Method for permanently marking glass

Claim 2

A process for permanently marking a glass surface comprising the steps of: (a) wiping a glass surface with a basic aqueous cleaning solution; (b) wiping the backside of a mask having a face and a back side with the basic aqueous cleaning solution, said mask comprising a porous support layer permeable to a glass etchant composition and a resist material impervious to said glass etchant composition, said mask having resist areas impervious to a glass etchant composition where said porous support layer is impregnated with said resist material, and non-resist areas pervious to said glass etchant composition where said porous support layer is substantially free of said resist material, said resist areas and non-resist areas in combination delineating a marking pattern on the mask to be etched into the glass surfce; (c) applying the back side of said mask to the wiped glass surface to bind the mask to said glass surface; (d) applying a glass etchant composition operative to etch glass to the face of the mask to cover all of the non-resist areas of the mask with the glass etchant composition for a time operative for the glass etchant composition to etch the marking pattern into the surface of the glass; and (e) removing the mask from the glass surface.

Claim 3

The process according to claim 1 wherein a basic aqueous neutralizing solution is applied to the glass surface after the removal of the mask to neutralize any residual glass etchant composition adhering to the glass surface and prevent further etching.

Claim 4

The process according to claim 2 wherein the basic aqueous cleaning solution and the basic aqueous neutralizing solution are the same solution.

Claim 5

The process according to claim 1 wherein the glass etchant composition comprises a hydrogen fluoride source selected from the group consisting of ammonium bifluoride, lithium bifluoride, sodium bifluoride, potassium bifluoride, calcium bifluoride, a mixture of a fluoride salt and a strong acid, and mixtures thereof.

Claim 6

The process according to claim 1 wherein the glass etchant composition comprises ammonium bifluoride and water.

Claim 7

The process according to claim 1 wherein the mask is a waxed tissue stencil material comprising a tissue porous support layer, said tissue porous support layer having resist areas impregnated with wax and non-resist areas being substantially free of wax.

Claim 8

The process according to claim 1 wherein the mask is squeegeed on the glass surface after application of the mask to said glass surface, to form a thin film with said basic aqueous cleaning solution to bind said mask to said glass surface.

Claim 9

A process for permanently marking a glass surface comprising the steps of: (a) preparing a mask having a face side and a back side, said mask comprising a porous support layer pervious to a glass etchant composition and a resist material impervious to said glass etchant composition, said support layer having resist areas impervious to said glass etchant composition, and non-resist areas pervious to said glass etchant composition, said porous support layer impregnated with said resist material impervious to said glass etchant composition in said resist areas, said porous support layer being substantially free of said resist material in said non-resist areas, said resist areas and non-resist areas in combination delineating a marking pattern to be etched into the glass surface; (b) wiping a glass surface with a basic aqueous cleaning solution; (c) wiping the back side of said mask with the basic aqueous cleaning solution; (d) applying the back side of said mask to the wetted glass surface to bind said mask to said glass surface and to form a thin film of said aqueous solution between the glass surface and the back side of the mask to detachably bind said mask to said glass surface; (e) applying to the face side of said mask a chemical etching composition operative to etch a glass surface, the glass etchant composition permeating the non-resist areas of the mask to etch the glass surface to form an etch pattern substantially identical to the marking pattern delineated by the resist and non-resist areas of the mask; and (f) removing the mask from the glass surface.

Claim 10

A process for permanently marking a glass surface comprising the steps of: (a) preparing a mask having a face side and a back side, said mask comprising a porous support layer pervious to a glass etchant composition and a resist material impervious to said glass etchant composition, said support layer having resist areas impervious to said glass etchant composition, and non-resist areas pervious to said glass etchant composition, said porous support layer impregnated with said resist material impervious to said glass etchant composition in said resist areas, said porous support layer being substantially free of said resist material in said non-resist areas, said resist areas and non-resist areas in combination delineating a marking pattern to be etched into the glass surface; (b) wiping a glass surface with a basic aqueous cleaning solution; (c) wiping the back side of said mask with the basic aqueous cleaning solution; (d) applying the back side of said mask to the wetted glass surface to bind said mask to said glass surface and to form a thin film of said aqueous solution between the glass surface and the back side of the mask to detachably bind said mask to said glass surface; (e) applying to the face side of said mask a chemical etching composition operative to etch a glass surface, the glass etchant composition permeating the non-resist areas of the mask to etch the glass surface to form an etch pattern substantially identical to the marking pattern delineated by the resist and non-resist areas of the mask; and (f) removing the mask from the glass surface.

Claim 11

The process according to claim 8 wherein a basic aqueous neutralizing solution is applied to the glass surface after the removal of the mask to neutralize any residual glass etchant composition adhering to the glass surface to prevent further etching.

Claim 12

The process according to claim 8 wherein the mask is squeegeed on the glass surface after application of the mask to said glass surface, to form a thin film of said basic aqueous cleaning solution between said mask and said glass surface to bind said mask to said glass surface.

Claim 13

The process according to claim 8 wherein the basic aqueous cleaning solution comprises a salt selected from the group consisting of an alkali metal salt of a weak acid or an ammonia salt of a weak acid.

Claim 14

A process according to claim 8 wherein the basic aqueous cleaning solution comprises ammonia hydroxide.

Claim 15

A process according to claim 11 wherein the basic aqueous cleaning solution comprises, in addition, a surface active agent selected from the group consisting non-ionic detergents, anionic detergents, cationic detergents, and mixtures thereof.

Claim 16

The process according to claim 8 wherein the the basic aqueous neutralizing solution comprises an aqueous solution of an alkali metal salt of a weak acid.

Claim 17

The process according to claim 8 wherein the glass etchant composition comprises a hydrogen fluoride source selected from the group consisting of ammonium bifluoride, lithium bifluoride, sodium bifluoride, potassium bifluoride, calcium fluoride, a mixture of a fluoride salt and a strong acid and mixtures thereof.

Claim 18

The process according to claim 8 wherein the glass etchant composition comprises ammonium bifluoride.

Claim 19

The process according to claim 8 wherein the mask is a waxed tissue stencil material comprising a tissue porous support layer, said tissue porous support layer having resist areas impregnated with wax and non-resist areas being substantially free of wax.

Claim 20

The process according to claim 8 wherein the mask is squeegeed on the glass surface after application of the mask to said glass surface, to form a thin film with said basic aqueous cleaning solution to bind said mask to said glass surface.