Process to permit improvement of functional properties of polyolefin articles by electron-beam initiated polymerization
Assignee: EG Technology Partners LP
•
Filing: 1987-10-19
•
Granted: 1989-02-07
•
Expires: 2007-10-19
Abstract
Abstract A process is described for modifying the surface of polymers such as polyolefins and the like to improve the wetability by barrier and other coatings and to enhance interlayer adhesion by graft polymerization through initiation by electron-beam radiation, optionally with an added electron energy acceptor.
Inventors
- 👤 John E. Wyman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 11:31
CPC Classifications
B; B32; B32B; B32B3/00; B32B3/26; B32B3/28; C; C08; C08J; C08J5/00; C08J5/12; C08J5/124; C08J7/00; C08J7/04; C08J7/0427; C08J7/043; C08J7/048; C08J7/12; C08J7/16; C08J7/18; C08J2323/00; C08J2323/02; C08J2483/00; C08J2483/02; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31652; Y10T428/31663
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
95 words
A process for modifying the surface of a polyolefin film and the like to increase the effective surface tension so as to permit adhesion thereto of a barrier coating, that comprises, hydrolyzing an organofunctional silane; coating the surface of a polyolefin film with the hydrolyzed silane and drying the same; and electron-beam irradiating the coated surface to initiate the further polymerization of the silane-to-silane structure in the hydrolyzed silane layer and also to graft the same to the polyolefin surface; and coating the silane-surface grafted polyolefin film with a polymer having the desired barrier properties.
Claim 2
Dependent Claim
95 words
A process for modifying the surface of a polyolefin film and the like to increase the effective surface tension so as to permit adhesion thereto of a barrier coating, that comprises, hydrolyzing an organofunctional silane; coating the surface of a polyolefin film with the hydrolyzed silane and drying the same; and electron-beam irradiating the coated surface to initiate the further polymerization of the silane-to-silane structure in the hydrolyzed silane layer and also to graft the same to the polyolefin surface; and coating the silane-surface grafted polyolefin film with a polymer having the desired barrier properties.
Claim 3
Dependent Claim
26 words
A process as claimed in claim 1 and in which the electron-beam irradiating is effected with 2-5 megarads of electron beam energy of about 180 kV.
Claim 4
Dependent Claim
28 words
A process as claimed in claim 1 and in which the polymer-coated silane-grafted film is further electron-beam irradiated to bond the polymer coating to the crosslinked silane coating.
Claim 5
Dependent Claim
29 words
A process as claimed in claim 1 and in which the last-named polymer is deposited in the form of latex which dries out to form a continuous polymer film.
Claim 6
Dependent Claim
45 words
A process as claimed in claim 1 and in which an acrylate ester monomer or monomer mixture is coated on the grafted polysiloxane, and the same is initiated with electron beam radiation to polymerize the coating and simultaneously to graft the coating to the siloxane.
Claim 7
Dependent Claim
26 words
A process as claimed in claim 1 and in which the latex coating is one of any acrylate latex, vinyl acetate latex, and vinylidene chloride latex.
Claim 8
Dependent Claim
77 words
A process as claimed in claim 1 and in which the coating is produced from a monomer of the type that normally does not produce free radicals for polymerization initiation on electron-beam radiation such as acrylonitrile and the like, and the step is performed for rendering the monomer useful to polymerize as a coating on the silane coating under electron beam radiation by adding an acceptor thereto that, under such radiation, forms free radicals to initiate polymerization.
Claim 9
Dependent Claim
22 words
A process as claimed in claim 1 and in which said acceptor is of the stable peroxide type such as benzoyl peroxide.
Claim 10
Dependent Claim
13 words
A barrier-coated polyolefin product manufactured in accordance with the process of claim 1.
Claim 11
Dependent Claim
72 words
A process for modifying the surface of a polyolefin film and the like to increase the effective surface tension to permit adhesion thereto of a barrier coating, that comprises, applying to the surface of a polyolefin film and the like both an organosilane and a latex having the desired barrier properties; and electron-beam irradiating the same to graft the silane to the film and the latex to the silane while polymerizing both.
Claim 12
Dependent Claim
72 words
A process for modifying the surface of a polyolefin film and the like to increase the effective surface tension to permit adhesion thereto of a barrier coating, that comprises, applying to the surface of a polyolefin film and the like both an organosilane and a latex having the desired barrier properties; and electron-beam irradiating the same to graft the silane to the film and the latex to the silane while polymerizing both.
References Cited (Backward Citations)
No citation records indexed.
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-02-07 | 1992-08-08 | 1993-02-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-02-07 | 1996-08-08 | 1997-02-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-02-07 | 2000-08-08 | 2001-02-07 | $7700.00 | Window Closed / Lapsed |