Damage tolerant composites containing infusible particles
Assignee: Hexcel Corp
•
Filing: 1987-03-30
•
Granted: 1988-11-08
•
Expires: 2007-03-30
Abstract
Abstract Damage tolerant composites comprising high strength filaments in the form of bundles or tows of continuous fiber and a tough phase separated, crosslinked epoxy resin matrix are disclosed. The crosslinked epoxy resin matrix comprises infusible particles made from a rubber polymer that reside primarily between piles of the composite and critically have a median particle size between 10-75 microns. Prepregs for making the damage tolerant composites and methods of making such prepregs and the epoxy resin compositions thereof are also disclosed. The epoxy resin compositions comprise the infusible particles which become segregated as to size on a surface layer of the prepreg during the process of combining the high strength filaments of the prepreg and the resin containing the epoxy resin composition.
Inventors
- 👤 Irena Gawin
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 09:33
CPC Classifications
C; C08; C08G; C08G59/00; C08G59/18; C08G59/20; C08G59/22; C08G59/226; C08L; C08L65/00; C08G59/32; C08G59/38; C08G59/40; C08G59/50; C08G65/00; C08G65/34; C08G65/48; C08J; C08J5/00; C08J5/24; C08J5/241; C08J5/243; C08J5/249; C08L63/00; C08L71/00; C08L81/00; C08L81/06; C08J2363/00
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
196 words
An epoxy resin composition comprising a polyepoxide component, a reactive oligomer, a curing agent and a rubber polymer, said resin composition exhibiting phase separation upon cure and made by a process comprising combining: 100 parts by weight of a polyepoxide component comprising a polyepoxide compound having a glass transition below 50° C. and having at least about two epoxide groups per molecule; between about 10 and 200 parts by weight of a reactive aromatic oligomer component comprising a crosslinkable oligomer having at least about two crosslinkable groups per molecule and a molecular weight (number average) between about 2000 and 10,000; between about 5 and 100 parts by weight of a curing agent for crosslinking said epoxy composition and having a molecular weight below about 1000; and a crosslinkable rubber polymer at a level between about 1 and 15% by weignt of said epoxy resin composition, an amount of said polymer being contained within infusible particles that are dispersed throughout said resin composition and have lower modulus than the matrix of said epoxy resin composition that is cured in absence of said infusible particles, said infusible particles having a median size between 10 microns and 75 microns.
Claim 2
Dependent Claim
196 words
An epoxy resin composition comprising a polyepoxide component, a reactive oligomer, a curing agent and a rubber polymer, said resin composition exhibiting phase separation upon cure and made by a process comprising combining: 100 parts by weight of a polyepoxide component comprising a polyepoxide compound having a glass transition below 50° C. and having at least about two epoxide groups per molecule; between about 10 and 200 parts by weight of a reactive aromatic oligomer component comprising a crosslinkable oligomer having at least about two crosslinkable groups per molecule and a molecular weight (number average) between about 2000 and 10,000; between about 5 and 100 parts by weight of a curing agent for crosslinking said epoxy composition and having a molecular weight below about 1000; and a crosslinkable rubber polymer at a level between about 1 and 15% by weignt of said epoxy resin composition, an amount of said polymer being contained within infusible particles that are dispersed throughout said resin composition and have lower modulus than the matrix of said epoxy resin composition that is cured in absence of said infusible particles, said infusible particles having a median size between 10 microns and 75 microns.
Claim 3
Dependent Claim
19 words
The epoxy resin composition in accordance with claim 1, wherein said particles are made using a cross-linkable rubber polymer.
Claim 4
Dependent Claim
16 words
The epoxy resin composition in accordance with claim 2, wherein said crosslinkable rubber polymer is carboxy-functional.
Claim 5
Dependent Claim
35 words
The epoxy resin composition in accordance with claim 3, wherein said reactive oligomer is selected from an amine functional polyarylene polyether sulfone or ketone, an amine functional polyarylene polythioether sulfone or ketone and combinations thereof.
Claim 6
Dependent Claim
18 words
The epoxy resin composition in accordance with claim 4, wherein said curing agent comprises an amine functional sulfone.
Claim 7
Dependent Claim
23 words
The epoxy resin composition in accordance with claim 5 wherein said amine functional sulfone is selected from 3,3'-bis(aminophenyl)sulfone, 4,4'-bis(aminophenyl) sulfone and combinations thereof.
Claim 8
Dependent Claim
27 words
The epoxy composition in accordance with claim 6, wherein said oligomer comprises an amine functional polyarylene polyether sulfone having a molecular weight between about 2,500 and 7,500.
Claim 9
Dependent Claim
22 words
The epoxy resin composition in accordance with claim 7, wherein said polyepoxide component comprises a combination of di and trifunctional polyepoxide compounds.
