Abstract
Abstract Plastic compositions having good sonar transmission, that is low loss of sound transmission, are a composite of a low loss sonar material, for example polyethylene, and a high tensile strength material, for example fiberglass, adhered together by a binder, for example an epoxy. The composite generally has a tensile strength of greater than 100,000 PSI. The composites unexpectantly have a lower sound level loss than would be expected based upon a linear proportion of the amount of high flexural strength material contained therein.
Inventors
- 👤 Ram S. Raghava
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 03:56
CPC Classifications
C; C08; C08F; C08F8/00; C08F8/30; B; B29; B29C; B29C70/00; B29C70/04; B29C70/06; B29C70/08; D; D03; D03D; D03D15/00; D03D15/20; D03D15/242; D03D15/267; D03D15/283; D03D15/50; D03D15/573; G; G10; G10K; G10K11/00; G10K11/004; G10K11/006; B29K; B29K2995/00; B29K2995/0001; D10; D10B; D10B2321/00; D10B2321/02; D10B2321/021; D10B2321/0211; D10B2321/04; D10B2321/042; D10B2331/00; D10B2331/02; D10B2331/021; D10B2401/00; D10B2401/06; D10B2401/063; Y; Y10; Y10S; Y10S428/00; Y10S428/902; Y10T; Y10T428/00; Y10T428/30; Y10T428/31504; Y10T428/31511; Y10T428/31515; Y10T428/31518; Y10T428/3154; Y10T442/00; Y10T442/30; Y10T442/3472; Y10T442/3528; Y10T442/3569; Y10T442/3585
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
71 words
A high sonar transmission composition, comprising: a plastic composite containing at least one layer of a low sound level loss material, at least one layer of a high tensile strength material, and a relatively rigid binder bonding said layers together, the amount of said low sound level loss material being an effective amount so that said composite has a sound level loss of about 4 decibels or less at 100 kilohertz.
Claim 2
Dependent Claim
71 words
A high sonar transmission composition, comprising: a plastic composite containing at least one layer of a low sound level loss material, at least one layer of a high tensile strength material, and a relatively rigid binder bonding said layers together, the amount of said low sound level loss material being an effective amount so that said composite has a sound level loss of about 4 decibels or less at 100 kilohertz.
Claim 3
Dependent Claim
50 words
A high sonar transmission composition according to claim 1, wherein said high tensile strength material has a strength of at least 200,000 PSI, and wherein the amount of said high tensile strength material is an effective amount to form a composite having a flexural strength of at least 7,000 PSI.
Claim 4
Dependent Claim
161 words
A high sonar transmission composition according to claim 2, wherein said low sound level loss material is polyethylene, or polytetrafluoroethylene, wherein said high tensile strength material is fiberglass, aramid, carbon filter, or graphite fiber, wherein said binder is an epoxy, a polyester, or a vinyl ester, wherein the amount of said low sound level loss material is from about 10 percent to about 90 percent by volume based upon the total volume of said low sound level loss material and said high tensile strength material, wherein the amount of said high tensile strength material is from about 10 percent to about 90 percnt by volume based upon the total volume of said low sound level loss material and said high tensile strength material, and wherein the amount of said binder is from about 30 percent to about 70 percent by volume based upon the total volume of said resin, said high tensile strength material, and said low sound level loss material.
Claim 5
Dependent Claim
29 words
A high sonar transmission composition according to claim 3, wherein said composite has a flexural strength of at least 15,000 PSI, and a flexural modulus of at least 1,500,000.
Claim 6
Dependent Claim
115 words
A high sonar transmission composition according to claim 4, wherein said low sound level loss material is a polyethylene having a molecular weight of at least 500,000, wherein said high tensile strength material is fiberglass, wherein said binder is epoxy, wherein the amount of said polyethylene is from about 25 percent to about 80 percent by volume, wherein the amount of said fiberglass is from about 20 percent to about 75 percent by volume, wherein the amount of said epoxy is from about 40 percent to about 65 percent by volume, wherein said composite has a flexural strength of at least 20,000 PSI and wherein said composite has a flexural modulus of at least 2,500,000.
