Recovery of vinyl chloride resin with aid of screen
Assignee: Zeon Corp
•
Filing: 1986-01-29
•
Granted: 1989-02-07
•
Expires: 2006-01-29
Abstract
Abstract A recovery method of vinyl chloride resin which comprises formulating an aggregate of vinyl chloride resin by adding to an aqueous dispersion of vinyl chloride resin an organic liquid which is difficultly soluble in water and does not dissolve or swell vinyl chloride resin and mixing the two; dehydrating the aggregate; and drying the same to recover granular vinyl chloride resin, the characteristic feature residing in that said aqueous dispersion is the one which has passed through the screen of 20 to 150-micron meshes.
Inventors
- 👤 Masaaki Nishina
- 👤 Junsei Kawahuti
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 15:52
CPC Classifications
C; C08; C08J; C08J3/00; C08J3/12; C08J3/16; C08F; C08F6/00; C08F6/14; C08J2327/00; C08J2327/02; C08J2327/04; C08J2327/06
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
180 words
A method for recovering vinyl chloride resin selected from the group consisting of vinyl chloride homopolymer and vinyl chloride copolymers composed of at least 70% by weight of vinyl chloride and up to 30% by weight of at least one olefinic monomer copolymerizable with vinyl chloride, said homopolymer or copolymer being prepared by emulsion polymerization, fine suspension polymerization or suspension polymerization, from an aqueous dispersion thereof, said aqueous dispersion having a vinyl resin content of from 10 to 70% by weight, which comprises (a) passing the aqueous dispersion of the vinyl chloride resin through a screen of 20 to 150 micron mesh; (b) mixing the aqueous dispersion which has passed through said screen with an organic liquid which is difficultly soluble in water and does not dissolve or swell vinyl chloride resin, said mixing causing aggregation of the dispersed vinyl chloride resin; (c) separating and removing the aqueous phase from the liquid mixture containing the resin aggregate obtained in step (b); and (d) dehydrating and drying the resin aggregate from which the aqueous phase has been separated in step (c).
Claim 2
Independent Claim
180 words
A method for recovering vinyl chloride resin selected from the group consisting of vinyl chloride homopolymer and vinyl chloride copolymers composed of at least 70% by weight of vinyl chloride and up to 30% by weight of at least one olefinic monomer copolymerizable with vinyl chloride, said homopolymer or copolymer being prepared by emulsion polymerization, fine suspension polymerization or suspension polymerization, from an aqueous dispersion thereof, said aqueous dispersion having a vinyl resin content of from 10 to 70% by weight, which comprises (a) passing the aqueous dispersion of the vinyl chloride resin through a screen of 20 to 150 micron mesh; (b) mixing the aqueous dispersion which has passed through said screen with an organic liquid which is difficultly soluble in water and does not dissolve or swell vinyl chloride resin, said mixing causing aggregation of the dispersed vinyl chloride resin; (c) separating and removing the aqueous phase from the liquid mixture containing the resin aggregate obtained in step (b); and (d) dehydrating and drying the resin aggregate from which the aqueous phase has been separated in step (c).
Claim 3
Dependent Claim
38 words
The method of claim 1 in which the amount of the organic liquid to be added ranges from 0.5 to 30 parts by weight per 100 parts by weight of the vinyl chloride resin in the aqueous dispersion.
Claim 4
Dependent Claim
16 words
The method of claim 1 in which the organic liquid is selected from alkyl phthalate-type plasticizers.
Claim 5
Dependent Claim
34 words
The method of claim 1 in which the mixing of the organic liquid with the aqueous dispersion of vinyl chloride resin is performed at a temperature within the range of 20° to 70° C.
Claim 6
Dependent Claim
22 words
The method of claim 1 which further comprises (a)' subjecting the aqueous dispersion to an ultrasonic dispersion treatment prior to step (a).
Claim 7
Dependent Claim
128 words
The method of claim 1 wherein the organic liquid is mixed with the aqueous dispersion at a temperature of from 20° C. to 70° C. in an amount of from 0.5 to 30 parts by weight per 100 parts by weight of the vinyl chloride resin in the aqueous dispersion, said organic liquid having a melting point not higher than 20° C. and a boiling point not lower than 200° C. and being selected from the group consisting of (1) alkylphthalate plasticizers, (2) aromatic carboxylate plasticizers, (3) aliphatic dibasic acid ester plasticizers, (4) phosphate plasticizers, (5) aliphatic glycol ester plasticizers, (6) polyester plasticizers, (7) fatty acid ester secondary plasticizers, epoxy secondary plasticizers, paraffin secondary plasticizers, aliphatic dibasic acid ester secondary plasticizers, (8) petroleum diluents and (9) liquid lubricants.
Claim 8
Dependent Claim
21 words
The method of claim 1 wherein in step (a) the aqueous dispersion is passed through a screen of 44 micron mesh.
Claim 9
Dependent Claim
21 words
The method of claim 1 wherein in step (a) the aqueous dispersion is passed through a screen of 77 micron mesh.
Claim 10
Dependent Claim
21 words
The method of claim 1 wherein in step (a) the aqueous dispersion is passed through a screen of 105 micron mesh.
References Cited (Backward Citations)
US2613191A
Cited
US2624718A
Cited
US3545093A
Cited
DE2453909A1
Cited
JPS57209905A
Cited
US4604454A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-02-07 | 1992-08-08 | 1993-02-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-02-07 | 1996-08-08 | 1997-02-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-02-07 | 2000-08-08 | 2001-02-07 | $7700.00 | Window Closed / Lapsed |