comprises in a heated compression mold having two halves forming a cavity for molding (1) placing a curable glass fiber reinforced thermosetting resin composition on one of said heated halves of said mold, (2) closing the mold to force the composition to flow between the mold halves to conform to the configuration defined by the mold halves at a pressure of from about 820 to 1200 psi for from about 5 to 12 seconds, (3) reducing the pressure to from about 80 to 330 psi for from about 30 to 100 seconds to effect at least about 90% cure of said composition to form an FRP part, (4) the temperature during steps (1) to (3) being from about 147° to 151° C., (5) applying a thermosetting in-mold coating composition on the outer surface of the FRP part at a pressure of from about 80 to 400 psi and at a temperature of from about 143° to 154° C. for from about 0.5 to 180 seconds to cure said in-mold coating composition to the surface of said FRP part while completing the cure of said FRP part, (6) maintaining the temperature non-uniformities across the molding surfaces of said mold halves at less than about 5° C. during the entire molding and in-mold coating steps 1 to 3 and 5 and, (7) removing the in-mold coated FRP part from the mold.
Claim 4
Independent Claim
232 words
The method which comprises in a heated compression mold having two halves forming a cavity for molding (1) placing a curable glass fiber reinforced thermosetting resin composition on one of said heated halves of said mold, (2) closing the mold to force the composition to flow between the mold halves to conform to the configuration defined by the mold halves at a pressure of from about 820 to 1200 psi for from about 5 to 12 seconds, (3) reducing the pressure to from about 80 to 330 psi for from about 30 to 100 seconds to effect at least about 90% cure of said composition to form an FRP part, (4) the temperature during steps (1) to (3) being from about 147° to 151° C., (5) applying a thermosetting in-mold coating composition on the outer surface of the FRP part at a pressure of from about 80 to 400 psi and at a temperature of from about 143° to 154° C. for from about 0.5 to 180 seconds to cure said in-mold coating composition to the surface of said FRP part while completing the cure of said FRP part, (6) maintaining the temperature non-uniformities across the molding surfaces of said mold halves at less than about 5° C. during the entire molding and in-mold coating steps 1 to 3 and 5 and, (7) removing the in-mold coated FRP part from the mold.
References Cited (Backward Citations)
US3681483A
Cited
GB1457935A
Cited
US4076788A
Cited
US4367192A
Cited
US4353857A
Cited
US4473215A
Cited
US4489031A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-02-28 | 1992-08-29 | 1993-02-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-02-28 | 1996-08-29 | 1997-02-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-02-28 | 2000-08-29 | 2001-02-28 | $7700.00 | Window Closed / Lapsed |