Claim 10
Independent Claim
149 words
A method of making an intermediate epoxy resin composition to a final epoxy resin composition, said final epoxy resin composition suitable for use in making damage tolerant composites with high strength filaments, said final epoxy resin composition made using a cross-linkable rubber polymer at a level between about 1 and 15 parts per hundred parts of said final epoxy resin composition, said method comprising: forming a liquid mixture comprising a polyepoxide component having at least one polyepoxide compound with a glass transition temperature below 50° C. and a reactive aromatic oligomer with a molecular weight between 2,000 and 10,000; admixing said level of crosslinkable rubber polymer and said liquid mixture; reacting said crosslinkable rubber polymer in said admixture so as to yield a resin premix with infusible particles (a) respectively comprising an amount of said rubber polymer and (b) having a median size between 10 microns and 75 microns.
Claim 11
Independent Claim
149 words
A method of making an intermediate epoxy resin composition to a final epoxy resin composition, said final epoxy resin composition suitable for use in making damage tolerant composites with high strength filaments, said final epoxy resin composition made using a cross-linkable rubber polymer at a level between about 1 and 15 parts per hundred parts of said final epoxy resin composition, said method comprising: forming a liquid mixture comprising a polyepoxide component having at least one polyepoxide compound with a glass transition temperature below 50° C. and a reactive aromatic oligomer with a molecular weight between 2,000 and 10,000; admixing said level of crosslinkable rubber polymer and said liquid mixture; reacting said crosslinkable rubber polymer in said admixture so as to yield a resin premix with infusible particles (a) respectively comprising an amount of said rubber polymer and (b) having a median size between 10 microns and 75 microns.
Claim 12
Dependent Claim
27 words
The method in accordance with claim 9, which further comprises admixing an amine hardener with said premix, said amine hardner having a molecular weight below about 1,000.
Claim 13
Dependent Claim
19 words
The method in accordance with claim 10, wherein said crosslinkable rubber polymer comprises a carboxy functional butadiene acrylonitrile polymer.
Claim 14
Dependent Claim
18 words
The method in accordance with claim 11, wherein said reactive oligomer comprises an amine functional polyarylene polyether sulfone.
Claim 15
Dependent Claim
31 words
The method in accordance with claim 9, wherein asid crosslinkable rubber polymer is admixed with a polyepoxide compound having a Tg below 50° C. prior to admixture with said liquid mixture.
Claim 16
Independent Claim
136 words
A method of making an epoxy resin composition suitable for use in making damage tolerant composites with high strength filaments, said method comprising: admixing a solution comprising a crosslinkable rubber polymer at a level between about 1 and 15 parts per hundred parts by weight of said epoxy resin composition, a solvent which dissolves said rubber polymer and a liquid mixture made from a polyepoxide component having at least one polyepoxide compound having a glass transition temperature below 50° C. and a reactive aromatic oligomer with a molecular weight between 2,000 and 10,000, said admixing forming an admixture; removing an amount of said solvent from said admixture so as to yield a composition with infusible particles respectively comprising an amount of said rubber polymer and having a median particle size between 10 microns and 75 microns.
Claim 17
Independent Claim
136 words
A method of making an epoxy resin composition suitable for use in making damage tolerant composites with high strength filaments, said method comprising: admixing a solution comprising a crosslinkable rubber polymer at a level between about 1 and 15 parts per hundred parts by weight of said epoxy resin composition, a solvent which dissolves said rubber polymer and a liquid mixture made from a polyepoxide component having at least one polyepoxide compound having a glass transition temperature below 50° C. and a reactive aromatic oligomer with a molecular weight between 2,000 and 10,000, said admixing forming an admixture; removing an amount of said solvent from said admixture so as to yield a composition with infusible particles respectively comprising an amount of said rubber polymer and having a median particle size between 10 microns and 75 microns.
Claim 18
Dependent Claim
27 words
The method in accordance with claim 14, which further comprises admixing an amine hardner with said composition, said amine hardner having a molecular weight below about 1,000.
Claim 19
Dependent Claim
19 words
The method in accordance with claim 15, wherein said crosslinkable rubber polymer comprises a carboxy functional butadiene acrylonitrile polymer.
Claim 20
Dependent Claim
17 words
The method in accordance with claim 16, wherein said reactive oligomer comprises an amine functional polyether sulfone.
Claim 21
Dependent Claim
24 words
The method in accordance with claim 17, wherein said particles are made infusible during removal of said solvent at elevated temperature and reduced pressure.
Claim 22
Dependent Claim
20 words
The method in accordance with claim 9, wherein said polyepoxide component comprises a combination of di- and trifunctional polyepoxide compounds.
References Cited (Backward Citations)
US3837904A
Cited
US3926903A
Cited
US3926904A
Cited
US4187347A
Cited
US4195113A
Cited
US4220686A
Cited
US4264655A
Cited
US4222918A
Cited
US4588778A
Cited
EP0130270A1
Cited
US4539253A
Cited
US4668736A
Cited
US4656207A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-11-08 | 1992-05-09 | 1992-11-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-11-08 | 1996-05-09 | 1996-11-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-11-08 | 2000-05-09 | 2000-11-08 | $7700.00 | Window Closed / Lapsed |