Hydrocarbon conversion catalyst

Claim 2

A process for making a hydrocarbon conversion cataylst which comprises: (a) extruding a mixture of a porous, inorganic refractory oxide component and a crystalline aluminosilicate zeolite having cracking activity to form extrudates; and (b) calcining said extrudates in the presence of added steam at a water vapor partial pressure greater than about 2.0 p.s.i.a. under conditions such that the unit cell size of said crystalline aluminosilicate zeolite is reduced to a value between about 24.20 and about 24.35 Angstroms.

Claim 3

A process as defined by claim 1 wherein the water vapor partial pressure of said added steam and the temperature and time of said calcination are such that, if said aluminosilicate zeolite was calcined in steam alone without first being mixed and extruded with said refractory oxide component, the water vapor sorptive capacity of said aluminosilicate zeolite would be less than about 5 weight percent of said zeolite at 25° C. and a p/p° value of 0.10.

Claim 4

A process as defined by claim 1 which further comprises impregnating said calcined extrudates with at least one hydrogenation component.

Claim 5

A process as defined by claim 3 wherein said calcined extrudates are impregnated with a Group VIII metal hydrogenation component and a Group VIA metal hydrogenation component.

Claim 6

A process as defined by claim 1 wherein said crystalline aluminosilicate zeolite used in step (a) comprises LZY-82 zeolite.

Claim 7

A process as defined by claim 1 wherein said mixture is extruded through a die having a shape that results in extrudates having a surface-to-volume ratio greater than that of a cylinder.

Claim 8

A process as defined by claim 1 comprising the further step of ion exchanging said calcined extrudates with ammonium ions to further reduce the sodium content of said extrudates.

Claim 9

A process as defined by claim 6 wherein said die has the shape of a three-leaf clover.

Claim 10

A process as defined by claim 4 wherein said Group VIA metal hydrogenation component comprises a tungsten component or a molybdenum component and said Group VIII metal hydrogenation component comprises a nickel component or a cobalt component.

Claim 11

A process as defined by claim 1 wherein said porous, inorganic refractory oxide component comprises a dispersion of silica-alumina in gamma alumina.

Claim 12

A process as defined by claim 1 wherein said crystalline aluminosilicate zeolite used in step (a) comprises LZ-210 zeolite.

Claim 13

A process as defined by claim 1 wherein said crystalline aluminosilicate zeolite used in step (a) is preparad by a process comprising (1) ammonium exchanging a sodium Y zeolite to a sodium content between about 0.6 and about 5 weight percent, calculated as Na 2 O, (2) calcining the ammonium-exchanged zeolite at a temperature between about 600° F. and about 1650° F. in the presence of steam at a water vapor partial pressure of at least about 0.2 p.s.i.a. to reduce the unit cell size of said ammonium-exchanged zeolite to a value in the range between about 24.40 and about 24.64 Angstroms, and (3) leaching the steam-calcined zeolite with a solution of hydrochloric acid having a concentration between about 0.1 N and about 1.0 N.

Claim 14

A process as defined by claim 1 wherein said extrudates are formed by extruding a mixture of a porous, inorganic refractory oxide component, a crystalline aluminosilicate zeolite having cracking activity and at least one hydrogenation component.

Claim 15

A process as defined by claim 1 wherein said water vapor partial pressure is between about 5 p.s.i.a. and about 35 p.s.i.a.

Claim 16

A process as defined by claim 1 wherein said mixture is extruded in the shape of cylinders.

Claim 17

A process for making a hydrocarbon conversion catalyst which consists essentially of: (a) extruding a mixture of a porous, inorganic refractory oxide component and a crystalline aluminosilicate zeolite having cracking activity to form extrudates; (b) calcining said extrudates in the presence of added steam at a water vapor partial pressure greater than about 2.0 p.s.i.a. under conditions such that the unit cell size of said crystalline aluminosilicate zeolite is reduced to a value between about 24.20 and about 24.35 Angstroms; and (c) impregnating said calcined extrudates with at least one hydrogenation metal component.

