Nonwoven fabric with improved abrasion resistance
Assignee: Ethicon Inc
•
Filing: 1987-06-22
•
Granted: 1988-09-27
•
Expires: 2007-06-22
Abstract
Abstract A melt-blown microfiber fabric having improved surface abrasion resistance is disclosed, having a surface veneer of melt-blown fibers with an average fiber diameter of greater than 8 microns and in which 75% of the fibers have a fiber diameter of at least 7 microns and a wet and dry abrasion resistance of greater than 15 cycles to pill.
Inventors
- 👤 Larry H. McAmish
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 17:55
CPC Classifications
D; D04; D04H; D04H1/00; D04H1/40; D04H1/54; D04H1/56; D04H1/559; Y; Y10; Y10S; Y10S428/00; Y10S428/903; Y10T; Y10T156/00; Y10T156/10; Y10T156/1002; Y10T156/1039; Y10T428/00; Y10T428/24; Y10T428/24479; Y10T428/24612; Y10T428/24802; Y10T428/24826; Y10T428/27; Y10T442/00; Y10T442/60; Y10T442/608; Y10T442/614; Y10T442/68
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
176 words
An improved unreinforced melt-blown microfiber fabric having improved surface abrasion resistance, said fabric comprising at least one unreinforced thermoplastic melt-blown microfiber core web having a minimum grab tensile strength to weight ratio greater than 0.8N per gram per square meter and a minimum Elmendorf tear strngth to weight ratio greater than 0.04N per gram per Square meter, said core web having a basis weight in the range of 14 grams per square meter to 85 grams per square meter, and at least one unreinforced surface veneer web on said core web, said veneer web being formed of melt-blown thermoplastic fibers having an average fiber diameter of greater than 8 microns in which 75% of the fibers have a diameter of at least 7 microns, having a wet and dry surface abrasion resistance of greater a than 15 cycles to pill, and having a basis weight in the range of 3 grams per square meter to 10 grams per square meter, said at least one veneer web being directly contiguous to said at least one core web.
Claim 2
Dependent Claim
176 words
An improved unreinforced melt-blown microfiber fabric having improved surface abrasion resistance, said fabric comprising at least one unreinforced thermoplastic melt-blown microfiber core web having a minimum grab tensile strength to weight ratio greater than 0.8N per gram per square meter and a minimum Elmendorf tear strngth to weight ratio greater than 0.04N per gram per Square meter, said core web having a basis weight in the range of 14 grams per square meter to 85 grams per square meter, and at least one unreinforced surface veneer web on said core web, said veneer web being formed of melt-blown thermoplastic fibers having an average fiber diameter of greater than 8 microns in which 75% of the fibers have a diameter of at least 7 microns, having a wet and dry surface abrasion resistance of greater a than 15 cycles to pill, and having a basis weight in the range of 3 grams per square meter to 10 grams per square meter, said at least one veneer web being directly contiguous to said at least one core web.
Claim 3
Dependent Claim
29 words
The fabric of claim 1 in which the fabric is thermally embossed at intermittent discrete bond regions which occupy between 5 and 30% of the surface of the fabric.
Claim 4
Dependent Claim
29 words
The fabric of claim 1 having a wet abrasion resistance to pill of at least 30 cycles and a dry abrasion resistance to pill of at least 40 cycles.
Claim 5
Dependent Claim
38 words
The fabric of claim 3 wherein the basis weight is no greater than 60 g/m 2 and the minimum grab tensile strength is not less than 65N and the minimum Elmendorf tear strength is not less than 6N.
Claim 6
Dependent Claim
23 words
An improved unreinforced melt-blown microfiber fabric as in claim 1 wherein said surface veneer has an average fiber diameter of about 9 microns.
