Mercury retention structure for introduction of measured amounts of mercury into a lamp and method of making the retention structure

Claim 2

Mercury-containing or mercury-alloy-containing retention structure, particularly to introduce liquid mercury or liquid mercury alloy into a discharge lap, in a predetermined quantity, comprising, a predetermined quantity of liquid mercury or mercury alloy, a porous pressed body retaining in its pores the predetermined quantity of mercury or mercury alloy, said porous pressed body comprising a metal which has the characteristics of: the melting point of the metal is over 250° C; the metal of the body does not form an alloy with mercury; the metal can be wetted by mercury; and wherein said metal comprises (i) more than 50%, by weight, of iron, and (ii) chromium and nickel.

Claim 3

In a method of manufacturing a discharge lamp, the step of introducing a pill or pellet comprising the mercury or mercury alloy retention structure as claimed in claim 1 into the discharge vessel of a fluorescent lamp.

Claim 4

In combination with an electric discharge lamp, a pill or pellet comprising the mercury or mercury alloy retention element of claim 1, wherein said body retains liquid mercury, or a liquid mercury alloy and, by weight, has the composition: 25% to 65% metal 75% to 35% liquid mercury or liquid mercury alloy.

Claim 5

Method of making a liquid mercury or liquid mercury alloy retention element, for handling of liquid mercury or liquid mercury alloy, and particularly for introduction of minute amounts of mercury or mercury alloy into a discharge vessel of a discharge lamp, comprising, the steps of (a) introducing the mercury or mercury alloy in an electrolysis vessel (1) having a metal salt solution therein and an anode (5) of the corresponding metal, wherein the metal comprises an element which, solely or as a mixture or alloy, does not form an alloy with mercury or the mercury alloy, and is wetted by mercury, (b) enriching the mercury or mercury alloy with the respective metal of the salt solution by electrolytic enrichment to form a mercury-metal suspension; (c) coating the resulting mercury-metal suspension with aqueous-free glycerine and tempering said coated suspension at a temperature of at least 100° C.; (d) decanting the glycerine, washing the suspension product, and drying the suspension product; (e) filtering off excess non-absorbed mercury or mercury alloy and forming a filter cake; (f) introducing the resulting filter cake into a press and pressing-out excess mercury or mercury alloy under high pressure; and (g) pulverizing the then brittle pressed body, and forming from the resulting powder, said retention elements of predetermined weight or dimension.

Claim 6

Method of making a liquid mercury or liquid mercury alloy retention element, for handling of liquid mercury or liquid mercury alloy, and particularly for introduction of minute amounts of mercury or mercury alloy into a discharge vessel of a discharge lamp, comprising, the steps of (a) introducing the mercury or mercury alloy in an electrolysis vessel (1) having a metal salt solution therein and an anode (5) of the corresponding metal, wherein the metal comprises an element which, solely or as a mixture or alloy, does not form an alloy with mercury or the mercury alloy, and is wetted by mercury, (b) enriching the mercury or mercury alloy with the respective metal of the salt solution by electrolytic enrichment to form a mercury-metal suspension; (c) coating the resulting mercury-metal suspension with aqueous-free glycerine and tempering said coated suspension at a temperature of at least 100° C.; (d) decanting the glycerine, washing the suspension product, and drying the suspension product; (e) filtering off excess non-absorbed mercury or mercury alloy and forming a filter cake; (f) introducing the resulting filter cake into a press and pressing-out excess mercury or mercury alloy under high pressure; and (g) pulverizing the then brittle pressed body, and forming from the resulting powder, said retention elements of predetermined weight or dimension.

Claim 7

The method of claim 4, including, in step (a), adding ammonium sulfate to increase the conductivity of the electrolyte.

Claim 8

The method of claim 4, including, in step (a), adding ethanol to the electrolyte vessel to inhibit anodic oxidation.

