Ionic semiconductor materials and applications thereof
Assignee: T AND G Corp A CT CORP
•
Filing: 1986-10-06
•
Granted: 1989-01-10
•
Expires: 2006-10-06
Abstract
Abstract An ion transport membrane includes 10 to approximately 50 percent by weight of a hydrogel which is dispersed within an inert nonporous matrix material to form a composite wherein the quantity of water that can be absorbed by the composite does not substantially exceed the weight of the composite. The membranes may be used in electrochemical cells, for water purification, as solid polymeric electrolytes, in breathable waterproof coatings, and in numerous other applications for controlled moisture or ion transfer.
Inventors
- 👤 Robert L. Peck
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 14:17
CPC Classifications
G; G01; G01N; G01N27/00; G01N27/26; G01N27/28; G01N27/40; H; H01; H01M; H01M10/00; H01M10/36; H01M12/00; H01M12/04; H01M12/06; H01M4/00; H01M4/02; H01M4/62; H01M50/00; H01M50/40; H01M50/409; H01M50/411; H01M50/414; H01M50/429; H01M8/00; H01M8/08; H01M8/18; H01M8/184; H01M8/188; H01M50/489; Y; Y02; Y02E; Y02E60/00; Y02E60/10; Y02E60/30; Y02E60/50
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
109 words
An ionic semiconductor having an ion transport rate which is temperature dependent, said semiconductor comprising an inert man-made polymeric matrix material and a hydrogel, the molecules of the hydrogel being substantially uniformly dispersed within said matrix material to form a composite structure wherein contact between hydrogel molecules is minimized by the matrix and the formation of channels is thereby limited, the composite allowing the transfer of ions and preventing the passage of un-ionized matter, the hydrogel comprising 10 to approximately 50% by weight of the dry composite, there being sufficient bonding between the hydrogel molecules and the matrix material to prevent substantial leach-out of hydrogel molecules from the composite.
Claim 2
Dependent Claim
109 words
An ionic semiconductor having an ion transport rate which is temperature dependent, said semiconductor comprising an inert man-made polymeric matrix material and a hydrogel, the molecules of the hydrogel being substantially uniformly dispersed within said matrix material to form a composite structure wherein contact between hydrogel molecules is minimized by the matrix and the formation of channels is thereby limited, the composite allowing the transfer of ions and preventing the passage of un-ionized matter, the hydrogel comprising 10 to approximately 50% by weight of the dry composite, there being sufficient bonding between the hydrogel molecules and the matrix material to prevent substantial leach-out of hydrogel molecules from the composite.
Claim 3
Dependent Claim
42 words
The material of claim 1 wherein the current attributable to copper ion diffusion does not exceed 16% of the equilibrium current when the composite separates H 2 SO 4 and CuSO 4 electrolytes and a potential difference is established across the composite.
Claim 4
Dependent Claim
24 words
The material of claim 1 wherein the hydrogel is a synthetic material selected form the group consisting of polyethylene oxide, polyacrylic acid and polyacrylamide.
Claim 5
Dependent Claim
26 words
The material of claim 1 wherein the hydrogel is devised from natural materials selected from the group consisting of hydroxyethy cellulose, gelatin, pectin, cellulose and starch.
Claim 6
Dependent Claim
27 words
The material of claim 1 wherein the matrix is selected from the group consisting of polyvinylidene chloride, polyvinyl chloride, polyvinylidene fluoride, polyethylene, polypropylene, urethane, and phenol formaldehyde.
Claim 7
Dependent Claim
20 words
The material of claim 1 further comprising a coupling agent to facilitate the bonding between the hydrogel and the matrix.
Claim 8
Dependent Claim
26 words
The material of claim 6 wherein the coupling agent is selected from the group consisting of polyacrylic acid, phenolic resin, cellulosic titanate, carbon, lignin and silica.
Claim 9
Dependent Claim
24 words
The material of claim 5 wherein the hydrogel is a synthetic material selected from the group consisting of pclyethylene oxide, polyacrylic acid and polyacrylamide.
Claim 10
Dependent Claim
26 words
The material of claim 5 wherein the hydrogel is devised from natural materials selected from the group consisting of hydroxyethyl cellulose, gelatin, pectin, cellulose and starch.
Claim 11
Dependent Claim
20 words
The material of claim 8 further comprising a coupling agent to facilitate the bonding between the hydrogel and the matrix.
Claim 12
Dependent Claim
26 words
The material of claim 10 wherein the coupling agent is selected from the group consisting of polyacrylic acid, phenolic resin, cellulose titanate, carbon, lignin and silica.
Claim 13
Dependent Claim
20 words
The material of claim 9 further comprising a coupling agent to facilitate the bonding between the hydrogel and the matrix.
Claim 14
Dependent Claim
26 words
The material of claim 12 wherein the coupling agent is selected from the group consisting of polyacrylic acid, phenolic resin, cellulosic titanate, carbon, lignin and silica.
Claim 15
Dependent Claim
42 words
The material of claim 8 wherein the current attributable to copper ion diffusion does not exceed 16% of the equilibrium current when the composite separates H 2 SO 4 and CuSO 4 electrolytes and a potential difference is established across the composite.
Claim 16
Dependent Claim
41 words
The material of claim 9 wherein the current attributable to copper ion diffusion does not exceed 16% of the equilibrium current when the composite separates H 2 SO 4 and CuSO 4 and a potential difference is established across the composite.
Claim 17
Dependent Claim
46 words
The material of claim 1 wherein the hydrogel and the matrix material and their respective proportions in the composite are selected such that the quantity of water absorbed by the composite will be limited to less than the weight of the composite prior to water absorption.
Claim 18
Dependent Claim
46 words
The material of claim 3 wherein the hydrogel and the matrix material and their respective proportions in the composite are selected such that the quantity of water absorbed by the composite will be limited to less than the weight of the composite prior to water absorption.
Claim 19
Dependent Claim
46 words
The material of claim 5 wherein the hydrogel and the matrix material and their respective proportions in the composite are selected such that the quantity of water absorbed by the composite will be limited to less than the weight of the composite prior to water absorption.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-01-10 | 1992-07-11 | 1993-01-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-01-10 | 1996-07-11 | 1997-01-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-01-10 | 2000-07-11 | 2001-01-10 | $7700.00 | Window Closed / Lapsed |