Selective plating process for the electrolytic coating of circuit boards without an electroless metal coating
Assignee: POB 1233 BAT-YAM 59112 8 METZUDAT-BEITAR STREET BAT-YAM 59592 ISRAEL A CORP OF ISRAEL
•
Filing: 1986-11-14
•
Granted: 1988-12-13
•
Expires: 2006-11-14
Abstract
Abstract A process is disclosed for selectively electrometallizing a non-conductive substrate such as the non-conductive surfaces of a circuit board and to directly effect through hole plating and/or form circuits of the boards without employing an electroless metal coating. A photoresist is employed in the process which is exposed, developed and neutralized prior to electrometallizing the substrate. Selectivity is obtained by neutralization. Metals are deposited on a non-conductive substrate in the process by using the reductive capacity of hydrogen in the presence of a metal catalyst of the substrate. The metal catalyst is combined with hydrogen that is generated electrolytically from a protic bath. The metal catalyst combined with hydrogen is contacted with a metal salt. The metal salt may be combined with the protic bath so that the hydrogen that is generated electrolytically combines with the metal catalyst and the metal salt is converted to a metal coating on the substrate.
Inventors
- 👤 Abraham M. Holtzman
- 👤 Joseph Relis
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 17:47
CPC Classifications
H; H05; H05K; H05K3/00; H05K3/40; H05K3/42; H05K3/423; H05K3/424; C; C25; C25D; C25D5/00; C25D5/54; C25D5/56; H05K2203/00; H05K2203/07; H05K2203/0703; H05K2203/0716; H05K2203/12; H05K2203/122; H05K3/425; H05K3/427
Claims Analysis
Total Claims: 45
Claim 1
Independent Claim
164 words
In a process for selectively depositing metals on a non-conductive substrate by employing the reductive capacity of hydrogen in the presence of a metal catalyst on the substrate, said metal catalyst being capable of combining with hydrogen that is generated electrolytically from a protic bath; said substrate being contacted with said metal catalyst to obtain a substrate that is combined with said catalyst; said substrate combined with said metal catalyst being contacted with a protic bath; the steps comprising: (a) imaging a photoresist on said substrate and neutralizing said photoresist after imaging and prior to contacting said substrate with said metal catalyst (b) electrolytically generating hydrogen from said protic bath in an amount sufficient to combine with said metal catalyst and thereby obtain a metal catalyst combined with said hydrogen on said substrate (c) contacting said metal catalyst combined with hydrogen on said substrate with a metal salt for a time sufficient to reduce said metal salt to a metal coating on said substrate.
Claim 2
Dependent Claim
164 words
In a process for selectively depositing metals on a non-conductive substrate by employing the reductive capacity of hydrogen in the presence of a metal catalyst on the substrate, said metal catalyst being capable of combining with hydrogen that is generated electrolytically from a protic bath; said substrate being contacted with said metal catalyst to obtain a substrate that is combined with said catalyst; said substrate combined with said metal catalyst being contacted with a protic bath; the steps comprising: (a) imaging a photoresist on said substrate and neutralizing said photoresist after imaging and prior to contacting said substrate with said metal catalyst (b) electrolytically generating hydrogen from said protic bath in an amount sufficient to combine with said metal catalyst and thereby obtain a metal catalyst combined with said hydrogen on said substrate (c) contacting said metal catalyst combined with hydrogen on said substrate with a metal salt for a time sufficient to reduce said metal salt to a metal coating on said substrate.
Claim 3
Dependent Claim
15 words
The process of claim 1 where said metal salt is present in said protic bath.
Claim 4
Dependent Claim
151 words
A process for depositing metals on a nonconductive substrate by employing the reductive capacity of hydrogen in the presence of a metal catalyst on the substrate, said metal catalyst being capable of combining with hydrogen that is generated electrolytically from a protic bath comprising: (a) imaging a photoresist on said substrate and neutralizing said photoresist after imaging (b) contacting said substrate with said metal catalyst to obtain a metal substrate that is combined with said catalyst; (c) contacting said substrate combined with said metal catalyst with a protic bath, (d) electrolytically generating hydrogen from said protic bath in an amount sufficient to combine with said metal catalyst and thereby obtain a metal catalyst combined with said hydrogen on said substrate (e) contacting said metal catalyst combined with hydrogen on said substrate with a metal salt for a time sufficient to reduce said metal salt to a metal coating on said substrate.
Claim 5
Dependent Claim
151 words
A process for depositing metals on a nonconductive substrate by employing the reductive capacity of hydrogen in the presence of a metal catalyst on the substrate, said metal catalyst being capable of combining with hydrogen that is generated electrolytically from a protic bath comprising: (a) imaging a photoresist on said substrate and neutralizing said photoresist after imaging (b) contacting said substrate with said metal catalyst to obtain a metal substrate that is combined with said catalyst; (c) contacting said substrate combined with said metal catalyst with a protic bath, (d) electrolytically generating hydrogen from said protic bath in an amount sufficient to combine with said metal catalyst and thereby obtain a metal catalyst combined with said hydrogen on said substrate (e) contacting said metal catalyst combined with hydrogen on said substrate with a metal salt for a time sufficient to reduce said metal salt to a metal coating on said substrate.
