Rubber laminate
Assignee: Toyoda Gosei Co Ltd
•
Filing: 1987-09-01
•
Granted: 1989-02-21
•
Expires: 2007-09-01
Abstract
Abstract This invention is directed to a rubber laminate that produces a sufficient bonding strength between a FKM layer and a NBR layer. The FKM layer is made of a FKM compound containing a polyol vulcanization system in which a vulcanization accelerator is incorporated in an amount more than usual, or a FKM compound of peroxide vulcanization system in which a vulcanizing agent and accelerator used for the polyol vulcanization system is incorporated along with the peroxide vulcanization system. The NBR layer is made of a NBR compound incorporated with an oxide or hydroxide of a metal selected from Goups II to IV of the Periodic Table such as calcium hydroxide in an amount more than usual. The rubber laminate of this invention is suitable for rubber hoses and rubber diaphragm.
Inventors
- 👤 Masatoshi Sugimoto
- 👤 Toshiki Kurosaki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 11:38
CPC Classifications
B; B32; B32B; B32B25/00; B32B25/14; B32B25/10; B32B38/00; B32B2038/0052; B32B2038/0076; B32B2305/00; B32B2305/72; B32B2319/00; Y; Y10; Y10T; Y10T428/00; Y10T428/13; Y10T428/1352; Y10T428/1386; Y10T428/31504; Y10T428/31855; Y10T428/31909; Y10T428/31928; Y10T428/31935
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
109 words
A rubber laminate which comprises a FKM layer of the following compound (A) and a NBR layer of the following compound (B), said layers being bonded together through vulcanization, wherein (A) is a FKM compound containing a polyol vulcanization system in which the polymer is vinylidene fluoride-propylene hexafluoride copolymer, the vulcanization agent is an aromatic polyol in an amount of 1.3 to 2 PHR and the vulcanization accelerator is an organic phosphonium salt or quaternary ammonium salt, said vulcanization accelerator being present in an amount of 0.5 to 2.2 PHR, and (B) is a NBR compound having incorporated therein calcium hydroxide in an amount of 5 to 30 PHR.
Claim 2
Dependent Claim
109 words
A rubber laminate which comprises a FKM layer of the following compound (A) and a NBR layer of the following compound (B), said layers being bonded together through vulcanization, wherein (A) is a FKM compound containing a polyol vulcanization system in which the polymer is vinylidene fluoride-propylene hexafluoride copolymer, the vulcanization agent is an aromatic polyol in an amount of 1.3 to 2 PHR and the vulcanization accelerator is an organic phosphonium salt or quaternary ammonium salt, said vulcanization accelerator being present in an amount of 0.5 to 2.2 PHR, and (B) is a NBR compound having incorporated therein calcium hydroxide in an amount of 5 to 30 PHR.
Claim 3
Dependent Claim
30 words
A rubber laminate as set forth in claim 1, wherein said NBR compound is an acrylonitrile-butadiene copolymer containing 15 to 55% acrylonitrile and the polyol vulcanization system includes other auxiliaries.
Claim 4
Dependent Claim
110 words
A rubber laminate which comprises a FKM layer of the following compound (A) and a NBR layer of the following compound (B), said layers being bonded together through vulcanization, wherein (A) is a FKM compound containing a polyol vulcanization system in which the polymer is vinylidene fluoride-propylene hexafluoride-ethylene tetrafluoride terpolymer, the vulcanization agent is an aromatic polyol in an amount of 1.3 to 2 PHR and the vulcanization accelerator is an organic phosphonium salt or quaternary ammonium salt, said vulcanization accelerator being present in an amount of 0.8 to 2.7 PHR, and (B) is a NBR compound having incorporated therein calcium hydroxide in an amount of 5 to 30 PHR.
Claim 5
Dependent Claim
110 words
A rubber laminate which comprises a FKM layer of the following compound (A) and a NBR layer of the following compound (B), said layers being bonded together through vulcanization, wherein (A) is a FKM compound containing a polyol vulcanization system in which the polymer is vinylidene fluoride-propylene hexafluoride-ethylene tetrafluoride terpolymer, the vulcanization agent is an aromatic polyol in an amount of 1.3 to 2 PHR and the vulcanization accelerator is an organic phosphonium salt or quaternary ammonium salt, said vulcanization accelerator being present in an amount of 0.8 to 2.7 PHR, and (B) is a NBR compound having incorporated therein calcium hydroxide in an amount of 5 to 30 PHR.