Claim 18

A process for making a hydrocarbon conversion catalyst which consists essentially of: (a) extruding a mixture of a porous, inorganic refractory oxide component and a crystalline aluminosilicate zeolite having cracking activity to form extrudates; (b) calcining said extrudates in the presence of added steam at a water vapor partial pressure greater than about 2.0 p.s.i.a. under conditions such that the unit cell size of said crystalline aluminosilicate zeolite is reduced to a value between about 24.20 and about 24.35 Angstroms; and (c) impregnating said calcined extrudates with at least one hydrogenation metal component.

Claim 19

A process as defined by claim 16 wherein the water vapor partial pressure of said added steam and the temperature and time of said calcination are such that, if said aluminosilicate zeolite was calcined in steam alone without first being mixed and extruded with said refractory oxide component, the water vapor sorptive capacity of said aluminosilicate zeolite would be less than about 5 weight percent of said zeolite at 25° C. and a p/p° value of 0.10.

Claim 20

A process as defined by claim 16 wherein said crystalline aluminosilicate Y zeolite used in step (a) comprises LZ-210 zeolite.

Claim 21

A process as defined by claim 16 wherein said crystalline aluminosilicate zeolite used in step (a) is prepared by a process comprising the steps of (1) ammonium exchanging a sodium Y zeolite to a sodium content between about 0.6 and about 5 weight percent, calculated as Na 2 O, (2) calcining the ammonium-exchanged zeolite at a temperature between about 600° F. and about 1650° F. in the presence of steam at a water vapor partial pressure of at least about 0.2 p.s.i.a. to reduce the unit cell size of said ammonium-exchanged zeolite to a value in the range between about 24.40 and about 24.64 Angstroms, and (3) ammonium exchanging the steam-calcined zeolite to reduce the sodium content of the zeolite below about 0.6 weight percent, calculated as Na 2 O.

Claim 22

A process for making a hydrocarbon conversion catalyst which comprises: (a) ammonium exchanging a sodium Y zeolite to a sodium content between about 0.6 and about 5 weight percent, calculated as Na 2 O; (b) calcining said ammonium-exchanged zeolite at a temperature between about 600° F. and about 1650° F. in the presence of steam at a water vapor partial pressure of at least about 0.2 p.s.i.a. to reduce the unit cell size of said ammonium-exchanged zeolite to a value in the range between about 24.40 and about 24.64 Angstroms; (c) ammonium exchanging the steam-calcined zeolite from step (b) to reduce the sodium content of the zeolite below about 0.6 weight percent, calculated as Na 2 O; (d) extruding a mixture of a porous, inorganic refractory oxide component and said ammonium-exchanged, steam-calcinad zeolite from step (c) to form extrudates; (e) calcined said extrudates in the presence of added steam at a water vapor partial pressure greater than about 5 p.s.i.a. under conditions such that the unit cell size of the zeolite in said extrudates is further reduced to a value between about 24.20 and about 24.35 Angstroms; and (f) impregnating said calcined extrudates with at least one hydrogenation metal component.

Claim 23

A process for making a hydrocarbon conversion catalyst which comprises: (a) ammonium exchanging a sodium Y zeolite to a sodium content between about 0.6 and about 5 weight percent, calculated as Na 2 O; (b) calcining said ammonium-exchanged zeolite at a temperature between about 600° F. and about 1650° F. in the presence of steam at a water vapor partial pressure of at least about 0.2 p.s.i.a. to reduce the unit cell size of said ammonium-exchanged zeolite to a value in the range between about 24.40 and about 24.64 Angstroms; (c) ammonium exchanging the steam-calcined zeolite from step (b) to reduce the sodium content of the zeolite below about 0.6 weight percent, calculated as Na 2 O; (d) extruding a mixture of a porous, inorganic refractory oxide component and said ammonium-exchanged, steam-calcinad zeolite from step (c) to form extrudates; (e) calcined said extrudates in the presence of added steam at a water vapor partial pressure greater than about 5 p.s.i.a. under conditions such that the unit cell size of the zeolite in said extrudates is further reduced to a value between about 24.20 and about 24.35 Angstroms; and (f) impregnating said calcined extrudates with at least one hydrogenation metal component.

