Preparation of polymers of acrylic acid or metharcylic acid
Assignee: BASF SE
•
Filing: 1987-01-29
•
Granted: 1988-09-27
•
Expires: 2007-01-29
Abstract
Abstract Polymers of acrylic acid or methacrylic acid are prepared by polymerizing acrylic acid and/or methacrylic acid at 50°-180° C. in a C 2 -C 6 -alcohol or mixtures thereof with water having a C 2 -C↓6↑-alcohol content of not less than 40% by weight in the presence of free radical polymerization initiators and from 0.01 to 5% by weight, based on the monomers used, of inorganic acids of phosphorus in which the phosphorus has an oxidation number of from 1 to 4, or of water-soluble salts thereof, water-soluble --PO(OH) 2 -containing compounds and/or water-soluble salts thereof. The polymers thus prepared are effective milling aids and dispersants for pigments for producing aqueous pigment slurries for use in paper-coating compositions.
Inventors
- 👤 Walter Denzinger
- 👤 Heinrich Hartmann
- 👤 Guenter Hirsch
- 👤 Hans-Werner Becker
- 👤 Michael Rohmann
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 10:21
CPC Classifications
C; C09; C09D; C09D17/00; C09D17/004; B; B29; B29C; B29C31/00; B29C31/04; B29C31/06; B29C31/065; B29C31/068; B29C45/00; B29C45/17; B29C45/18; C08; C08F; C08F20/00; C08F20/02; C08F20/04; C08F20/06; C09C; C09C1/00; C09C1/02; C09C1/021; C09C3/00; C09C3/04; C09C3/041; D; D21; D21H; D21H19/00; D21H19/36; D21H19/38; D21H19/40; D21H19/44; D21H19/56; D21H19/58; B29K; B29K2067/00; C01; C01P; C01P2004/00; C01P2004/60; C01P2004/62
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
125 words
A process for preparing a polymer of acrylic acid or methacrylic acid by polymerizing acrylic acid, methacrylic acid, or mixtures thereof, if desired together with up to 10% by weight of another ethylenically unsaturated compound copolymerizable therewith, at 40°-180° C. in a secondary C 2 -C 6 -alcohol or a mixture thereof with water with a C 2 -C 6 -alcohol content of not less than 40% by weight in the presence of a free radical polymerization initiator and of from 0.01 to 5% by weight, based on the monomers used, of an inorganic acid of phosphorhus in which the phosphorus has an oxidation number of from 1-4, a water-soluble salt thereof, a water-soluble --PO(OH) 2 -containing compound, a water-soluble salt thereof, or mixtures thereof.
Claim 2
Dependent Claim
125 words
A process for preparing a polymer of acrylic acid or methacrylic acid by polymerizing acrylic acid, methacrylic acid, or mixtures thereof, if desired together with up to 10% by weight of another ethylenically unsaturated compound copolymerizable therewith, at 40°-180° C. in a secondary C 2 -C 6 -alcohol or a mixture thereof with water with a C 2 -C 6 -alcohol content of not less than 40% by weight in the presence of a free radical polymerization initiator and of from 0.01 to 5% by weight, based on the monomers used, of an inorganic acid of phosphorhus in which the phosphorus has an oxidation number of from 1-4, a water-soluble salt thereof, a water-soluble --PO(OH) 2 -containing compound, a water-soluble salt thereof, or mixtures thereof.
Claim 3
Dependent Claim
25 words
The process as claimed in claim 1, wherein the water-soluble --PO(OH) 2 -containing compound used in aminotrismethylenetriphosphonic acid, ethylenediaminetetramethylenetetraphosphonic acid, ethylenetriaminepentamethylenephosphonic acid and/or 1-hydroxyethane-1,1-diphosphonic acid.
Claim 4
Dependent Claim
56 words
The process as claimed in claim 1, wherein acrylic acid is polymerized in isopropanol or a mixture thereof with water having an isopropanol content of not less than 40% by weight in the presence of from 0.1 to 1% by weight, based on acrylic acid, of phosphorous acid or an alkali metal or ammonium salt thereof.
Claim 5
Dependent Claim
58 words
The process as claimed in claim 1, wherein the polymerization is conducted in isopropanol, secbutanol, or mixtures thereof with water such that the polymerization medium has a secondary alcohol content of not less than 40% by weight, in the presence of a phosphorus acid, a water-soluble-PO(OH) 2 -containing compound, or mixtures thereof at 90°-130° C. under super-atmospheric pressure.
Claim 6
Dependent Claim
80 words
The process as claimed in claim 1, wherein said ethylenically unsaturated compound copolymerizable with said acid is an acrylic acid or methacrylic acid ester formed from a monohydric alcohol of 1-8 carbon atoms, a dicarboxylic acid, a monoester of said dicarboxylic acid, a diester of said dicarboxylic acid, both of said esters being formed from C 1 -C 8 monohydric alcohols, acrylonitrile, methacrylonitrile, acrylamide, methacrylamide, vinyl acetate, vinyl propionate, vinyl butyrate, 2-acrylamido-2-methylpropanesulfonic acid, vinylsulfonic acid, allylsulfonic acid or vinylphosphonic acid.
Claim 7
Dependent Claim
45 words
The process as claimed in claim 1, wherein said inorganic acid of phosphorus or water-soluble salt thereof is hypophosphorous acid, the sodium or potassium salt thereof, hypodiphosphorous acid, sodium hypodisphosphite, phosphorous acid, monosodium phosphite, disodium phosphite, diphosphorous acid, sodium diphosphite, hypodiphosphorous acid or sodium hypodiphosphite.
Claim 8
Dependent Claim
26 words
The process as claimed in claim 1, wherein the amount of said inorganic phosphorous acid employed ranges from 0.1-1% by weight, based on the monomers employed.
Claim 9
Dependent Claim
40 words
The process as claimed in claim 1, wherein said polymer product has a Fikentscher K value ranging from 15-50 as measured at 25° C. in a 1% aqueous solution in the form of a sodium salt at pH of 8.5.
References Cited (Backward Citations)
GB578849A
Cited
US2576720A
Cited
US3787488A
Cited
JPS4928672A
Cited
US4209398A
Cited
US4301266A
Cited
US4534866A
Cited
US4499002A
Cited
US4639490A
Cited
US4640793A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-09-27 | 1992-03-28 | 1992-09-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-09-27 | 1996-03-28 | 1996-09-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-09-27 | 2000-03-28 | 2000-09-27 | $7700.00 | Window Closed / Lapsed |