Claim 6
Dependent Claim
30 words
A rubber laminate as set forth in claim 3, wherein said NBR compound is an acrylonitrile-butadiene copolymer containing 15 to 55% acrylonitrile and the polyol vulcanization system includes other auxiliaries.
Claim 7
Dependent Claim
110 words
A rubber laminate which comprises a FKM layer of the following compound (A) and a NBR layer of the following compound (B), said layers being bonded together through vulcanization, wherein (A) is a FKM compound containing a peroxide vulcanization system comprising an organic peroxide, an acid acceptor, an inorganic accelerator, and a co-crosslinking agent and a polyol vulcanization system comprising an aromatic polyol compound as the vulcanization agent in an amount of 0.5-5 PHR and an organic phosphonium salt or quaternary ammonium salt as vulcanization accelerator in an amount of 0.5-5 PHR, and (B) is NBR compound having incorporated therein calcium hydroxide in an amount of 5 to 30 PHR.
Claim 8
Dependent Claim
110 words
A rubber laminate which comprises a FKM layer of the following compound (A) and a NBR layer of the following compound (B), said layers being bonded together through vulcanization, wherein (A) is a FKM compound containing a peroxide vulcanization system comprising an organic peroxide, an acid acceptor, an inorganic accelerator, and a co-crosslinking agent and a polyol vulcanization system comprising an aromatic polyol compound as the vulcanization agent in an amount of 0.5-5 PHR and an organic phosphonium salt or quaternary ammonium salt as vulcanization accelerator in an amount of 0.5-5 PHR, and (B) is NBR compound having incorporated therein calcium hydroxide in an amount of 5 to 30 PHR.
Claim 9
Dependent Claim
30 words
A rubber laminate as set forth in claim 5, wherein said NBR compound is an acrylonitrile-butadiene copolymer containing 15 to 55% acrylonitrile and the peroxide-polyol vulcanization systems include other auxiliaries.
Claim 10
Dependent Claim
20 words
A rubber laminate as set forth in claim 5 wherein said FKM compound is a vinylidene fluoride-propylene hexafluoride-ethylene tetrafluoride terpolymer.
Claim 11
Dependent Claim
125 words
A rubber laminate which comprises a FKM layer of the following compound (A) in which the polymer is vinylidene fluoride-propylene hexafluoride copolymer, and a NBR layer of the following compound (B) in which the polymer is an acrylonitridebutadiene copolymer containing 15 to 55% acrylonitrile, said layers being bonded together through vulcanization, wherein: (A) is a FKM compound containing a polyol vulcanization system agent comprising an aromatic polyol in an amount of 1.3 to 2 phr as the vulcanization agent, and an organic phosphonium salt or quaternary ammonium salt as the vulcanization accelerator in an amount of 0.5 to 2.2 PHR, and other auxiliaries, and (B) is a NBR compound having incorporated therein calcium hydroxide in an amount of 5 to 30 PHR and other auxiliaries.
Claim 12
Dependent Claim
125 words
A rubber laminate which comprises a FKM layer of the following compound (A) in which the polymer is vinylidene fluoride-propylene hexafluoride copolymer, and a NBR layer of the following compound (B) in which the polymer is an acrylonitridebutadiene copolymer containing 15 to 55% acrylonitrile, said layers being bonded together through vulcanization, wherein: (A) is a FKM compound containing a polyol vulcanization system agent comprising an aromatic polyol in an amount of 1.3 to 2 phr as the vulcanization agent, and an organic phosphonium salt or quaternary ammonium salt as the vulcanization accelerator in an amount of 0.5 to 2.2 PHR, and other auxiliaries, and (B) is a NBR compound having incorporated therein calcium hydroxide in an amount of 5 to 30 PHR and other auxiliaries.
References Cited (Backward Citations)
US2833752A
Cited
US4259463A
Cited
US4361608A
Cited
JPS5749391A
Cited
EP0089162A1
Cited
US4457799A
Cited
US4394205A
Cited
JPS5933304A
Cited
US4395462A
Cited
US4563393A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-02-21 | 1992-08-22 | 1993-02-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-02-21 | 1996-08-22 | 1997-02-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-02-21 | 2000-08-22 | 2001-02-21 | $7700.00 | Window Closed / Lapsed |