Claim 9

The method of claim 4, including, in steps (a) and (b), the step of stirring the mixture of mercury or mercury alloy and the metal salt solution essentially continuously with a stirrer (8).

Claim 10

The method of claim 4, wherein said steps (a) and (b) are carried out in a continuous process in the vessel (1) including the step of drawing-off from the bottom of the vessel the formed mercury-or mercury alloy-metal suspension and adding mercury or mercury alloy at the top of the vessel.

Claim 11

The method of claim 4, wherein the step (f) of pressing-out excess mercury or mercury alloy comprises introducing the filter cake into a bore of a steel cylinder (13); and pressing-out the excess mercury or mercury alloy by applying a high pressure to a stamp o plunger (17) fitting into the bore, while permitting the mercury or mercury alloy to escape from the bore through minute openings in a bottom of the steel cylinder (13).

Claim 12

The method of claim 4, wherein a plurality of electrolyte vessels are utilized, each having a respective anode of different metals, and an electrolyte of a different metal salt therein; carrying out the steps (a) and (b) in the respective electrolyte vessels (1) to form the respective mercury-or mercury alloy- metal suspensions; and then, before carrying out the step (c), carrying out the further step of mixing the respective mercury or mercury alloy metal suspensions in predetermined proportions.

Claim 13

The method of claim 10, wherein the metals of the metal salt solutions and the anodes in the respective electrolysis vessels comprise iron and copper, respectively.

Claim 14

The method of claim 11, wherein the proportion of metals of the resulting mercury or mercury alloy metal suspension is: 75% to 99.5% iron remainder, to 100%, 25% to 0.5% copper, percentages by weight.

Claim 15

The method of claim 10, wherein the metals of the metal salt solutions and the anodes in the respective electrolysis vessels comprise nickel and copper, respectively.

Claim 16

The method of claim 13, wherein the proportion of metals of the resulting mercury or mercury alloy metal suspension is: 55% to 80% nickel remainder, to 100%, 45% to 20% copper, percentages by weight.

Claim 17

The method of claim 10, wherein the metals of the metal salt solutions and the anodes in the respective electrolysis vessels comprises iron, chromium and nickel, respectively.

Claim 18

The method of claim 15, wherein the proportion of metals in the resulting mercury or mercury alloy metal suspension is: 65% to 75% iron 12% to 25% chromium remainder, to 100%, 23% to 0% nickel.

Claim 19

The method of claim 4, wherein said step (f) of pressing out the excess mercury or mercury alloy comprises subjecting the filter cake to a pressure of at least 5·10 -7 Pascal; and controlling the remaining proportion, by weight, of mercury or mercury alloy within the filter cake by controlling the pressure in the direction of reducing the proportion of mercury or mercury alloy to said metal upon increase of pressure.

Claim 20

The method of claim 4, wherein said step (g) forming said retention element comprises forming a pill or pellet of a diameter in the order of about 1.5 mm and having a height or thickness of up to about 0.5 mm.

Claim 21

The method of claim 4, wherein the metal, which, besides the mercury, forms the major metallic proportion of the mercury-metal suspension, comprises an element of the fourth to the eighth subgroup of the periodic system.

Claim 22

Mercury-containing or mercury-alloy-containing retention structure, particularly to introduce liquid mercury or liquid mercury alloy into a discharge lamp, in a predetermined quantity, comprising, a predetermined quantity of liquid mercury or mercury alloy, a porous pressed body retaining in its pores the predetermined quantity of mercury o mercury alloy, said porous pressed body comprising a metal which has the characteristics of: the melting point of the metal is over 250° C; the metal of the body does not form an alloy with mercury; the metal can be wetted by mercury; and wherein said metal comprises more than 50%, by weight of iron, and (ii) copper.

