Silicon nitride glow plug with alumina corrosion and erosion protective coating
Assignee: Niterra Co Ltd
•
Filing: 1988-01-14
•
Granted: 1988-11-22
•
Expires: 2008-01-14
Abstract
Abstract A ceramic glow plug comprises a ceramic heater formed by embedding a metal wire in a sintered Si 3 N 4 -based ceramic. The ceramic heater is brazed to the inner surface of an axial bore of a metal tube and the metal tube is brazed to the inner surface of an axial bore of a metal holder. The tip of the ceramic heater extends from the metal tube and metal holder and is coated with highly heat and corrosion resistant material to minimize erosion and corrosion due to combustion gases. The coating consists essentially of a thin CVD film of alumina (Al 2 O 3 ) having a thickness of 2 μm deposited on a precoating AlON layer having a thickness of 0.5 μm formed on the exposed surface of the tip. Alternatively, the protective coating may consist of thin CVD film of silicon carbide (SiC) or silicon nitride (Si 3 N 4 ) formed directly on the exposed surface of the tip.
Inventors
- 👤 Shunkichi Nozaki
- 👤 Yukihiro Kimura
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 16:01
CPC Classifications
F; F23; F23Q; F23Q7/00; F23Q7/001
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
163 words
A ceramic glow plug comprising: a metal tube having an axial bore; a sintered ceramic heater including a wire embedded in sintered Si 3 N 4 -based ceramic, said ceramic heater having a tip portion and being attached to the inner surface of said axial bore of said metal tube such that said tip of said ceramic heater extends from an end of said bore of said metal tube and is exposed; a metal holder having an axial bore, said metal tube being attached at its other end to the inner surface of said axial bore of said metal holder; and a heat-resistant coating covering the exposed surface of said tip of said ceramic heater, wherein said heat-resistant coating consists essentially of a thin CVD film of alumina having a thickness of about 2 μm and wherein an AlON pre-coating layer is first formed on the exposed surface of said ceramic heater tip, and said alumina coating is formed on the AlON layer.
Claim 2
Dependent Claim
163 words
A ceramic glow plug comprising: a metal tube having an axial bore; a sintered ceramic heater including a wire embedded in sintered Si 3 N 4 -based ceramic, said ceramic heater having a tip portion and being attached to the inner surface of said axial bore of said metal tube such that said tip of said ceramic heater extends from an end of said bore of said metal tube and is exposed; a metal holder having an axial bore, said metal tube being attached at its other end to the inner surface of said axial bore of said metal holder; and a heat-resistant coating covering the exposed surface of said tip of said ceramic heater, wherein said heat-resistant coating consists essentially of a thin CVD film of alumina having a thickness of about 2 μm and wherein an AlON pre-coating layer is first formed on the exposed surface of said ceramic heater tip, and said alumina coating is formed on the AlON layer.
Claim 3
Dependent Claim
36 words
The ceramic glow plug according to claim 1, wherein said ceramic heater is brazed to said axial bore of said metal tube and said metal tube is brazed to said axial bore of said metal holder.
Claim 4
Dependent Claim
19 words
The ceramic glow plug according to claim 1 wherein the thickness of said AlON layer is about 0.5 μm.
Claim 5
Independent Claim
122 words
A method for forming a heat-resistant alumina coating over an AlON pre-coating layer on a sintered silicon nitride glow plug heater tip comprising the steps of: heating the heater tip to about 1,000° C.; exposing the heated heater tip to a streaming gaseous mixture including AlCl 3 , carbon dioxide, hydrogen, and nitrogen at a reduced pressure of about 10 Torr for a time sufficient to form an A1ON pre-coating layer of about 0.5 μm thickness; exposing the heated heater tip having the AlON coating to a second, nitrogen-free, streaming gaseous mixture including AlCl 3 , carbon dioxide and hydrogen at a pressure of about 10 Torr for a time sufficient to form an alumina coating layer thickness of about 2 μm.
Claim 6
Independent Claim
122 words
A method for forming a heat-resistant alumina coating over an AlON pre-coating layer on a sintered silicon nitride glow plug heater tip comprising the steps of: heating the heater tip to about 1,000° C.; exposing the heated heater tip to a streaming gaseous mixture including AlCl 3 , carbon dioxide, hydrogen, and nitrogen at a reduced pressure of about 10 Torr for a time sufficient to form an A1ON pre-coating layer of about 0.5 μm thickness; exposing the heated heater tip having the AlON coating to a second, nitrogen-free, streaming gaseous mixture including AlCl 3 , carbon dioxide and hydrogen at a pressure of about 10 Torr for a time sufficient to form an alumina coating layer thickness of about 2 μm.
References Cited (Backward Citations)
US4336305A
Cited
US4336304A
Cited
US4418661A
Cited
US4502430A
Cited
US4556780A
Cited
JPH113663A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-11-22 | 1992-05-23 | 1992-11-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-11-22 | 1996-05-23 | 1996-11-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-11-22 | 2000-05-23 | 2000-11-22 | $7700.00 | Window Closed / Lapsed |