Claim 24

A process as defined by claim 20 wherein said calcined extrudates are impregnated with a Group VIA metal hydrogenation component and a Group VIII metal hydrogenation component.

Claim 25

A process as defined by claim 21 wherein the water vapor partial pressure of said added steam in step (e) and the temperature and time of said calcination in step (e) are such that if the zeolite in said extrudates from step (c) was calcined in steam alone without first being mixed and extruded with said refractory oxide component, the water vapor sorptive capacity of said zeolite would be less than about 5 weight percent of said zeolite at 25° C. and a p/p° value of 0.10.

Claim 26

A process as defined by claim 22 wherein said porous, inorganic refractory oxide component comprises a dispersion of silica-alumina in gamma alumina.

Claim 27

A catalyst composition prepared by a process comprising: (a) extruding a mixture of a porous, inorganic refractory oxide component and a crystalline aliminosilicate zeolite having cracking activity to form extrudates; and (b) calcining said extrudates in the presence of added steam at a water vapor partial pressure greater than about 2.0 p.s.i.a. under conditions such that the unit cell size of said crystalline aluminosilicate zeolite is reduced to a value between about 24.20 and about 24.35 Angstroms.

Claim 28

A catalyst composition prepared by a process comprising: (a) extruding a mixture of a porous, inorganic refractory oxide component and a crystalline aliminosilicate zeolite having cracking activity to form extrudates; and (b) calcining said extrudates in the presence of added steam at a water vapor partial pressure greater than about 2.0 p.s.i.a. under conditions such that the unit cell size of said crystalline aluminosilicate zeolite is reduced to a value between about 24.20 and about 24.35 Angstroms.

Claim 29

A catalyst composition as defined by claim 24 wherein the water vapor partial pressure of said added steam and the temperature and time of said calcination are such that, if said aluminosilicate zeolite was calcined in steam alone without first being mixed and extruded with said refractory oxide component, the water vapor sorptive capacity of said aluminosilicate zeolite would be less than about 5 weight percent of said zeolite at 25° C. and a p/p° value of 0.10.

Claim 30

A catalyst composition as defined by claim 24 wherein said calcined extrudates are impregnated with at least one hydrogenation component.

Claim 31

A catalyst composition as defined by claim 24 wherein said porous, inorganic refractory oxide component comprises a dispersion of silica-alumina in gamma alumina.

Claim 32

A catalyst composition as defined by claim 24 wherein said crystalline aluminosilicate Y zeolite used in step (a) comprises LZY-82 zeolite.

Claim 33

A catalyst composition as defined by claim 24 wherein said crystalline aluminosilicate zeolite used in step (a) comprises LZ-210 zeolite.

Claim 34

A catalyst composition as defined by claim 24 wherein said crystalline aluminosilicate zeolite used in step (a) is prepared by a process comprising the steps of (1) ammonium exchanging a sodium Y zeolite to a sodium content between about 0.6 and about 5 weight percent, calculated as Na 2 O (2) calcining the ammonium-exchanged zeolite at a temperature between about 600° F. and about 1650° F. in the presence of steam at a water vapor partial pressure of at least about 0.2 p.s.i.a. to reduce the unit cell size of said ammonium-exchanged zeolite to a value in the range between about 24.40 and about 24.64 Angstroms, and (3) ammonium exchanging the steam-calcined zeolite to reduce the sodium content of the zeolite below about 0.6 weight percent, calcinated as Na 2 O.