US4791073A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Trench isolation method for semiconductor devices
Assignee: NXP USA Inc
•
Filing: 1987-11-17
•
Granted: 1988-12-13
•
Expires: 2007-11-17
Abstract
Abstract A method is described for forming dielectric filled isolation trenches in semiconductor substrates in which a differentially etchable etch-stop layer is provided above the surface of the substrate during the trench filling process so that the height of the trench filling relative to the surface of the substrate may be adjusted for optimum overall results during subsequent fabrication steps and so that the substrate surface may be protected from contact with the etching reagents used during planarization of the trench filling material. This avoids damage to the substrate surface and permits improved surface planarity.
Inventors
- 👤 Andrew G. Nagy
- 👤 Robert J. Mattox
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 21:28
CPC Classifications
H; H10; H10P; H10P70/00; H10P70/20; H10P70/23; H10P70/234; H10P50/00; H10P50/20; H10P50/28; H10P50/282; H10P50/283; H10P50/73; H10P95/00; H10P95/06; H10P95/062; H10P95/064; H10W; H10W10/00; H10W10/01; H10W10/011; H10W10/014; H10W10/10; H10W10/17
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
201 words
A method for forming an isolation wall in a semiconductor device, comprising: providing a semiconductor substrate having a principal surface; forming a dielectric layer on the principal surface; forming a polycrystalline semiconductor layer on the dielectric layer; forming a masking layer having an opening on the polycrystalline layer; removing a portion of the polycrystalline layer and the dielectric layer and the substrate underneath the opening to form a trench extending through the polycrystalline layer and the dielectric layer and into the substrate; depositing a first material comprising a silicon oxy-nitride overlying the polycrystalline layer and in the trench to substantially fill the trench at least to the polycrystalline layer; removing the first material above the polycrystalline layer thereby exposing a first upper surface of the first material in the trench; etching a crevice in the first upper surface of the first material in the trench; filling the crevice with a second material comprising silicon nitride extending above the polycrystalline layer; etching the second material to expose the polycrystalline layer, the first upper surface, and a second upper surface of the second material so that the second upper surface is substantially level with the first upper surface; and removing the polycrystalline layer.
Claim 2
Independent Claim
201 words
A method for forming an isolation wall in a semiconductor device, comprising: providing a semiconductor substrate having a principal surface; forming a dielectric layer on the principal surface; forming a polycrystalline semiconductor layer on the dielectric layer; forming a masking layer having an opening on the polycrystalline layer; removing a portion of the polycrystalline layer and the dielectric layer and the substrate underneath the opening to form a trench extending through the polycrystalline layer and the dielectric layer and into the substrate; depositing a first material comprising a silicon oxy-nitride overlying the polycrystalline layer and in the trench to substantially fill the trench at least to the polycrystalline layer; removing the first material above the polycrystalline layer thereby exposing a first upper surface of the first material in the trench; etching a crevice in the first upper surface of the first material in the trench; filling the crevice with a second material comprising silicon nitride extending above the polycrystalline layer; etching the second material to expose the polycrystalline layer, the first upper surface, and a second upper surface of the second material so that the second upper surface is substantially level with the first upper surface; and removing the polycrystalline layer.
Claim 3
Dependent Claim
33 words
The method of claim 1 wherein the step of removing the oxy-nitride material comprises etching the first material in a gas comprising CHF 3 and oxygen at pressures in the range 40-60 millitorr.
Claim 4
Dependent Claim
36 words
The method of claim 1 wherein the step of removing the silicon nitride material comprises etching the silicon nitride material in a gas comprising CHF 3 and CO 2 at pressures in the range 15-25 millitorr.
Claim 5
Dependent Claim
19 words
The method of claim 1 wherein the step of etching the first material comprises isotropically etching the first material.
Claim 6
Dependent Claim
22 words
The method of claim 1 wherein the step of etching the first material comprises etching the first material without intervening masking steps.
Claim 7
Dependent Claim
19 words
The method of claim 1 wherein the step of forming a dielectic layer comprises thermally oxidizing the substrate surface.
Claim 8
Dependent Claim
31 words
The method of claim 1 further comprising prior to the step of depositing the first material, forming a dielectric layer at least on walls of the trench exposed in the substrate.
Claim 9
Dependent Claim
19 words
The method of claim 5 wherein the step of forming the dielectric layer comprises forming a silicon oxide layer.
Claim 10
Dependent Claim
24 words
The method of claim 1 further comprising prior to the step of removing the first material, depositing a planarizing layer on the first material.
Claim 11
Dependent Claim
29 words
The method of claim 9 wherein the step of removing the first material comprises simultaneously removing a portion of the first material and a portion of the planarizing layer.
