US4780436A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Zeolite of omega structure catalysts
Assignee: IFP Energies nouvelles
•
Filing: 1986-09-04
•
Granted: 1988-10-25
•
Expires: 2006-09-04
Abstract
Abstract The invention concerns a new stabilized and dealuminated zeolite of OMEGA structure, characterized by: a total SiO2/Al2O3 molar ratio of at least 10, a sodium content lower than 0.5% by weight, a and c parameters of elementary mesh respectively lower than 1.814 nm and 0.759 nm, a nitrogen adsorption capacity at 77 K higher than about 5% by weight for a partial pressure P/Po of 0.19, a lattice of mesopores whose radii range preferably from 1.5 to 14 nm. This zeolite can be used in admixture with a convenient matrix in reactions of hydrocarbon conversion.
Inventors
- 👤 Francis Raatz
- 👤 Christian Marcilly
- 👤 Pierre Dufresne
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 22:58
CPC Classifications
B; B01; B01J; B01J29/00; B01J29/04; B01J29/06; B01J29/70; B01J29/72; B01J29/74; B01J29/7423; B01J29/7011; B01J29/78; B01J29/7823; C; C10; C10G; C10G47/00; C10G47/02; C10G47/10; C10G47/12; C10G47/16; B01J2229/00; B01J2229/10; B01J2229/16; B01J2229/26; B01J2229/30; B01J2229/36; B01J2229/37; B01J2229/40; B01J2229/42
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
112 words
A dealuminated zeolite of omega (or mazzite) structure characterized by: a total SiO 2 Al 2 O 3 molar ratio of at least 10, a sodium content lower than 0.5% by weight, determined on the zeolite roasted at 1100° C., a and c parameters of elementary mesh respectively lower than 1.84 nm and 0.759 nm, a nitrogen adsorption capacity at 77 K, under a partial pressure P/Po=0.19, higher than 5% by weight, a pore distribution such that from 0.2 to 50% of the pore volume is provided by pores of radii ranging from 1.5 to 14 nm, the remaining pore volume being provided by pores of a radius less than 1 nm.
Claim 2
Dependent Claim
112 words
A dealuminated zeolite of omega (or mazzite) structure characterized by: a total SiO 2 Al 2 O 3 molar ratio of at least 10, a sodium content lower than 0.5% by weight, determined on the zeolite roasted at 1100° C., a and c parameters of elementary mesh respectively lower than 1.84 nm and 0.759 nm, a nitrogen adsorption capacity at 77 K, under a partial pressure P/Po=0.19, higher than 5% by weight, a pore distribution such that from 0.2 to 50% of the pore volume is provided by pores of radii ranging from 1.5 to 14 nm, the remaining pore volume being provided by pores of a radius less than 1 nm.
Claim 3
Dependent Claim
91 words
A zeolite according to claim 1, characterized by: a total SiO 2 /Al 2 O 3 molar ratio higher than 15, a and c crystalline parameters respectively ranging from 1.814 to 1.794 nm and from 0.759 to 0.749 nm, a nitrogen adsorption capacity at 77 K, for a partial pressure P/Po=0.19, higher than 11% by weight, a pore distribution such that 1 to 50% of the pore volume is pores of radii ranging from 2 to 8 nm, the remaining pore volume being in pores of radii lower than 1 nm.
Claim 4
Dependent Claim
143 words
A process for manufacturing an omega zeolite as defined in claim 1, from a synthetic omega zeolite, containing alkali cations and organic cations, and whose SiO 2 /Al 2 O 3 molar ratio is from 6 to 10, said manufacturing process being characterized in that (a) in a first step the synthetic zeolite is subjected to a treatment for removal of the major part of the organic cations, while decreasing the alkali content to a value lower than 0.5% by weight, by means of at least one treatment selected from the group consisting of a cation exchange and a roasting, and (b) in a second step the solid obtained in the preceding step is subjected to at least one roasting followed with at least one acid etching, so as to obtain a SiO 2 /Al 2 O 3 molar ratio higher than 10.
Claim 5
Dependent Claim
42 words
A process according to claim 3, wherein, during the second step, the synthetic zeolite is subjected to at least one roasting in air or in inert atmosphere between 500° and 900° C., the acid etching temperature being from 0° to 150° C.
Claim 6
Dependent Claim
12 words
A process according to claim 4, performed in the presence of steam.
