Activation of polyethylene terephthalate materials for improved bonding to adhesives
Assignee: CNA Holdings LLC
•
Filing: 1983-09-21
•
Granted: 1988-12-27
•
Expires: 2003-09-21
Abstract
Abstract A method for the activation of polyethylene terephthalate materials such as tire yarns is provided whereby the adhesion of the material to an adhesive is enhanced. The material is activated by means of an electron beam to promote free radical formation, which free radicals are permitted to form carboxyl and hydroxyl functionalities under ambient conditions. Such functionalities improve the adhesion with a suitable adhesive such as an epoxy or isocyanate adhesive which is reactive to carboxyl or hydroxyl functionalities and which may be applied to the material before or after activation thereof.
Inventors
- 👤 Gunilla E. Gillberg-LaForce
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 23:05
CPC Classifications
C; C08; C08J; C08J5/00; C08J5/04; C08J5/06; C08J2321/00; Y; Y10; Y10S; Y10S156/00; Y10S156/91; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2933; Y10T428/2964; Y10T428/2967; Y10T428/31504; Y10T428/31786
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
126 words
A process for the treatment of a polyethylene terephthlate material to improve the adhesion thereof in subsequent rubber-reinforcing applications comprising the steps of: (1) activating the surface of the polyethylene terephthalate material with an electron beam from a suitable source to promote free radical formation on said material; (2) permitting said free radicals to form hydrophilic carboxyl and hydroxyl functional groups under ambient conditions; and (3) applying an adhesive composition which is reactive to carboxyl or hydroxyl functional groups to said material, said adhesive composition being selected from the group consisting of: (i) multifunctional isocyanate compounds, (ii) epoxy compounds, (iii) mixtures of (i) and (ii), and (iv) mixtures of (i), (ii) or (iii) with a phenolic-aldehyde latex adhesive whereby the material is suitable for reinforcing rubber.
Claim 2
Dependent Claim
126 words
A process for the treatment of a polyethylene terephthlate material to improve the adhesion thereof in subsequent rubber-reinforcing applications comprising the steps of: (1) activating the surface of the polyethylene terephthalate material with an electron beam from a suitable source to promote free radical formation on said material; (2) permitting said free radicals to form hydrophilic carboxyl and hydroxyl functional groups under ambient conditions; and (3) applying an adhesive composition which is reactive to carboxyl or hydroxyl functional groups to said material, said adhesive composition being selected from the group consisting of: (i) multifunctional isocyanate compounds, (ii) epoxy compounds, (iii) mixtures of (i) and (ii), and (iv) mixtures of (i), (ii) or (iii) with a phenolic-aldehyde latex adhesive whereby the material is suitable for reinforcing rubber.
Claim 3
Dependent Claim
15 words
The process of claim 1 wherein said polyethylene terephthalate material comprises a filament or yarn.
Claim 4
Dependent Claim
30 words
The process of claim 1 wherein said adhesive composition is applied in a quantity of between about 0.05 to 10 percent by weight based on the weight of the material.
Claim 5
Dependent Claim
30 words
The process of claim 3 wherein said adhesive composition is applied in a quantity of between about 0.1 to 2.0 percent by weight based on the weight of the material.
Claim 6
Dependent Claim
11 words
The process of claim 1 wherein said adhesive comprises an epoxy.
Claim 7
Dependent Claim
11 words
The process of claim 1 wherein said adhesive comprises an isocyanate.
Claim 8
Dependent Claim
17 words
The process of claim 1 wherein said adhesive is cured by heat treatment subsequent to step (3).
Claim 9
Dependent Claim
26 words
The process of claim 1 wherein said polyethylene terephthalate material is in the form of a yarn which is spun into cord prior to step (1).
Claim 10
Dependent Claim
142 words
A process for the treatment of a polyethylene terephthlate filament or yarn to improve the adhesion thereof in subsequent rubber-reinforcing applications comprising the steps of: (1) applying a spin finish to the filament or yarn; (2) activating the surface of the polyethylene terephthalate filament or yarn with an electron beam from a suitable source to promote free radical formation on said material; (3) permitting said free radicals to form hydrophilic carboxyl and hydroxyl functional groups under ambient conditions; and (4) applying an adhesive composition which is reactive to carboxyl or hydroxyl functional groups to said filament or yarn, said adhesive composition being selected from the group consisting of: (i) multifunctional isocyanate compounds, (ii) epoxy compounds, (iii) mixtures of (i) and (ii), and (iv) mixtures of (i), (ii) or (iii) with a phenolic-aldehyde latex adhesive whereby the material is suitable for reinforcing rubber.
