Vehicle component having improved friction material
Assignee: Eaton Corp
•
Filing: 1987-06-03
•
Granted: 1988-08-09
•
Expires: 2007-06-03
Abstract
Abstract A vehicle component such as a transmission blocker ring (81) having an improved friction material (56) is provided. Friction material (56) comprises a composite of from about 25% to about 75% by weight of a flurocarbon polymer and from about 75% to about 25% by weight of substantially uniformly dispersed ceramic fiber and which is provided with controlled crystallinity by reason of having been cooled at a rate of less than about 20° C. per minute after having been sintered at a predetermined sintering or annealing temperature and time for the friction material.
Inventors
- 👤 Selami Y. Pusatcioglu
- 👤 Thomas A. Genise
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 23:13
CPC Classifications
F; F16; F16D; F16D69/00; F16D69/02; F16D69/025; F16D69/026; F16H; F16H63/00; F16H63/02; F16H63/30; F16H2063/3093
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
118 words
A component for a vehicle part, said component having an improved friction material disposed thereupon operative to enhance frictional engagement therewith, said friction material comprising a composite of from about 25% to about 75% by weight of a flurocarbon polymer and from about 75% to about 25% by weight ceramic fibers dispersed substantially uniformly therein, and said improvement characterized by said material having improved frictional engagement characteristics imparted thereto by reason of said polymer having controlled increased crystallinity arising from said material having been cooled at a rate of less than about 20° C. per minute after having been sintered at a temperature within a predetermined sintering temperature range for said polymer for a predetermined period of time.
Claim 2
Dependent Claim
118 words
A component for a vehicle part, said component having an improved friction material disposed thereupon operative to enhance frictional engagement therewith, said friction material comprising a composite of from about 25% to about 75% by weight of a flurocarbon polymer and from about 75% to about 25% by weight ceramic fibers dispersed substantially uniformly therein, and said improvement characterized by said material having improved frictional engagement characteristics imparted thereto by reason of said polymer having controlled increased crystallinity arising from said material having been cooled at a rate of less than about 20° C. per minute after having been sintered at a temperature within a predetermined sintering temperature range for said polymer for a predetermined period of time.
Claim 3
Dependent Claim
119 words
A component for a vehicle part, said component having an improved friction material disposed thereupon operative to enhance frictional engagement therewith, said friction material comprising a composite of from about 25% to about 75% by weight of a flurocarbon polymer and from about 75% to about 25% by weight ceramic fibers dispersed substantially uniformly therein, and said improvement characterized by said material having improved frictional engagement characteristics imparted thereto by reason of said polymer having controlled increased crystallinity arising from said material having been heated at a temperature within a predetermined annealing temperature range for said polymer for a predetermined period of time and thence having been cooled at a rate of less than about 20° C. per minute.
Claim 4
Dependent Claim
119 words
A component for a vehicle part, said component having an improved friction material disposed thereupon operative to enhance frictional engagement therewith, said friction material comprising a composite of from about 25% to about 75% by weight of a flurocarbon polymer and from about 75% to about 25% by weight ceramic fibers dispersed substantially uniformly therein, and said improvement characterized by said material having improved frictional engagement characteristics imparted thereto by reason of said polymer having controlled increased crystallinity arising from said material having been heated at a temperature within a predetermined annealing temperature range for said polymer for a predetermined period of time and thence having been cooled at a rate of less than about 20° C. per minute.
Claim 5
Dependent Claim
23 words
The component of claim 1 or 2 wherein said flurocarbon polymer comprises from about 40% to about 60% by weight of said material.
Claim 6
Dependent Claim
26 words
The component of claim 1 or 2 wherein said flurocarbon polymer is selected from the group consisting of polytetrafluoroethylene polymer, fluorinated ethylenepropylene copolymer, and perfluoroalkoxy copolymer.
Claim 7
Dependent Claim
39 words
The component of claim 1 wherein the flurocarbon polymer is polytetrafluoroethylene polymer and the sintering temperature range is from about 340° C. to about 440° C. and the time period is from about 1/2 hour to about 3 hours.
Claim 8
Dependent Claim
36 words
The component of claim 2 wherein the flurocarbon polymer is polytetrafluoroethylene polymer and the annealing temperature range is from about 300° C. to about 325° C. and the time period is at least about 5 hours.
Claim 9
Dependent Claim
19 words
The component of claim 1 or 2 wherein the cooling rate is less than about 5° C. per minute.
Claim 10
Dependent Claim
23 words
The component of claim 1 or 2 wherein the vehicle part is a twin shaft transmission and the component is a blocker ring.
References Cited (Backward Citations)
US3983979A
Cited
US4593802A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-08-09 | 1992-02-08 | 1992-08-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-08-09 | 1996-02-08 | 1996-08-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-08-09 | 2000-02-08 | 2000-08-09 | $7700.00 | Window Closed / Lapsed |