Optically transparent electrically conductive semiconductor windows and methods of manufacture
Assignee: Northrop Grumman Corp
•
Filing: 1987-02-13
•
Granted: 1988-10-18
•
Expires: 2007-02-13
Abstract
Abstract A semiconductor window which is transparent to light in the infrared range and which has good electrical conductivity is formed with a substrate of semi-conductor material which has a conduction modifying dopant diffused, grown or deposited on one surface thereof to a substantial depth so that a layer thereof exhibits reduced resistance to a value below 10 ohms/square. Anti-reflection dielectric layers are stacked on both outer surfaces thereof. The dielectric substrate may be of silicon, germanium or gallium arsenide depending on the transparency bandwidth of interest. The thickness of the substrate and the doping of the surface thereof is closely controlled to obtain both low electrical resistivity and high optical transmissivity.
Inventors
- 👤 Paul Kraatz
- 👤 James M. Rowe
- 👤 John W. Tully
- 👤 Vahram W. Biricik
- 👤 Wesley J. Thompson
- 👤 Rudolph W. Modster
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 18:45
CPC Classifications
G; G02; G02B; G02B1/00; G02B1/10; G02B1/11; G02B1/113; G02B1/115; G02B1/116; G02B1/02; G02B5/00; G02B5/20; G02B5/208; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12535; Y10T428/12542; Y10T428/12549; Y10T428/12611; Y10T428/12618; Y10T428/1266; Y10T428/12674; Y10T428/12681
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
64 words
A transparent conductive window for transmission in the infrared comprising: a semiconductor substrate transmissive to infrared and having an input surface, dopant means forming a doped layer adjacent said surface for rendering said layer conductive, said dopant means being distributed into the layer to obtain an electrical resistivity thereat of less than about 10 ohms per square while essentially preserving the optical properties thereof.
Claim 2
Dependent Claim
64 words
A transparent conductive window for transmission in the infrared comprising: a semiconductor substrate transmissive to infrared and having an input surface, dopant means forming a doped layer adjacent said surface for rendering said layer conductive, said dopant means being distributed into the layer to obtain an electrical resistivity thereat of less than about 10 ohms per square while essentially preserving the optical properties thereof.
Claim 3
Dependent Claim
22 words
The window of claim 1 wherein the doped layer has been fabricated by diffusion of an elemental dopant into said substrate surface.
Claim 4
Dependent Claim
19 words
The window of claim 1 wherein the doped layer has been epitaxially grown on the surface of said substrate.
Claim 5
Dependent Claim
19 words
The window of claim 1 wherein the doped layer has been deposited to a thickness of substantially 25 microns.
Claim 6
Dependent Claim
14 words
The window of claim 1 wherein said doped layer is of the N type.
Claim 7
Dependent Claim
24 words
The window of claim 1 and further including a plurality of anti-reflectant coatings deposited on the other of the optical surfaces of said substrate.
Claim 8
Dependent Claim
28 words
The window of claim 1 wherein the substrate is of silicon and the dopant is of a material selected from the group consisting of antimony, phosphorous and arsenic.
Claim 9
Dependent Claim
29 words
The window of claim 1 wherein the substrate is of germanium and the doped layer is of a material selected from the group consisting of antimony, phosphorous and arsenic.
Claim 10
Dependent Claim
24 words
The window of claim 1 wherein the substrate is of gallium arsenide and the doped layer comprises a layer epitaxially grown on the substrate.
Claim 11
Dependent Claim
91 words
A transparent conductive window for use in the infrared comprising a sheet of semiconductive material having front and back surfaces and selected to be transparent to infrared radiation, an N type dopant diffused into said front surface of said semiconductor to a thickness sufficient to give a sheet resistance of less than 10 ohms/square and transmittance at least 75% of that of the undoped substrate, and an antireflection coating stack deposited over said dopant surface, said antireflection coating being selected to form an impedance match between air and said doped surface.
Claim 12
Dependent Claim
91 words
A transparent conductive window for use in the infrared comprising a sheet of semiconductive material having front and back surfaces and selected to be transparent to infrared radiation, an N type dopant diffused into said front surface of said semiconductor to a thickness sufficient to give a sheet resistance of less than 10 ohms/square and transmittance at least 75% of that of the undoped substrate, and an antireflection coating stack deposited over said dopant surface, said antireflection coating being selected to form an impedance match between air and said doped surface.
Claim 13
Dependent Claim
23 words
The transparent window as in claim 10 wherein said semiconductor material is selected from the group consisting of germanium, silicon and gallium arsenide.
Claim 14
Dependent Claim
72 words
A transparent conductive window for use in the infrared comprising: a sheet made of semiconductor material and having a front surface, said semiconductor material being selected to be transparent to infrared radiation, and means forming an impurity zone established into said semiconductor sheet from the front surface to a thickness sufficient to give a sheet resistance of less than 10 ohms/square and transmittance at least 75% of that of pure semiconductor material.
