Process for the production of an oriented monocrystalline silicon film with localized defects on an insulating support
Assignee: Individual
•
Filing: 1986-04-21
•
Granted: 1988-09-27
•
Expires: 2006-04-21
Abstract
Abstract This process consists of producing in the insulating support a periodic configuration which, in the form of regularly spaced parallel insulating strips, has overhanging and recessed parts, the width of the overhanging parts being smaller than that of the recessed parts; depositing on the complete structure obtained a silicon film; covering the silicon film with an encapsulating material layer; carrying out heat treatment in order to recrystallize the silicon film in monocrystalline form, said treatment consisting of locally melting the silicon film and displacing the melted zone parallel to the insulating strips, the melted zone being in the form of a line perpendicular to said strips, followed by the elimination of the encapsulating material layer.
Inventors
- 👤 Michel Haond
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 21:31
CPC Classifications
C; C30; C30B; C30B13/00; C30B13/34; Y; Y10; Y10S; Y10S117/00; Y10S117/913
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
141 words
A process for the production of a monocrystalline silicon film on an insulating support, comprising the steps of: (a) etching an insulating support in a manner which produces overhanging insulating strips and recessed insulating strips thereon, said strips being parallel and alternating with each other with the width of the overhanging strips being less than the width of the recessed strips; (b) depositing a silicon film on the etched structures; (c) covering the deposited silicon film with an encapsulating material as a layer; (d) heat treating the structure in order to recrystallize the silicon film in monocrystalline form, said treatment consisting of locally melting the silicon film and moving the melted zone parallel to the insulating strips, the melted zone being in the form of a line which is perpendicular to said strips; and (e) removing the layer of encapsulating material.
Claim 2
Dependent Claim
141 words
A process for the production of a monocrystalline silicon film on an insulating support, comprising the steps of: (a) etching an insulating support in a manner which produces overhanging insulating strips and recessed insulating strips thereon, said strips being parallel and alternating with each other with the width of the overhanging strips being less than the width of the recessed strips; (b) depositing a silicon film on the etched structures; (c) covering the deposited silicon film with an encapsulating material as a layer; (d) heat treating the structure in order to recrystallize the silicon film in monocrystalline form, said treatment consisting of locally melting the silicon film and moving the melted zone parallel to the insulating strips, the melted zone being in the form of a line which is perpendicular to said strips; and (e) removing the layer of encapsulating material.
Claim 3
Dependent Claim
19 words
The production process according to claim 1, wherein the overhanging and recessed strips are arranged in a periodic configuration.
Claim 4
Dependent Claim
41 words
The production process according to claim 1, which further comprises, prior to step (d), forming a crystallization delaying strip on the encapsulating material layer above each overhanging strip, said crystallization delaying strip having the same width as the associated overhanging strip.
Claim 5
Dependent Claim
19 words
The production process according to claim 1, wherein the melted zone is displaced at a speed below 0.5 mm/s.
Claim 6
Dependent Claim
21 words
The production process according to claim 1, wherein the melted zone is displaced at a speed of 0.1 to 0.2 mm/s.
Claim 7
Dependent Claim
35 words
The production process according to claim 1, wherein the heat treatment takes place by subjecting the structure to the action of an energy line perpendicular to the insulating strips and moving parallel to said strips.
Claim 8
Dependent Claim
35 words
The production process according to claim 5, wherein an energy line is formed by rapidly scanning the surface of the encapsulating material layer with an energy beam in a direction perpendicular to the insulating strips.
Claim 9
Dependent Claim
36 words
The production process according to claim 1, wherein at least one notch is formed in each recessed strip, by etching the insulating support, said notches being in the form of strips parallel to the overhanging strips.
Claim 10
Dependent Claim
19 words
The production process according to claim 8, wherein each notch is produced in the centre of each recessed part.
Claim 11
Dependent Claim
43 words
The production process according to claim 3, wherein the crystallization delaying strips are formed by covering the encapsulating material layer with a layer of a crystallization delaying material and by etching the latter with a pattern identical to that of the overhanging strips.
Claim 12
Dependent Claim
77 words
The production process according to claim 1, which further comprises, before stage (c), depositing an insulating material as a layer on the silicon film thereby eliminating the relief of the latter, followed by simultaneous etching of the insulating material layer and the silicon film at identical etching speeds for insulant and silicon until the insulating material layer and the relief parts of the silicon are completely eliminated, in order to flatten the surface of said silicon film.
Claim 13
Dependent Claim
25 words
The production process according to claim 8, wherein the insulating support is etched to form recessed strips and/or notches by a reactive ionic etching process.
Claim 14
Dependent Claim
20 words
The production process according to claim 1, wherein the insulating support and/or encapsulating material layer are made from silicon oxide.
Claim 15
Dependent Claim
23 words
The production process according to claim 1, wherein stage b) consists of depositing an amorphous or polycrystalline silicon film on the etched structure.
Claim 16
Dependent Claim
37 words
The production process according to any one of the claims 2 to 14 and 1, wherein the heat treatment comprises a stage of preheating the structure obtained at a temperature below the melting point of the silicon.
Claim 17
Dependent Claim
16 words
The production process according to claim 3, wherein the crystallization delaying strips are silicon nitride strips.
Claim 18
Dependent Claim
35 words
The production process according to claim 3, wherein the crystallization delaying strips are formed with an antireflecting material when the heat treatment takes place by subjecting the structure to the action of a light beam.
References Cited (Backward Citations)
FR2537607A1
Cited
US4678538A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-09-27 | 1992-03-28 | 1992-09-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-09-27 | 1996-03-28 | 1996-09-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-09-27 | 2000-03-28 | 2000-09-27 | $7700.00 | Window Closed / Lapsed |