Method of crystallizing a zeolite on the surface of a monolithic ceramic substrate
Assignee: Corning Glass Works
•
Filing: 1987-10-28
•
Granted: 1989-01-24
•
Expires: 2007-10-28
Abstract
Abstract A method is provided of crystallizing strong-bound zeolites on the surfaces of a monolithic ceramic substrate by hydrothermally treating the substrate, in the presence of active silica, with a caustic bath to zeolitize the silica. According to various embodiments of the invention, the active silica can be present as a component of the caustic bath, in the form of a dried coating pre-deposited on the substrate, or as a separate phase of the monolithic substrate, homogeneous dispersed within the ceramic material.
Inventors
- 👤 Irwin M. Lachman
- 👤 Mallanagouda D. Patil
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 23:32
CPC Classifications
B; B01; B01J; B01J37/00; B01J37/02; B01J37/0201; B01J37/0207; B01J29/00; B01J29/04; B01J29/06; B01J29/08; B01J29/082; B01J29/084; B01J29/18; B01J29/40; B01J35/00; B01J35/50; B01J35/56; B01J35/57; B01J35/60; B01J35/61; B01J35/613; B01J37/024; B01J37/0246; C; C04; C04B; C04B41/00; C04B41/45; C04B41/50; C04B41/5025; C04B41/5035; B01J2229/00; B01J2229/60; B01J2229/64
Claims Analysis
Total Claims: 32
Claim 1
Independent Claim
77 words
A method of crystallizing a zeolite on the surfaces of a monolithic ceramic substrate, comprising (a) providing a sintered monolithic substrate having an oxide composition consisting essentially of 45-75% by weight silica, 8-45% by weight alumina, and 7-20% by weight magnesia; and (b) hydrothermally treating the substrate with an aqueous solution comprising sodium oxide or sodium hydroxide and alumina at a temperature and for a time sufficient to crystallize a zeolite on the surfaces of said substrate.
Claim 2
Independent Claim
77 words
A method of crystallizing a zeolite on the surfaces of a monolithic ceramic substrate, comprising (a) providing a sintered monolithic substrate having an oxide composition consisting essentially of 45-75% by weight silica, 8-45% by weight alumina, and 7-20% by weight magnesia; and (b) hydrothermally treating the substrate with an aqueous solution comprising sodium oxide or sodium hydroxide and alumina at a temperature and for a time sufficient to crystallize a zeolite on the surfaces of said substrate.
Claim 3
Dependent Claim
25 words
The method of claim 1 in which the aqueous solution further comprises active silica having a surface area of at least 25 m 2 /g.
Claim 4
Dependent Claim
24 words
The method of claim 2 of crystallizing a X-type zeolite wherein the molar ratios of silica/alumina/sodium oxide/water in the aqueous solution are about 1/0.2-0.5/1.2-1.5/40-60.
Claim 5
Dependent Claim
24 words
The method of claim 2 of crystallizing a Y-type zeolite wherein the molar ratios of silica/alumina/sodium oxide/water in the aqueous solution are about 1/0.04-0.14/0.4-0.6/16-24.
Claim 6
Dependent Claim
24 words
The method of claim 2 of crystallizing a mordenite zeolite wherein the molar ratios of silica/alumina/sodium oxide/water in the aqueous solution are about 1/0.04-0.09/0.11-0.15/20-25.
Claim 7
Dependent Claim
25 words
The method of claim 2 of crystallizing a ZSM-5 zeolite in which the molar ratios of silica/alumina/sodium oxide/water in the aqueous solution are about 1/0-0.04/0.2-0.75/16-20.
Claim 8
Dependent Claim
15 words
The method of claim 6 wherein the aqueous solution further comprises an organic templating agent.
Claim 9
Independent Claim
89 words
A method of crystallizing a zeolite on the surfaces of a monolithic ceramic substrate, comprising (a) providing a substantially sintered monolithic substrate of cordierite, a glass, or a glass-ceramic; (b) contacting said substrate with a strong mineral acid for a time sufficient to produce a weight loss of about 4-32% in the substrate; and (c) hydrothermally treating the substrate with an aqueous solution comprising sodium oxide or sodium hydroxide and alumina at a temperature and for a time sufficient to crystallize a zeolite on the surfaces of said substrate.
Claim 10
Independent Claim
89 words
A method of crystallizing a zeolite on the surfaces of a monolithic ceramic substrate, comprising (a) providing a substantially sintered monolithic substrate of cordierite, a glass, or a glass-ceramic; (b) contacting said substrate with a strong mineral acid for a time sufficient to produce a weight loss of about 4-32% in the substrate; and (c) hydrothermally treating the substrate with an aqueous solution comprising sodium oxide or sodium hydroxide and alumina at a temperature and for a time sufficient to crystallize a zeolite on the surfaces of said substrate.
Claim 11
Dependent Claim
35 words
The method of claim 8 in which the monolithic substrate consists essentially of cordierite and in which the aqueous solution further comprises active silica having a surface area of at least 25 m 2 /g.
Claim 12
Dependent Claim
24 words
The method of claim 9 of crystallizing a X-type zeolite wherein the molar ratios of silica/alumina/sodium oxide/water in the aqueous solution are about 1/0.2-0.5/1.2-1.5/40-60.
Claim 13
Dependent Claim
24 words
The method of claim 9 of crystallizing a Y-type zeolite wherein the molar ratios of silica/alumina/sodium oxide/water in the aqueous solution are about 1/0.04-0.14/0.4-0.6/16-24.
