Process for the manufacture of a rough-shaped, cold-rolled cladding tube of zirconium alloy
Assignee: Pechiney SA
•
Filing: 1985-08-13
•
Granted: 1988-08-16
•
Expires: 2005-08-13
Abstract
Abstract A process for the manufacture of a rough-shaped, cold-rolled cladding tube of "Zircaloy 2" or "Zircaloy 4", in which (a) an ingot of the alloy is transformed by hot working and the bar obtained is cut up into billets, (b) the bar or the billet is then immersed from the β range, (c) at least one billet which has thus been immersed is extruded in the α range, (d) the rough shape extruded is cold-rolled and heat-treated to give rise to a cold-rolled, rough-shaped cladding tube, wherein the hot working is first carried out in the β range with a cross-sectional reduction ratio of at least 1.5 and then in the α range with a cross-sectional reduction ratio of at least 3, is disclosed.
Inventors
- 👤 Daniel Charquet
- 👤 Yvon Millet
- 👤 Marc Dall'Agnol
- 👤 Rene Robin
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 22:32
CPC Classifications
C; C22; C22F; C22F1/00; C22F1/16; C22F1/18; C22F1/186; Y; Y10; Y10S; Y10S376/00; Y10S376/90
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
194 words
A process for the manufacture of a rough-shaped, cold-rolled cladding tube of zirconium alloy, Zircaloy 2 or Zircaloy 4, said process comprising: (a) transforming an ingot of the said zirconium alloy to the form of a bar by hot-working; cutting the worked bar obtained into billets; piercing a hole substantially coaxially in one of the said billets; and machining this billet; (b) quenching in water, from the β range, either the worked-bar before it is cut into billets or at least one of the said billets before or after piercing; (c) extruding in the α range at least one of the said perforated and quenched billets in the form of an extruded rough-shaped; and (d) cold-rolling and heat-treating at least one of the said extruded rough-shape to produce a cold-rolled, rough-shaped cladding tube; wherein the said process is characterized in that the said hot-working is first carried out in the β range at a temperature of from 960° to 1050° C. with a cross-sectional reduction ratio of from 1.5 to 3, and then in the α range at a temperature from 740° to 790° C. with a cross-sectional reduction ratio of at least 3.
Claim 2
Dependent Claim
194 words
A process for the manufacture of a rough-shaped, cold-rolled cladding tube of zirconium alloy, Zircaloy 2 or Zircaloy 4, said process comprising: (a) transforming an ingot of the said zirconium alloy to the form of a bar by hot-working; cutting the worked bar obtained into billets; piercing a hole substantially coaxially in one of the said billets; and machining this billet; (b) quenching in water, from the β range, either the worked-bar before it is cut into billets or at least one of the said billets before or after piercing; (c) extruding in the α range at least one of the said perforated and quenched billets in the form of an extruded rough-shaped; and (d) cold-rolling and heat-treating at least one of the said extruded rough-shape to produce a cold-rolled, rough-shaped cladding tube; wherein the said process is characterized in that the said hot-working is first carried out in the β range at a temperature of from 960° to 1050° C. with a cross-sectional reduction ratio of from 1.5 to 3, and then in the α range at a temperature from 740° to 790° C. with a cross-sectional reduction ratio of at least 3.
Claim 3
Dependent Claim
32 words
The process of claim 1, wherein after the said hot-working in the β range, hot-working is carried out in the α range with a cross-sectional reduction ratio of from 5 to 8.
Claim 4
Dependent Claim
68 words
The process of claim 1, wherein said hot-working is first carried out in the β range at a temperature of from 960° to 1050° C. with a cross-sectional reduction ratio of from 1.5 to 3, and then in the α range at a temperature of from 740° to 790° C. with a cross-sectional reduction ratio of at least 3, wherein said hot-working is carried out without intermediate quenching.
Claim 5
Dependent Claim
68 words
The process of claim 2, wherein said hot-working is carried out in the β range at a temperature of from 960° to 1050° C. with a cross-sectional reduction ratio of from 1.5 to 3, and then in the α range at a temperature of from 740° to 790° C. with a cross-sectional reduction ratio of from 5 to 8, wherein said hot-working is carried out without intermediate quenching.
References Cited (Backward Citations)
FR1327734A
Cited
JPS6050155A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-08-16 | 1992-02-15 | 1992-08-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-08-16 | 1996-02-15 | 1996-08-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-08-16 | 2000-02-15 | 2000-08-16 | $7700.00 | Window Closed / Lapsed |