Claim 7
Dependent Claim
227 words
An improved unreinforced melt-blown fabric having improved abrasion resistance, said fabric comprising at least one unreinforced thermoplastic core web in which at least 80% of the fibers have a diameter of 7 microns or less and in which the autogenous bonding of the fibers contribute no more than 30% of the strip tensile strength of the fabric, and at least one unreinforced surface veneer web on said core web, said surface venner web being formed of melt-blown thermoplastic fibers having an average fiber diameter of greater than 8 microns and in which 75% of said fibers have a diameter of at least 7 microns and having a basis weight in the range of 3 grams per square meter to 10 grams per square meter, said fabric being thermally emobossed at intermittent discrete bond regions which occupy between 5 and 30% of the surface of the fabric, said core web having a minimum grab tensile strength to weight ratio greater than 0.8N per gram per square meter and an Elmendorf tear strength to weight ratio greater than 0.04N per gram per square meter, and said fabric having a wet surface abrasion resistance of at least 30 cycles to pill and a dry surface abrasion resistance of at least 40 cycles to pill, said at least one veneer web being directly contigous to said at least one core web.
Claim 8
Dependent Claim
227 words
An improved unreinforced melt-blown fabric having improved abrasion resistance, said fabric comprising at least one unreinforced thermoplastic core web in which at least 80% of the fibers have a diameter of 7 microns or less and in which the autogenous bonding of the fibers contribute no more than 30% of the strip tensile strength of the fabric, and at least one unreinforced surface veneer web on said core web, said surface venner web being formed of melt-blown thermoplastic fibers having an average fiber diameter of greater than 8 microns and in which 75% of said fibers have a diameter of at least 7 microns and having a basis weight in the range of 3 grams per square meter to 10 grams per square meter, said fabric being thermally emobossed at intermittent discrete bond regions which occupy between 5 and 30% of the surface of the fabric, said core web having a minimum grab tensile strength to weight ratio greater than 0.8N per gram per square meter and an Elmendorf tear strength to weight ratio greater than 0.04N per gram per square meter, and said fabric having a wet surface abrasion resistance of at least 30 cycles to pill and a dry surface abrasion resistance of at least 40 cycles to pill, said at least one veneer web being directly contigous to said at least one core web.
Claim 9
Dependent Claim
22 words
An improved unreinforced melt-blown fabric as in claim 6 wherein said surface veneer has an average fiber diameter of about 9 microns.
Claim 10
Independent Claim
179 words
A method of producing a melt-blown microfiber fabric having improved abrasion resistance comprising: (1) forming at least one core web of thermoplastic melt-blown microfibers having a minimum grab tensile strength to weight ratio greater than 0.8N per gram per square meter, a minimum Elmendorf tear strength to weight ratio greater than 0.04N per gram per square meter, and a basis weight in the range of 14 grams per square meter to 85 grams per square meter, (2) forming at least one unreinforced surface veneer web of melt-blown thermoplastic fibers on said core web, said veneer web having high initial autogenous bonding and an average fiber diameter of greater than 8 microns, in which 75% of the fibers have a fiber diameter of at least 7 microns, said veneer web having a basis weight in the range of 3 grams per square meter to 10 grams per square meter and a wet and dry surface abrasion resistance greater than 15 cycles to pill, (3) said at least one veneer web being directly contiguous to said at least one core web.
Claim 11
Independent Claim
179 words
A method of producing a melt-blown microfiber fabric having improved abrasion resistance comprising: (1) forming at least one core web of thermoplastic melt-blown microfibers having a minimum grab tensile strength to weight ratio greater than 0.8N per gram per square meter, a minimum Elmendorf tear strength to weight ratio greater than 0.04N per gram per square meter, and a basis weight in the range of 14 grams per square meter to 85 grams per square meter, (2) forming at least one unreinforced surface veneer web of melt-blown thermoplastic fibers on said core web, said veneer web having high initial autogenous bonding and an average fiber diameter of greater than 8 microns, in which 75% of the fibers have a fiber diameter of at least 7 microns, said veneer web having a basis weight in the range of 3 grams per square meter to 10 grams per square meter and a wet and dry surface abrasion resistance greater than 15 cycles to pill, (3) said at least one veneer web being directly contiguous to said at least one core web.
Claim 12
Dependent Claim
25 words
A method of producing a melt-blown microfiber fabric as in claim 8 wherein said veneer web has an average fiber diameter of about 9 microns.
Claim 13
Dependent Claim
16 words
The method of claim 8 further comprising thermally embossing said laminate at discrete intermittent bond regions.
