Microparticles having crosslinking reaction promotor function and method of use
Assignee: Nippon Paint Co Ltd
•
Filing: 1987-03-02
•
Granted: 1988-10-11
•
Expires: 2007-03-02
Abstract
Abstract Promoters for a crosslinking reaction involved in the curing of a system comprising crosslinkable polymers are bound to polymeric microparticles having a diameter of about 0.01 to 6 microns prepared by polymerizing a mixture of ethylenically unsaturated monomers. The microparticles carrying the crosslinking reaction promoter may be incorporated to coating compositions, printing inks, sealants, adhesives and other polymeric products in place of conventional crosslinking reaction promoters.
Inventors
- 👤 Kazunori Kanda
- 👤 Shinichi Ishikura
- 👤 Keizou Ishii
- 👤 Akio Kashihara
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 12:40
CPC Classifications
C; C08; C08J; C08J3/00; C08J3/24; C08G; C08G18/00; C08G18/06; C08G18/08; C08G18/16; Y; Y10; Y10S; Y10S524/00; Y10S524/901; Y10S524/902; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31511; Y10T428/31525; Y10T428/31529; Y10T428/31678; Y10T428/31681
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
150 words
A coating system comprising a film-forming polymer capable of curing through a selfcrosslinking reaction or a crosslinking reaction with a separate crosslinker and a catalytic amount of an agent for promoting the crosslinking reaction, wherein said agent is bound to polymeric microparticles having a diameter of 0.01 to 6 microns present in said system, and polymer microparticles being prepared by polymerizing a mixture of ethylenically unsaturated monomers, said agent being (i) an electron donating tertiary amine, present in a combination with an epoxy resin and an acid anhydride hardener, (ii) a metallic compound or a tertiary amine present in a combination with an active hydrogen atomcontaining polymer and a polyisocyanate, (iii) a dryer present in a polymer capable of curing through an oxidation polymerization reaction, (iv) an organic cobalt salt, an amine or a mercaptan present in an unsaturated polyester resin, or (v) a photosensitizer present in a photocurable resin.
Claim 2
Dependent Claim
150 words
A coating system comprising a film-forming polymer capable of curing through a selfcrosslinking reaction or a crosslinking reaction with a separate crosslinker and a catalytic amount of an agent for promoting the crosslinking reaction, wherein said agent is bound to polymeric microparticles having a diameter of 0.01 to 6 microns present in said system, and polymer microparticles being prepared by polymerizing a mixture of ethylenically unsaturated monomers, said agent being (i) an electron donating tertiary amine, present in a combination with an epoxy resin and an acid anhydride hardener, (ii) a metallic compound or a tertiary amine present in a combination with an active hydrogen atomcontaining polymer and a polyisocyanate, (iii) a dryer present in a polymer capable of curing through an oxidation polymerization reaction, (iv) an organic cobalt salt, an amine or a mercaptan present in an unsaturated polyester resin, or (v) a photosensitizer present in a photocurable resin.
Claim 3
Dependent Claim
27 words
The system according to claim 1 wherein at least a portion of said monomer mixture consists of a monomer having at least two polymerizable sites per molecule.
Claim 4
Dependent Claim
26 words
The system according to claim 1 wherein at least a portion of said monomer mixture consists of a combination of two monomers having mutually reactive groups.
Claim 5
Dependent Claim
24 words
The system according to claim 1 comprising an epoxy resin and an acid anhydride hardener, wherein said agent is an electron donating tertiary amine.
Claim 6
Dependent Claim
28 words
The system according to claim 1 comprising a polymer having active hydrogen atoms and a polyisocyanate, and wherein said agent is a metallic compound or a tertiary amine.
Claim 7
Dependent Claim
24 words
The system according to claim 1, comprising a polymer capable of curing through an oxidation polymerization reaction and wherein said agent is a dryer.
Claim 8
Dependent Claim
25 words
The system according to claim 1 comprising an unsaturated polyester resin and wherein said agent is an organic cobalt salt, an amine or a mercaptan.
Claim 9
Dependent Claim
17 words
The system according to claim 1 comprising a photocurable resin and wherein said agent is a photosensitizer.
Claim 10
Dependent Claim
19 words
The system according to claim 1 wherein said polymerization is carried out in the presence of an amphoionic substance.
Claim 11
Dependent Claim
38 words
The system according to claim 1 wherein said agent is bound to said polymeric microparticles by chemically introducing an ethylenic unsaturation function into the promoting agent molecule and copolymerizing the resulting promoting agent-containing monomer with said monomer mixture.
Claim 12
Dependent Claim
32 words
The system according to claim 1 wherein said agent is bound to said polymeric microparticles by incorporating the promoting agent into said monomer mixture and polmerizing the monomer mixture containing the promoter.
Claim 13
Dependent Claim
27 words
The system according to claim 1 wherein said agent is bound to said polymeric microparticles by impregnating the polymeric microparticles with a solution of said promoting agent.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-10-11 | 1992-04-11 | 1992-10-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-10-11 | 1996-04-11 | 1996-10-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-10-11 | 2000-04-11 | 2000-10-11 | $7700.00 | Window Closed / Lapsed |