Claim 7
Dependent Claim
69 words
A high sonar transmission composition according to claim 3, wherein said low sound level loss material is in the form of a fiber weave, wherein said high strength material is in the form of a fiber weave, wherein said binder bonds said low sound level loss fiber weave to said high strength fiber weave, and wherein said composite has a sound level loss of about 3 decibels or less.
Claim 8
Dependent Claim
36 words
A high sonar transmission composition according to claim 4, wherein said low sound level loss material is in the form of a binder-ply, wherein said high strength material is in a form of a binder ply.
Claim 9
Dependent Claim
10 words
A sonar dome made from the composition of claim 1.
Claim 10
Dependent Claim
10 words
A sonar dome made from the composition of claim 3.
Claim 11
Dependent Claim
10 words
A sonar dome made from the composition of claim 5.
Claim 12
Dependent Claim
70 words
A composite of high sonar transmission capabilities, comprising: at least one layer of a high tensile strength material, at least one layer of a high sonar transmission material, and a binder bonding said tensile strength material layer and said high sonar transmission material layer, the amount of said high sonar transmission material being an effective amount so that said composite is capable of transmitting a high amount of sonar therethrough.
Claim 13
Dependent Claim
70 words
A composite of high sonar transmission capabilities, comprising: at least one layer of a high tensile strength material, at least one layer of a high sonar transmission material, and a binder bonding said tensile strength material layer and said high sonar transmission material layer, the amount of said high sonar transmission material being an effective amount so that said composite is capable of transmitting a high amount of sonar therethrough.
Claim 14
Dependent Claim
18 words
A composite according to claim 11, wherein said composite has a tensile strength of at least 1000,000 PSI.
Claim 15
Dependent Claim
26 words
A composite according to claim 12, wherein said composite has a sonar transmitting loss of about 4 decibels or less at a frequency of 100 kilohertz.
Claim 16
Dependent Claim
152 words
A composite according to claim 13, wherein said high sonar transmission material is polyethylene or polytetrafluoroethylene, wherein said high tensile strength material is fiberglass, aramid, carbon fiber, or graphite fiber, wherein said binder has a tensile modulus of at least 50,000 PSI, wherein the amount of said high sonar transmission material is from about 10 percent to about 90 percent by volume based upon the total volume of said high sonar transmission material and said high tensile strength material, wherein the amount of said high tensile strength material is from about 10 to about 90 percent by volume based upoon the total volume of said high sonar transmission material and said high tensile strength material, and wherein the amount of said binder is from about 30 percent to about 70 percent by volume based upon the total volume of said resin, said high tensile strength material, and said high sonar transmission material.
Claim 17
Dependent Claim
51 words
A composite according to claim 14, wherein said binder is an epoxy, a polyester, or a vinyl ester, wherein said composite has a tensile strength of at least 150,000 PSI, and wherein said composite has a sonar transmission loss of about 3 decibels or less at a frequency of 100 kilohertz.
Claim 18
Dependent Claim
24 words
A composite according to claim 11, wherein said high sonar transmission material is in the form of at least two binder-ply sheets clustered together.
Claim 19
Dependent Claim
37 words
A composite according to claim 14, wherein said high sonar transmission material is in the form of a woven fiber layer and wherein said high tensile strength material is in the form of a woven fiber layer.
Claim 20
Dependent Claim
32 words
A composite according to claim 14, wherein said high sonar transmission material and said layer of high tensile strength material are in the form of fibers woven into a single woven layer.
Claim 21
Dependent Claim
9 words
A sonar dome comprising the composition of claim 12.
Claim 22
Dependent Claim
9 words
A sonar dome comprising the composition of claim 15.
Claim 23
Dependent Claim
40 words
A high sonar transmission composition according to claim 6, wherein said layer of said low sound level loss material and said layer of said high tensile strength material are in the form of fibers woven into a single woven layer.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-11-15 | 1992-05-16 | 1992-11-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-11-15 | 1996-05-16 | 1996-11-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-11-15 | 2000-05-16 | 2000-11-15 | $7700.00 | Window Closed / Lapsed |