Claim 23

Mercury-containing or mercury-alloy-containing retention structure, particularly to introduce liquid mercury or liquid mercury alloy into a discharge lamp, in a predetermined quantity, comprising, a predetermined quantity of liquid mercury or mercury alloy, a porous pressed body retaining in its pores the predetermined quantity of mercury o mercury alloy, said porous pressed body comprising a metal which has the characteristics of: the melting point of the metal is over 250° C; the metal of the body does not form an alloy with mercury; the metal can be wetted by mercury; and wherein said metal comprises more than 50%, by weight of iron, and (ii) copper.

Claim 24

The structure of claim 20, wherein said metal comprises 75-99.5% iron, remainder, to 100%, 25% to 0.5% copper, all percentages by weight.

Claim 25

Mercury-containing or mercury-alloy-containing retention structure, particularly to introduce liquid mercury or liquid mercury alloy into a discharge lamp, in a predetermined quantity, comprising, a predetermined quantity of liquid mercury or mercury alloy, a porous pressed body retaining in its pores the predetermined quantity of mercury o: mercury alloy, said porous pressed body comprising a metal which has the characteristics of: the melting point of the metal is over 250° C; the metal of the body does not form an alloy with mercury; the metal can be wetted by mercury; and wherein said metal comprises (i) more than 50%, by weight, of nickel, and (ii) copper.

Claim 26

Mercury-containing or mercury-alloy-containing retention structure, particularly to introduce liquid mercury or liquid mercury alloy into a discharge lamp, in a predetermined quantity, comprising, a predetermined quantity of liquid mercury or mercury alloy, a porous pressed body retaining in its pores the predetermined quantity of mercury o: mercury alloy, said porous pressed body comprising a metal which has the characteristics of: the melting point of the metal is over 250° C; the metal of the body does not form an alloy with mercury; the metal can be wetted by mercury; and wherein said metal comprises (i) more than 50%, by weight, of nickel, and (ii) copper.

Claim 27

The structure of claim 22, wherein said metal comprises 55-80% nickel, remainder, to 100%, 45% to 20% copper, all percentages by weight.

Claim 28

Mercury-containing or mercury-alloy-containing retention structure, particularly to introduce liquid mercury or liquid mercury alloy into a discharge lamp, in a predetermined quantity, comprising, a predetermined quantity of liquid mercury or mercury alloy, a porous pressed body retaining in its pores the predetermined quantity of mercury or mercury alloy, said porous pressed body comprising a metal which has the characteristics of: the melting point of the metal is over 250° C; the metal of the body does not form an alloy with mercury; the metal can be wetted by mercury; and wherein said metal comprises 65-75% of iron, 12-25% of chromium, and 23-0% of nickel, all percentages by weight.

Claim 29

Mercury-containing or mercury-alloy-containing retention structure, particularly to introduce liquid mercury or liquid mercury alloy into a discharge lamp, in a predetermined quantity, comprising, a predetermined quantity of liquid mercury or mercury alloy, a porous pressed body retaining in its pores the predetermined quantity of mercury or mercury alloy, said porous pressed body comprising a metal which has the characteristics of: the melting point of the metal is over 250° C; the metal of the body does not form an alloy with mercury; the metal can be wetted by mercury; and wherein said metal comprises 65-75% of iron, 12-25% of chromium, and 23-0% of nickel, all percentages by weight.

Claim 32

The method of claim 25 wherein the step of forming the suspension comprises electrolytically enriching the mercury or mercury alloy with said metal or metal alloy in an electro-winning or electro-plating process wherein the mercury or mercury alloy is used as a cathode.

Claim 33

The method of claim 26, wherein the electrolytically enriching step comprises introducing the mercury or mercury alloy into an electrolysis cell as said cathode, said cell containing an electrolyte; using the metal or metal alloy as an anode; and using, as the electrolyte, a solution containing ions of said metal or metal alloy.

Claim 34

The method of claim 27, wherein the filtering step further comprises increasing the crystal size of the suspension before filtering by coating the suspension with aqueous-free glycerine and tempering the coated suspension at a temperature of at least 100° C.