Claim 6
Dependent Claim
14 words
The process of claim 1 where said metal salt is present in said bath.
Claim 7
Dependent Claim
16 words
The process of claims 3 or 4 where said metal catalyst is combined with a promoter.
Claim 8
Dependent Claim
61 words
The process of claims 3 or 4 where said metal catatyst is combined with a promoter (a) by applying said promoter to said substrate before contacting said substrate with said metal catalyst or (b) by adding said promoter to said metal catalyst or (c) by adding said promoter to said protic bath or any combination of steps (a), (b) or (c).
Claim 9
Dependent Claim
38 words
The process of claim 5 where said promoter is selected from the group consisting of (a) organic hydroxy compounds (b) surfactants (c) thiourea compounds (d) amino acids (e) polycarboxylic acids and (f) water soluble polymers or mixtures therof.
Claim 10
Dependent Claim
28 words
The process of claim 3 where said metal catalyst is based on a metal of Group VIII of the Periodic Table of the Elements that combines with hydrogen.
Claim 11
Dependent Claim
23 words
The process of claim 7 where said metal catalyst is appiied to said substrate from an aqueous system and contains a protective colloid.
Claim 12
Dependent Claim
13 words
The process of claim 9 where said protective colloid is a tin colloid.
Claim 13
Dependent Claim
36 words
The process of claim 3 where said metal catalyst is employed in an aqueous system and is further combined with a stabilizer that minimizes said metal catalyst's sensitivity to water, said stabilizer comprising a metal salt.
Claim 14
Dependent Claim
39 words
The process of claim 11 where said stabilizer is selected from a member of the group consisting of the salts of magnesium, titanium, zirconium, hafnium, manganese, cobalt, nickel, silver, zinc, cadmium, aluminum, gallium, indium and thallium and mixtures thereof.
Claim 15
Dependent Claim
23 words
The process of claim 9 where said stabilizer is selected from the group consisting of the salts of aluminum, titanium, zirconium and hafnium.
Claim 16
Dependent Claim
16 words
The process of claims 12 or 13, where said stabilizer comprises stable water soluble halide salts.
Claim 17
Dependent Claim
19 words
The process of claim 12 where said stabilizer forms complexes with the Group VIII metals or tin or both.
Claim 18
Dependent Claim
12 words
The process of claim 14 where said stabilizer comprises an aluminum halide.
Claim 19
Dependent Claim
26 words
The process of claim 3 where said photoresist is developed by means bf an alkaline developer and said neutralizing is effected by means of an acid.
Claim 20
Dependent Claim
13 words
The process of claim 17 where said developer is an aqueous alkaline developer.
Claim 21
Dependent Claim
62 words
The process of claim 3 where said substrate, prior to or subsequent to said imaging is contacted with a cleaner/conditioner composition comprising: a chelating agent; an acid; a member selected from the group consisting of a surfactant selected from a member of the group consisting of nonionic, catioic, anionic, and amphoteric surface active agents or a poly(oxyalkylene) condensate of an alkyl phenol.
Claim 22
Dependent Claim
64 words
The method of claim 19 where said surfactant is selected from a member of the group consisting of; (a) quaternary ammonium compounds including; (i) cationic quaternary ammonium salts based on fatty amines, (ii) ampnoteric quaternary ammonium salts based on fatty amines, (b) non-ionic surfactants of; (i) polyoxyethylene esters of fatty acids; (ii) polyoxyethylene esters of sorbitan fatty acid esters, (iii) monalkanolamides of fatty acids.
Claim 23
Dependent Claim
12 words
The method of claim 19 where said surfactants are quaternary ammonium compounds.
Claim 24
Dependent Claim
17 words
The method of claim 21 where said surfactants are cationic quaternary ammonium salts based on fatty amines.
Claim 25
Dependent Claim
31 words
The method of claim 22 where said surfactants are selected from a member of the group consisting of: (a) 1-propanaminium, N-(2-hydroxyethyl)-N,N-dimethyl-3-[(1-oxooctadecyl) amino]-salts (b) 1-propanaminium, N,N-trimethyl-3-[(1-oxododecyl)amino]-alkyl ester salts (c) 1-propanaminium,3-dodecyloxy-2-hydroxy-N-bis(2-hydroxyethyl)-N-methyl-,alkyl ester salts.
Claim 26
Dependent Claim
10 words
The method of claim 19 further comprising a fluoride salt.