Claim 15
Dependent Claim
72 words
A transparent conductive window for use in the infrared comprising: a sheet made of semiconductor material and having a front surface, said semiconductor material being selected to be transparent to infrared radiation, and means forming an impurity zone established into said semiconductor sheet from the front surface to a thickness sufficient to give a sheet resistance of less than 10 ohms/square and transmittance at least 75% of that of pure semiconductor material.
Claim 16
Dependent Claim
79 words
An optical window transparent to light energy in the infrared range and having low electrical resistivity comprising: a germanium substrate having opposite optical surfaces, a doped layer of a material selected from the group consisting of antimony phosphorous and arsenic diffused into one of the optical surfaces of said substrate to a thickness of substantially 25 microns, and a plurality of anti-reflectant coatings deposited over said doped layer and over the other of the optical surfaces of said substrate.
Claim 17
Dependent Claim
79 words
An optical window transparent to light energy in the infrared range and having low electrical resistivity comprising: a germanium substrate having opposite optical surfaces, a doped layer of a material selected from the group consisting of antimony phosphorous and arsenic diffused into one of the optical surfaces of said substrate to a thickness of substantially 25 microns, and a plurality of anti-reflectant coatings deposited over said doped layer and over the other of the optical surfaces of said substrate.
Claim 18
Dependent Claim
79 words
An optical window transparent to light energy in the infrared range and having low electrical resistivity comprising: a silicon substrate having opposite optical surfaces, a doped layer of a material selected from the group consisting of antimony phosphorous and arsenic diffused into one of the optical surfaces of said substrate to a thickness of substantially 25 microns, and a plurality of anti-reflectant coatings deposited over said doped layer and over the other of the optical surfaces of said substrate.
Claim 19
Dependent Claim
79 words
An optical window transparent to light energy in the infrared range and having low electrical resistivity comprising: a silicon substrate having opposite optical surfaces, a doped layer of a material selected from the group consisting of antimony phosphorous and arsenic diffused into one of the optical surfaces of said substrate to a thickness of substantially 25 microns, and a plurality of anti-reflectant coatings deposited over said doped layer and over the other of the optical surfaces of said substrate.
Claim 20
Dependent Claim
70 words
An optical window transparent to light energy in the infrared range and having low electrical resistivity comprising: a gallium arsenide substrate having opposite optical surfaces, a doped gallium arsenide film epitaxially deposited on one of the optical surfaces of said substrate to a thickness of substantially 25 microns, and a plurality of anti-reflectant coatings deposited over said doped layer and over the other of the optical surfaces of said substrate.
Claim 21
Dependent Claim
70 words
An optical window transparent to light energy in the infrared range and having low electrical resistivity comprising: a gallium arsenide substrate having opposite optical surfaces, a doped gallium arsenide film epitaxially deposited on one of the optical surfaces of said substrate to a thickness of substantially 25 microns, and a plurality of anti-reflectant coatings deposited over said doped layer and over the other of the optical surfaces of said substrate.
Claim 22
Dependent Claim
109 words
A conductive window for transmission in the infrared comprising: a semiconductor substrate having an input surface transmissive to infrared energy; said semiconductor being selected from the group consisting of silicon, germanium, and gallium arsenide; dopant means forming a doped layer adjacent said surface for rendering said layer conductive while essentially preserving the optical properties thereof, said semiconductor substrate and dopant means being selected from one of the substrate-dopant pairs consisting of silicon doped with phosphorous; germanium doped with antimony, arsenic, or phosphorous; and gallium arsenide doped with silicon; said dopant being distributed into the layer to obtain an electrical resistivity thereat of less than about 10 ohms per square.
Claim 23
Dependent Claim
109 words
A conductive window for transmission in the infrared comprising: a semiconductor substrate having an input surface transmissive to infrared energy; said semiconductor being selected from the group consisting of silicon, germanium, and gallium arsenide; dopant means forming a doped layer adjacent said surface for rendering said layer conductive while essentially preserving the optical properties thereof, said semiconductor substrate and dopant means being selected from one of the substrate-dopant pairs consisting of silicon doped with phosphorous; germanium doped with antimony, arsenic, or phosphorous; and gallium arsenide doped with silicon; said dopant being distributed into the layer to obtain an electrical resistivity thereat of less than about 10 ohms per square.
References Cited (Backward Citations)
US4058638A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-10-18 | 1992-04-18 | 1992-10-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-10-18 | 1996-04-18 | 1996-10-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-10-18 | 2000-04-18 | 2000-10-18 | $7700.00 | Window Closed / Lapsed |