Claim 7
Dependent Claim
35 words
A process according to claim 3, wherein, during the second step, the synthetic zeolite is subjected to at least one calcination in confined atmosphere, the temperature of acid etching being from 0° to 150° C.
Claim 8
Dependent Claim
121 words
A catalyst containing by weight: (a) about 50 to 95% of a matrix selected from the group consisting of at least alumina, silica, silica-alumina, alumina-boron oxide, magnesia, silica-magnesia, zirconia, titanium oxide, clay, (b) about 3 to 50% of a zeolite according to claim 1, (c) at least one metal or compound of metal selected from the group consisting of the noble or non noble metals of group VIII of the periodic classification of elements, the concentration of noble metal or metals from group VIII, expressed by weight of this or these metals, ranging from 0.03 to 3%, the concentration of non noble metal or metals from group VIII, expressed by weight of this or these metals, ranging from 0.05 to 10%.
Claim 9
Dependent Claim
7 words
A zeolite produced according to claim 3.
Claim 10
Dependent Claim
7 words
A zeolite produced according to claim 4.
Claim 11
Dependent Claim
7 words
A zeolite produced according to claim 5.
Claim 12
Dependent Claim
7 words
A zeolite produced according to claim 6.
Claim 13
Dependent Claim
121 words
A catalyst containing by weight: (a) about 50 to 95% of a matrix selected from the group consisting of at least alumina, silica, silica-alumina, alumina-boron oxide, magnesia, silica-magnesia, zirconia, titanium oxide, clay, (b) about 3 to 50% of a zeolite according to claim 8, (c) at least one metal or compound of metal selected from the group consisting of the noble or non noble metals of group VIII of the periodic classification of elements, the concentration of noble metal or metals from group VIII, expressed by weight of this or these metals, ranging from 0.03 to 3%, the concentration of non noble metal or metals from group VIII, expressed by weight of this or these metals, ranging from 0.05 to 10%.
Claim 14
Dependent Claim
121 words
A catalyst containing by weight: (a) about 50 to 95% of a matrix selected from the group consisting of at least alumina, silica, silica-alumina, alumina-boron oxide, magnesia, silica-magnesia, zirconia, titanium oxide, clay, (b) about 3 to 50% of a zeolite according to claim 9, (c) at least one metal or compound of metal selected from the group consisting of the noble or non noble metals of group VIII of the periodic classification of elements, the concentration of noble metal or metals from group VIII, expressed by weight of this or these metals, ranging from 0.03 to 3%, the concentration of non noble metal or metals from group VIII, expressed by weight of this or these metals, ranging from 0.05 to 10%.
Claim 15
Dependent Claim
121 words
A catalyst containing by weight: (a) about 50 to 95% of a matrix selected from the group consisting of at least alumina, silica, silica-alumina, alumina-boron oxide, magnesia, silica-magnesia, zirconia, titanium oxide, clay, (b) about 3 to 50% of a zeolite according to claim 13, (c) at least one metal or compound of metal selected from the group consisting of the noble or non noble metals of group VIII of the periodic classification of elements, the concentration of noble metal or metals from group VIII, expressed by weight of this or these metals, ranging from 0.03 to 3%, the concentration of non noble metal or metals from group VIII, expressed by weight of this or these metals, ranging from 0.05 to 10%.
Claim 16
Dependent Claim
121 words
A catalyst containing by weight: (a) about 50 to 95% of a matrix selected from the group consisting of at least alumina, silica, silica-alumina, alumina-boron oxide, magnesia, silica-magnesia, zirconia, titanium oxide, clay, (b) about 3 to 50% of a zeolite according to claim 11, (c) at least one metal or compound of metal selected from the group consisting of the noble or non noble metals of group VIII of the periodic classification of elements, the concentration of noble metal or metals from group VIII, expressed by weight of this or these metals, ranging from 0.03 to 3%, the concentration of non noble metal or metals from group VIII, expressed by weight of this or these metals, ranging from 0.05 to 10%.
References Cited (Backward Citations)
US3367884A
Cited
US3812199A
Cited
US3551510A
Cited
US3640681A
Cited
US4120825A
Cited
US3944482A
Cited
US4241036A
Cited
US4228036A
Cited
US4377502A
Cited
US4297335A
Cited
US4331643A
Cited
US4515902A
Cited
US4591576A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-10-25 | 1992-04-25 | 1992-10-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-10-25 | 1996-04-25 | 1996-10-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-10-25 | 2000-04-25 | 2000-10-25 | $7700.00 | Window Closed / Lapsed |