Claim 14
Dependent Claim
24 words
The method of claim 9 of crystallizing a mordenite zeolite wherein the molar ratios of silica/alumina/sodium oxide/water in the aqueous solution are about 1/0.04-0.09/0.11-0.15/20-25.
Claim 15
Dependent Claim
25 words
The method of claim 9 of crystallizing a ZSM-5 zeolite in which the molar ratios of silica/alumina/sodium oxide/water in the aqueous solution are about 1/0-0.04/0.2-0.75/16-20.
Claim 16
Dependent Claim
15 words
The method of claim 13 wherein the aqueous solution further comprises an organic templating agent.
Claim 17
Dependent Claim
41 words
The method of claim 8 further comprising the step prior to said contacting step (b), of providing a dried coating of active silica on said substrate wherein the weight of the coating is 1-45% of the weight of the coated substrate.
Claim 18
Independent Claim
83 words
A method of crystallizing a zeolite on the surface of a monolithic ceramic substrate, comprising (a) providing a substantially sintered monolithic substrate comprising a porous ceramic matrix material and 10-40% by weight, based on the total substrate weight, of active silica dispersed throughout and embedded within the matrix material; and (b) hydrothermally treating said substrate with an aqueous solution comprising sodium oxide and optionally alumina at a temperature and for a time sufficient to crystallize a zeolite on the surfaces of said substrate.
Claim 19
Independent Claim
83 words
A method of crystallizing a zeolite on the surface of a monolithic ceramic substrate, comprising (a) providing a substantially sintered monolithic substrate comprising a porous ceramic matrix material and 10-40% by weight, based on the total substrate weight, of active silica dispersed throughout and embedded within the matrix material; and (b) hydrothermally treating said substrate with an aqueous solution comprising sodium oxide and optionally alumina at a temperature and for a time sufficient to crystallize a zeolite on the surfaces of said substrate.
Claim 20
Dependent Claim
36 words
The method of claim 16 wherein said porous ceramic material consists essentially of cordierite, mullite, zircon, quartz, spinel, feldspar, titania, fused silica, alumina, zirconia, lithium aluminosilicate, kaolin clay, metal, silicon carbide, silicon nitride, or mixtures thereof.
Claim 21
Dependent Claim
36 words
The method of claim 17 wherein the monolithic substrate consists essentially of cordierite, fused silica, mullite, zirconia, or quartz and wherein said active silica has a surface area of at least about 25 m 2 /g.
Claim 22
Dependent Claim
34 words
The method of claim 18 of crystallizing an X-type zeolite wherein the molar ratios of alumina/sodium oxide/water in the aqueous solution are about 0.2-0.5/1.2-1.5/40-60 for each mole of active silica in said monolithic substrate.
Claim 23
Dependent Claim
24 words
The method of claim 19 wherein said monolithic substrate further comprises pre-formed crystals of X-type zeolite dispersed throughout and embedded within the matrix material.
Claim 24
Dependent Claim
34 words
The method of claim 18 of crystallizing a Y-type zeolite wherein the molar ratios of alumina/sodium oxide/water in the aqueous solution are about 0.04-0.14/0.4-0.6/16-24 for each mole of active silica in said monolithic substrate.
Claim 25
Dependent Claim
24 words
The method of claim 21 wherein said monolithic substrate further comprises pre-formed crystals of Y-type zeolite dispersed throughout and embedded within the matrix material.
Claim 26
Dependent Claim
34 words
The method of claim 18 of crystallizing a mordenite zeolite wherein the molar ratios of alumina/sodium oxide/water in the aqueous solution are about 0.04-0.09/0.11-0.15/20-25 for each mole of active silica in said monolithic substrate.
Claim 27
Dependent Claim
24 words
The method of claim 23 wherein said monolithic substrate further comprises pre-formed crystals of mordenite zeolite dispersed throughout and embedded within the matrix material.
Claim 28
Dependent Claim
34 words
The method of claim 18 of crystallizing a ZSM-5 zeolite wherein the molar ratios of alumina/sodium oxide/water in said aqueous solution are about 0-0.04/0.2-0.75/16-20 for each mole of active silica in said monolithic substrate.
Claim 29
Dependent Claim
15 words
The method of claim 25 wherein said aqueous solution further comprises an organic templating agent.
Claim 30
Dependent Claim
24 words
The method of claim 25 wherein said monolithic substrate further comprises pre-formed crystals of silicalite zeolite dispersed throughout and embedded within the matrix material.
Claim 31
Dependent Claim
46 words
The method of claim 16, 20, 22, 24, or 27 further comprising the step, prior to said treating step (b), of providing a dried coating of active silica on said substrate wherein the weight of the coating is 1-45% of the weight of the coated substrate.
Claim 32
Dependent Claim
44 words
The method of claim 16, 20, 22, 24, or 27 further comprising the step, prior to said treating step (b), of contacting said substrate with a strong mineral acid for a time sufficient to produce a weight loss of about 4-32% in the substrate.
References Cited (Backward Citations)
US3244643A
Cited
US3406124A
Cited
US3468815A
Cited
US3523092A
Cited
US3518206A
Cited
US3795631A
Cited
US3730910A
Cited
US3958058A
Cited
US4157375A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-01-24 | 1992-07-25 | 1993-01-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-01-24 | 1996-07-25 | 1997-01-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-01-24 | 2000-07-25 | 2001-01-24 | $7700.00 | Window Closed / Lapsed |