Claim 27
Dependent Claim
102 words
The method of claim 19 including the following components of said composition are present in the following amounts on a molar basis: (a) from about 2 to about 500 parts of a chelating agent; (b) from 0 to about 200 parts of a fluoride salt; (c) from 0 to about 90 parts of a thiourea compound; (d) from 0 to about 0.8 parts of a surfactant; (e) from 0 to about 0.3 parts of poly(oxyalkylene) condensate of an alkylphenol; (f) from about 10 to about 180 parts of an acid; where at least one of said components (d) or (e) is present.
Claim 28
Independent Claim
59 words
The method of claims 3 where said catalyst is employed for applying an electrolytic coating to a non-conductive substrate and comprises: (a) a metal which can combine with hydrogen; (b) an acid; (c) an Sn 2+ salt; (d) a member selected from the group of an alkali metal stannate and an Sn 4+ salt; (e) a metal salt stabilizer.
Claim 29
Dependent Claim
20 words
The method of claim 26 where said metal is a Group VIII metal of the Periodic Table of the Elements.
Claim 30
Dependent Claim
10 words
The method of claim 27 where said metal is palladimm.
Claim 31
Dependent Claim
40 words
The method of claim 27 where said stabilizer is a water-soluble stable salt selected from the group consisting of the salts of magnesium, titanium, zirconium, hafnium, manganese, cobalt, nickel, silver, zinc, cadmium, aluminum, gallium, indium and thallium and mixtures thereof.
Claim 32
Dependent Claim
23 words
The method of claim 29 where said stabilizer is selected from the group consisiing of the salts of aluminum, titanium, zirconium and hafnium.
Claim 33
Dependent Claim
10 words
The method of claim 29 where said metal comprises aluminum.
Claim 34
Dependent Claim
13 words
The method of claim 29 where said metal salt comprises an aluminum halide.
Claim 35
Dependent Claim
87 words
The method of claim 26 where the components of said composition are present in the following amounts on a molar basis: (a) from about 0.1 to about 2 parts of said metal salt; (b) from about 3 to about 6 parts of said acid; (c) from about 4 to about 85 parts of said Sn 2+ salt; (d) from about 0.5 to about 10 parts of said alkali metal stannate or Sn 4+ salt; (e) from about 100 to about 1000 parts of said metal salt stabilizer.
Claim 36
Dependent Claim
46 words
The method of claim 3 where said metal salt is combined with: (a) an acid; (b) an adjuvant selected from the group consisting of (i) polyhydroxy cyclic compounds; (ii) acetylenic alcohols and their derivatives; (iii) acetylenic compounds; (iv) water soluble polymers and; (c) a halogen ion.
Claim 37
Dependent Claim
73 words
The method of claim 34 where said polyhydroxy compound comprises a cyclic polyhydroxy compound having a six carbon atom ring and from 2 to about 3 hydroxy groups on said ring and a cyclic hydroxy compound having a 6 carbon atom ring and one hydroxy group on said ring, said second cyclic hydroxy compound being present in an amount of from 0 to about 80% of said polyhydroxy compound on a molar basis.
Claim 38
Dependent Claim
27 words
The method of claim 35 where said cyclic polyhydroxy compound is selected from the group consisting of resorcinol and pyrogallol and said cyclic hydroxy compound comprises phenol.
Claim 39
Dependent Claim
22 words
The method of claim 35 where said polyhydroxy compound comprises a nitrogen heterocyclic compound having from 1 to about 2 nitrogen atoms.
Claim 40
Dependent Claim
11 words
The method of claim 35 where said hydroxy compound comprises 2,4-dihydroxy-6-methylpyrimidine.
Claim 41
Dependent Claim
14 words
The method of claim 35 where said adjuvant comprises propargyl alcohol and its derivatives.
Claim 42
Dependent Claim
13 words
The method of claim 35 where said adjuvant is a water soluble polymer.
Claim 43
Dependent Claim
11 words
The method of claim 35 where said adjuvant is a hydroxyalkylcellulose.
Claim 44
Dependent Claim
58 words
The method of claim 35 where the components of said composition are present in the following amounts on a molar basis: (a) from about 2.5 to about 50 parts of said metal salt (c) from about 0.4 to about 8 parts of said adjuvant (d) from about 10 to about 100 parts per million of a halide ion.
Claim 45
Dependent Claim
77 words
The method of claim 3 comprising applying said photoresist to a substrate comprising a circuit board having a metal surface and through holes, imaging and neutralizing said photoresist, forming a circuit pattern of said metal coating on said board and in said through holes, to obtain an exposed metal coating, applying an immersion tin coating to said exposed metal coating, removing said photoresist and etching said metal surface that has not been coated with said immersion tin.
References Cited (Backward Citations)
US3099608A
Cited
US3930963A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-12-13 | 1992-06-13 | 1992-12-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-12-13 | 1996-06-13 | 1996-12-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-12-13 | 2000-06-13 | 2000-12-13 | $7700.00 | Window Closed / Lapsed |