Strontium-containing yttrium oxide ceramic body

Claim 2

A process for producing a closed-pore sintered body consisting essentially of a solid solution of strontium oxide in yttrium oxide which consists essentially of forming a powder consisting essentially of a mixture and/or solid solution of yttrium oxide and strontium oxide, said strontium oxide ranging from about 0.15 mole % to about 1.2 mole % of said powder, forming said powder into a compact having a density of at least about 45% of the density of yttrium oxide, an firing said compact in an atmosphere of hydrogen at a temperature ranging from about 1625° C. to about 2000° C. for a time sufficient to produce said sintered body.

Claim 3

The process according to claim 1 wherein said atmosphere is wet hydrogen.

Claim 4

The process according to claim 1 wherein said firing is initially carried out in an atmosphere of dry hydrogen to produce a closed pore body, then said firing is carried out in an atmosphere of wet hydrogen.

Claim 5

The process according to claim 1 wherein said temperature ranges from about 1700° C. to about 1950° C.

Claim 6

The process according to claim 1 wherein said strontium oxide ranges from about 0.3 mole % to about 0.8 mole % of said powder.

Claim 7

A process for producing a sintered body consisting essentially of a solid solution of strontium oxide in yttrium oxide which is at least optically translucent which consists essentially of preparing a forming powder consisting essentially of a mixture and/or solid solution of yttrium oxide and strontium oxide, said strontium oxide ranging from about 0.15 mole % to about 1.2 mole % of said forming powder, shaping said forming powder into a compact having a density of at least about 45% of the density for yttrium oxide, firing said compact at a temperature ranging from about 1625° C. to about 2000° C. for a time sufficient to produce said sintered body, and decreasing the firing temperature at a rate which has no significant deleterious effect on said sintered body, said firing being carried out in an atmosphere of hydrogen, said hydrogen atmosphere containing at least a sufficient partial pressure of oxygen at least when said compact becomes a closed pore body to produce said optically translucent sintered body.

Claim 8

A process for producing a sintered body consisting essentially of a solid solution of strontium oxide in yttrium oxide which is at least optically translucent which consists essentially of preparing a forming powder consisting essentially of a mixture and/or solid solution of yttrium oxide and strontium oxide, said strontium oxide ranging from about 0.15 mole % to about 1.2 mole % of said forming powder, shaping said forming powder into a compact having a density of at least about 45% of the density for yttrium oxide, firing said compact at a temperature ranging from about 1625° C. to about 2000° C. for a time sufficient to produce said sintered body, and decreasing the firing temperature at a rate which has no significant deleterious effect on said sintered body, said firing being carried out in an atmosphere of hydrogen, said hydrogen atmosphere containing at least a sufficient partial pressure of oxygen at least when said compact becomes a closed pore body to produce said optically translucent sintered body.

Claim 9

The process according to claim 6 wherein said firing is carried out in an atmosphere of wet hydrogen.

Claim 10

The process according to claim 6 wherein said firing is initially carried out in an atmosphere of dry hydrogen to produce a closed pore body, then said firing is carried out in an atmosphere of wet hydrogen.

Claim 11

The process according to claim 6 wherein said temperature ranges from about 1700° C. to about 1950° C.

Claim 12

The process according to claim 6 wherein said strontium oxide ranges from about 0.3 mole % to about 0.8 mole % of said powder.

Claim 13

The process according to claim 6 wherein said sintered strontium-containing yttrium oxide body is optically transparent.

Claim 14

A closed-pore polycrystalline body having a composition consisting essentially of Y 2-x Sr x O 3-x/2 wherein x ranges from about 0.0015 to about 0.012, said body having an average grain size ranging from about 5 microns to about 250 microns, said grains being cubic in symmetry, said body consisting essentially of a solid solution of strontium oxide in yttrium oxide.

Claim 15

A closed-pore polycrystalline body having a composition consisting essentially of Y 2-x Sr x O 3-x/2 wherein x ranges from about 0.0015 to about 0.012, said body having an average grain size ranging from about 5 microns to about 250 microns, said grains being cubic in symmetry, said body consisting essentially of a solid solution of strontium oxide in yttrium oxide.

Claim 16

The body according to claim 12 wherein x ranges from about 0.003 to 0.008.

Claim 17

The body according to claim 12 having an average grain size ranging from about 20 microns to about 50 microns.

Claim 18

An optically translucent closed-pore polycrystalline body having a composition consisting essentially of Y 2-x Sr x O 3-x/2 wherein x ranges from about 0.0015 to about 0.012, said body having an average grain size ranging from about 5 microns to about 250 microns, said grains being cubic in symmetry, said body consisting essentially of a solid solution of strontium oxie in yttrium oxide.

Claim 19

An optically translucent closed-pore polycrystalline body having a composition consisting essentially of Y 2-x Sr x O 3-x/2 wherein x ranges from about 0.0015 to about 0.012, said body having an average grain size ranging from about 5 microns to about 250 microns, said grains being cubic in symmetry, said body consisting essentially of a solid solution of strontium oxie in yttrium oxide.

Claim 20

The optically translucent body according to claim 15 wherein x ranges from about 0.003 to 0.008.

Claim 21

The optically translucent body according to claim 15 having an average grain size ranging from about 25 microns to about 50 microns, said body being in the form of a hollow body having a wall thickness ranging from about 1/2 to about 1 millimeter.

Claim 22

The body according to claim 15 in the form of a lamp envelope.

Claim 23

An optically transparent closed-pore polycrystalline body having a composition consisting essentially of Y 2-x Sr x O 3-x/2 wherein x ranges from about 0.003 to about 0.012, said body having an average grain size ranging from about 5 microns to about 250 microns, said grains being cubic in symmetry, said body consisting essentially of a solid solution of strontium oxide in yttrium oxide.

Claim 24

An optically transparent closed-pore polycrystalline body having a composition consisting essentially of Y 2-x Sr x O 3-x/2 wherein x ranges from about 0.003 to about 0.012, said body having an average grain size ranging from about 5 microns to about 250 microns, said grains being cubic in symmetry, said body consisting essentially of a solid solution of strontium oxide in yttrium oxide.

Claim 25

The optically transparent body according to claim 19 wherein x ranges from about 0.003 to 0.008.

Claim 26

The optically transparent body according to claim 19 having an average grain size ranging from about 25 microns to about 50 microns, said body being in the form of a hollow body having a wall thickness ranging from about 1/2 to about 1 millimeter.

Claim 27

body according to claim 19 in the form of a lamp envelope.