Claim 11
Dependent Claim
142 words
A process for the treatment of a polyethylene terephthlate filament or yarn to improve the adhesion thereof in subsequent rubber-reinforcing applications comprising the steps of: (1) applying a spin finish to the filament or yarn; (2) activating the surface of the polyethylene terephthalate filament or yarn with an electron beam from a suitable source to promote free radical formation on said material; (3) permitting said free radicals to form hydrophilic carboxyl and hydroxyl functional groups under ambient conditions; and (4) applying an adhesive composition which is reactive to carboxyl or hydroxyl functional groups to said filament or yarn, said adhesive composition being selected from the group consisting of: (i) multifunctional isocyanate compounds, (ii) epoxy compounds, (iii) mixtures of (i) and (ii), and (iv) mixtures of (i), (ii) or (iii) with a phenolic-aldehyde latex adhesive whereby the material is suitable for reinforcing rubber.
Claim 12
Dependent Claim
28 words
The process of claim 9 wherein said spin finish is applied in a quantity of between 0.1 to 5 weight percent based on the weight of the yarn.
Claim 13
Dependent Claim
30 words
The process of claim 9 wherein said adhesive composition is applied in a quantity of between about 0.05 to 10 percent by weight based on the weight of the yarn.
Claim 14
Dependent Claim
30 words
The process of claim 11 wherein said adhesive composition is applied in a quantity of between about 0.1 to 2.0 percent by weight based on the weight of the yarn.
Claim 15
Dependent Claim
11 words
The process of claim 9 wherein said adhesive comprises an epoxy.
Claim 16
Dependent Claim
11 words
The process of claim 9 wherein said adhesive comprises an isocyanate.
Claim 17
Dependent Claim
17 words
The process of claim 9 wherein said adhesive is cured by heat treatment subsequent to step (4).
Claim 18
Dependent Claim
9 words
A product produced by the process of claim 1.
Claim 19
Dependent Claim
9 words
A product produced by the process of claim 9.
Claim 20
Dependent Claim
119 words
A process for the treatment of a polyethylene terephthalate material to improve the adhesion thereof in subsequent rubber-reinforcing applications comprising the steps of: (1) applying an adhesive composition which is reactive to carboxyl or hydroxyl functional groups to said material, said adhesive composition being selected from the consisting of multifunctional isocyanate compounds, epoxy compounds and mixtures thereof; (2) activating the surface of the polyethylene terephthalate material with an electron beam from a suitable source to promote free radical formation on said material; and (3) permitting said free radicals to form hydrophilic carboxyl and hydroxy functional groups under ambient conditions whereby the adhesive composition reacts with the carboxyl and hydroxyl functional groups whereby the material is suitable for reinforcing rubber.
Claim 21
Dependent Claim
119 words
A process for the treatment of a polyethylene terephthalate material to improve the adhesion thereof in subsequent rubber-reinforcing applications comprising the steps of: (1) applying an adhesive composition which is reactive to carboxyl or hydroxyl functional groups to said material, said adhesive composition being selected from the consisting of multifunctional isocyanate compounds, epoxy compounds and mixtures thereof; (2) activating the surface of the polyethylene terephthalate material with an electron beam from a suitable source to promote free radical formation on said material; and (3) permitting said free radicals to form hydrophilic carboxyl and hydroxy functional groups under ambient conditions whereby the adhesive composition reacts with the carboxyl and hydroxyl functional groups whereby the material is suitable for reinforcing rubber.
Claim 22
Dependent Claim
15 words
The process of claim 18 wherein said polyethylene terephthalate material comprises a filament or yarn.
Claim 23
Dependent Claim
30 words
The process of claim 18 wherein said adhesive composition is applied in a quantity of between about 0.05 to 10 percent by weight based o the weight of the material.
Claim 24
Dependent Claim
30 words
The process of claim 20 wherein said adhesive composition is applied in a quantity of between about 0.1 to 2.0 percent by weight based on the weight of the material.
Claim 25
Dependent Claim
11 words
The process of claim 18 wherein said adhesive comprises an epoxy.
References Cited (Backward Citations)
US2956899A
Cited
US3101275A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-12-27 | 1992-06-27 | 1992-12-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-12-27 | 1996-06-27 | 1996-12-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-12-27 | 2000-06-27 | 2000-12-27 | $7700.00 | Window Closed / Lapsed |