Claim 14
Independent Claim
315 words
A method of producing an unreinforced microfiber fabric having improved surface abrasion resistance wherein a fiber-forming thermoplastic polymer resin in molten form is forced through a row of orifices in a heated nozzle into a stream of inert gas to attenuate the resin into fibers, the fibers are collected on a receiver to form a web, and the web is thermally bonded to form a fabric comprising: (a) at a first heated nozzle, maintaining the polymer melt temperature at a level which minimizes molecular degradation, controlling the primary air velocity, volume and temperature, polymer resin throughput and exit temperature to produce a first layer of thermoplastic fibers having an average fiber diameter of greater than 8 microns, and in which 75% of the fibers have a fiber diameter of at least 7 microns, collecting the fibers on a receiver at a forming distance to form a first unreinforced surface veneer web with good interfiber bonding and having a basis weight in the range of 3 grams per square meter to 10 grams per square meter and a wet and dry surface abrasion resistance of greater than 15 cycles to pill; (b) at a second heated nozzle, maintaining the polymer melt temperature at a level which minimizes molecular degradation, controlling the primary air velocity, volume and temperature to produce thermoplastic fibers at least 80% of which have a diameter of 7 microns or less and having an average length of more than 10 centimeters, introducing a highly uniform high velocity secondary air stream in quantities sufficient to cool the fibers and maintain good fiber separation, collecting the fibers at a forming distance to form a core web with low interfiber bonding, prior to embossing the web to form a fabric, and collecting the fibers of said core web on said first surface veneer web such that said veneer web is directly contiguous to said core web.
Claim 15
Independent Claim
315 words
A method of producing an unreinforced microfiber fabric having improved surface abrasion resistance wherein a fiber-forming thermoplastic polymer resin in molten form is forced through a row of orifices in a heated nozzle into a stream of inert gas to attenuate the resin into fibers, the fibers are collected on a receiver to form a web, and the web is thermally bonded to form a fabric comprising: (a) at a first heated nozzle, maintaining the polymer melt temperature at a level which minimizes molecular degradation, controlling the primary air velocity, volume and temperature, polymer resin throughput and exit temperature to produce a first layer of thermoplastic fibers having an average fiber diameter of greater than 8 microns, and in which 75% of the fibers have a fiber diameter of at least 7 microns, collecting the fibers on a receiver at a forming distance to form a first unreinforced surface veneer web with good interfiber bonding and having a basis weight in the range of 3 grams per square meter to 10 grams per square meter and a wet and dry surface abrasion resistance of greater than 15 cycles to pill; (b) at a second heated nozzle, maintaining the polymer melt temperature at a level which minimizes molecular degradation, controlling the primary air velocity, volume and temperature to produce thermoplastic fibers at least 80% of which have a diameter of 7 microns or less and having an average length of more than 10 centimeters, introducing a highly uniform high velocity secondary air stream in quantities sufficient to cool the fibers and maintain good fiber separation, collecting the fibers at a forming distance to form a core web with low interfiber bonding, prior to embossing the web to form a fabric, and collecting the fibers of said core web on said first surface veneer web such that said veneer web is directly contiguous to said core web.
Claim 16
Dependent Claim
42 words
The method of claim 11 further comprising: (c) at a third heated nozzle producing a second surface veneer web of fibers similar to said first veneer web and collecting said second surface veneer web on the exposed surface of said core web.
Claim 17
Dependent Claim
28 words
A method of producing an unreinforced microfiber embossed fabric as in claim 11 or 12 wherein said veneer webs have an average fiber diameter of about 9 microns.
Claim 18
Dependent Claim
13 words
The method of claim 11 or 12 further comprising thermally embossing said webs.
References Cited (Backward Citations)
US2988469A
Cited
US3795571A
Cited
US4355066A
Cited
US4652487A
Cited
US4657802A
Cited
US4622259A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-09-27 | 1992-03-28 | 1992-09-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-09-27 | 1996-03-28 | 1996-09-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-09-27 | 2000-03-28 | 2000-09-27 | $7700.00 | Window Closed / Lapsed |