Claim 12
Independent Claim
232 words
A method for providing a dielectric filled trench extending into a semiconductor substrate, comprising: providing a semiconductor substrate having a principal surface; forming a first layer on the substrate surface, wherein the first layer is a dielectric differentially etchable with respect to the substrate; forming a second layer on the first layer, wherein the second layer comprises polysilicon and is differentially etchable with respect to the first layer; providing a masking material over the second layer and forming a first opening therein extending to the second layer; through the first opening, etching underlying portions of the second layer and first layer to expose an underlying portion of the substrate; etching the underlying portion of the substrate to form a trench therein extending into the substrate; depositing a third layer in the trench and extending over the second layer, wherein the third layer is differentially etchable with respect to the second layer; removing the third layer extending over the second layer, leaving part of the third layer in the trench; forming a second opening extending at least partly into the third layer in the trench; filling the second opening with a fourth layer extending over the second layer, wherein the fourth layer is differentially etchable with respect to the second layer; removing the fourth layer above the second layer while leaving the fourth layer in the second opening; and removing the second layer.
Claim 13
Independent Claim
232 words
A method for providing a dielectric filled trench extending into a semiconductor substrate, comprising: providing a semiconductor substrate having a principal surface; forming a first layer on the substrate surface, wherein the first layer is a dielectric differentially etchable with respect to the substrate; forming a second layer on the first layer, wherein the second layer comprises polysilicon and is differentially etchable with respect to the first layer; providing a masking material over the second layer and forming a first opening therein extending to the second layer; through the first opening, etching underlying portions of the second layer and first layer to expose an underlying portion of the substrate; etching the underlying portion of the substrate to form a trench therein extending into the substrate; depositing a third layer in the trench and extending over the second layer, wherein the third layer is differentially etchable with respect to the second layer; removing the third layer extending over the second layer, leaving part of the third layer in the trench; forming a second opening extending at least partly into the third layer in the trench; filling the second opening with a fourth layer extending over the second layer, wherein the fourth layer is differentially etchable with respect to the second layer; removing the fourth layer above the second layer while leaving the fourth layer in the second opening; and removing the second layer.
Claim 14
Dependent Claim
39 words
The method of claim 11 further comprising after the step of removing the fourth layer above the second layer, simultaneously removing part of the third layer above the trench and part of the fourth layer in the second opening.
Claim 15
Dependent Claim
25 words
The method of claim 11 wherein the step of forming the second opening comprises etching a central portion of the third layer in the trench.
Claim 16
Dependent Claim
34 words
The method of claim 11 wherein the third layer comprises a silicon oxy-nitride and wherein the step of removing the third layer comprises etching the oxy-nitride in a gas comprising CHF 3 and oxygen.
Claim 17
Dependent Claim
34 words
The method of claim 11 wherein the fourth layer comprises silicon nitride and the step of removing the fourth layer comprises etching the fourth layer in a gas comprising CHF 3 and carbon dioxide.
Claim 18
Dependent Claim
119 words
The method of claim 11 wherein the third layer comprises a silicon oxy-nitride and wherein the step of removing the third layer comprises etching the oxy-nitride in a gas comprising CHF 3 and oxygen and wherein the fourth layer comprises silicon nitride and the step of removing the fourth layer comprises etching the fourth layer in a gas comprising CHF 3 and CO 2 , and wherein the step of etching the silicon oxy-nitride is carried out at a first gas pressure and the step of etching the nitride is carried out at a second gas pressure and wherein the first and second gas pressures are in the ratio (oxy-nitride etch gas pressure:nitride etch gas pressure) of about 40-60:15-25.
Claim 19
Dependent Claim
39 words
The method of claim 11 wherein the steps of removing the third layer and removing the fourth layer comprise gaseous etching, respectively, at first and second pressures, and wherein the first pressure is about 2-5 times the second pressure.
Claim 20
Dependent Claim
70 words
The method of claim 11 wherein the third layer comprises silicon oxy-nitride and the step of removing the third layer comprises gaseous etching in a mixture comprising CHF 3 and O 2 , and wherein a first portion of third layer is etched using a ratio of CHF 3 :O 2 in the range 50-60:25-35 and second portion of the third layer is etched using a ratio of about 70-90:5-10.
References Cited (Backward Citations)
EP0076942A2
Cited
JPS59182538A
Cited
JPS59193044A
Cited
JPS60124841A
Cited
US4484979A
Cited
US4631219A
Cited
US4626317A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-12-13 | 1992-06-13 | 1992-12-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-12-13 | 1996-06-13 | 1996-12-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-12-13 | 2000-06-13 | 2000-12-13 | $7700.00 | Window Closed / Lapsed |