Modified polyolefin resin and a composition containing the same
Assignee: Mitsubishi Chemical Corp
•
Filing: 1986-06-26
•
Granted: 1988-08-09
•
Expires: 2006-06-26
Abstract
Abstract A modified polyolefin resin and a composition containing therein such modified polyolefin, having excellent adhesive property and heat-sealing property at the time of high speed forming operations, the modified polyolefin resin consisting essentially of: a copolymer of ethylene and alpha -olefin having 4 or more carbon atoms, the copolymer having a density in a range of from 0.890 to 0.910 g/cm3, a ratio of a weight-average molecular weight (Mw) to a number-average molecular weight (Mn) of Mw/Mn=2 to 15, and a product of a melt tension (g) and a melt-index (g/10 min.) of a molten resin measured at 160 DEG C. of 4 or below; and unsaturated carboxylic acid or derivatives thereof grafted on the ethylene type copolymer at a ratio of from 0.01 to 3% by weight.
Inventors
- 👤 Shigeaki Okano
- 👤 Katsuhiko Hayashi
- 👤 Yoshiteru Sakurazawa
- 👤 Yoshinori Suga
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 07:34
CPC Classifications
C; C08; C08F; C08F255/00; C08F255/02
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
107 words
A modified polyolefin resin, which consists essentially of: (a) a copolymer of ethylene and an α-olefin of at least 4 carbon atoms, said copolymer having a density in the range of from 0.890 to 0.910 g/cm 3 , a ratio of the weight-average molecular weight (Mw) to the number-average molecular weight (Mn) of Mw/Mn=2 to 15, and a product of the melt tension (g) and the melt index (g/10 min) of the molten copolymer measured at 160° C. of no more than 4; and (b) an unsaturated carboxylic acid or derivative thereof grafted on said ethylene copolymer in an amount of from 0.01 to 3% by weight.
Claim 2
Dependent Claim
107 words
A modified polyolefin resin, which consists essentially of: (a) a copolymer of ethylene and an α-olefin of at least 4 carbon atoms, said copolymer having a density in the range of from 0.890 to 0.910 g/cm 3 , a ratio of the weight-average molecular weight (Mw) to the number-average molecular weight (Mn) of Mw/Mn=2 to 15, and a product of the melt tension (g) and the melt index (g/10 min) of the molten copolymer measured at 160° C. of no more than 4; and (b) an unsaturated carboxylic acid or derivative thereof grafted on said ethylene copolymer in an amount of from 0.01 to 3% by weight.
Claim 3
Dependent Claim
122 words
The modified polyolefin resin of claim 1, wherein said unsaturated carboxylic acid or derivative thereof is acrylic acid, ethacrylic acid, maleic acid, fumaric acid, itaconic acid, citraconic acid, maleic anhydride, citraconic anhydride, itaconic anhydride, methyl acrylate, methy methacrylate, ethyl acrylate, ethyl methacrylate, butyl acrylate, butyl methacrylate, glycidyl acrylate, glycidyl methacrylate, hydroxyethyl acrylate, hydroxybutyl acrylate, maleic acid monoethyl ester, maleic acid diethyl ester, fumaric acid monomethyl ester, fumaric acid dimethyl ester, itaconic acid monomethyl ester, itaconic acid diethyl ester, acrylamide, methacrylamide, maleic acid monoamide, maleic acid diamide, maleic acid-N-monoethyl amide, maleic acid-N,N-diethyl amide, maleic acid-N-monoethylamide, fumaric acid-N,N-dibutylamide, maleimide, N-butyl maleimide, N-phenyl maleimide, sodium acrylate, sodium methacrylate, potassium acrylate, potassium methacrylate, cis-4-cyclohexene-1,2-dicarboxylic acid, endo-bicyclo-[5]-heptene-2,3-dicarboxylic anhydride, endo-bicyclo-[2,2,1]-5- heptene-2,3-dicarboxylic acid, endo-bicyclo[2,2,1]-1,2,3, 4,7,7-hexachloro-2-heptene-5,6-dicarboxylic anhydride, or endo-bicyclo[2,2,1]-1,2,3,4,7,7-hexachloro-2-heptene-5,6-dicarboxylic acid.
Claim 4
Dependent Claim
157 words
A modified polyolefin resin composition, which consists essentially of: (a) a modified polyolefin resin composed of a copolymer of ethylene and an α- olefin having a carbon atom content of at least 5, said copolymer having a density within the range of from 0.890-0.910 g/cm 3 , a weight-average molecular weight (Mw) to number-average molecular weight (Mn) ratio of 2 to 15, and a product of the melt tension (g) and the melt index (g/10 min) of the molten copolymer measured at 160° C. of no more than 4, and an unsaturated carboxylic acid or derivative thereof grafted on said ethylene copolymer in an amount of from 0.01 to 3% by weight; and (b) an unmodified polyolefin resin blended with said modified polyolefin resin in a ratio of from 1:99 to 99:1(by weight), with the content of said unsaturated carboxylic acid or derivative thereof being present in the blended composition ranging from 0.01 to 1% by weight.
Claim 5
Dependent Claim
157 words
A modified polyolefin resin composition, which consists essentially of: (a) a modified polyolefin resin composed of a copolymer of ethylene and an α- olefin having a carbon atom content of at least 5, said copolymer having a density within the range of from 0.890-0.910 g/cm 3 , a weight-average molecular weight (Mw) to number-average molecular weight (Mn) ratio of 2 to 15, and a product of the melt tension (g) and the melt index (g/10 min) of the molten copolymer measured at 160° C. of no more than 4, and an unsaturated carboxylic acid or derivative thereof grafted on said ethylene copolymer in an amount of from 0.01 to 3% by weight; and (b) an unmodified polyolefin resin blended with said modified polyolefin resin in a ratio of from 1:99 to 99:1(by weight), with the content of said unsaturated carboxylic acid or derivative thereof being present in the blended composition ranging from 0.01 to 1% by weight.
Claim 6
Dependent Claim
99 words
The modified polyolefin resin composition of claim 3, wherein said unmodified polyolefin resin is a high density polyethylene, a linear low density polyethylene, a low density polyethylene, a copolymer of a low crystalline ethylene and an α- olefin, a copolymer rubber of ethylene and an α- olefin, a copolymer rubber of ethylene, an α- olefin and a diene, a polypropylene, a copolymer of propylene and an α- olefin, a polybutene-1, a poly-4-methyl-pentene-1, poly-3-methylbutene-1, a copolymer of ethylene and a vinyl ester, a copolymer of ethylene and an acrylic acid ester, a copolymer of ethylene and an unsaturated carboxylic acid.
References Cited (Backward Citations)
US4011382A
Cited
GB2006232A
Cited
US4619972A
Cited
US4330639A
Cited
US4440911A
Cited
GB2116187A
Cited
JPS59179543A
Cited
JPS6114272A
Cited
US4612155A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-08-09 | 1992-02-08 | 1992-08-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-08-09 | 1996-02-08 | 1996-08-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-08-09 | 2000-02-08 | 2000-08-09 | $7700.00 | Window Closed / Lapsed |