Method of forming closely sized openings
Assignee: Sandvik Rock Tools Inc
•
Filing: 1986-12-23
•
Granted: 1988-08-02
•
Expires: 2006-12-23
Abstract
Abstract A method of forming precision openings in hardened steel workpieces is disclosed. The method generally includes drilling nominal size openings in the workpiece while it is in a soft condition. Thereafter, sizing plugs formed from a material having a strength greater than that of the steel body during a predetermined range of temperatures are press-fitted in the openings. With the plugs in position, the body is heat treated to harden it. Subsequently, the plugs are removed and the resulting openings are found to be of an extremely uniform size without the wide variations present when hardening is performed without the sizing plugs.
Inventors
- 👤 George O. Keller
- 👤 Joseph J. Portugal
- 👤 Robert F. Kane
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 06:18
CPC Classifications
B; B23; B23P; B23P15/00; B23P15/28; B23P9/00; C; C21; C21D; C21D1/00; C21D1/68; E; E21; E21B; E21B10/00; E21B10/46; E21B10/56; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49826; Y10T29/49863; Y10T29/49865; Y10T29/49945
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
114 words
A method of forming at least one closely toleranced opening in a hardened steel body comprising the steps of: (a) providing a body formed of a steel capable of being hardened; (b) while said steel body is in a soft condition, forming an opening therein; (c) providing a plug formed from a material having a coefficient of thermal expansion less than said steel body, said plug being stronger than said steel body through a temperature range; (d) placing said plug in said opening; (e) heat treating said steel body through said temperature range with said plug in said opening to significantly increase the hardness of said steel body; and thereafter, (f) removing said plug.
Claim 2
Independent Claim
114 words
A method of forming at least one closely toleranced opening in a hardened steel body comprising the steps of: (a) providing a body formed of a steel capable of being hardened; (b) while said steel body is in a soft condition, forming an opening therein; (c) providing a plug formed from a material having a coefficient of thermal expansion less than said steel body, said plug being stronger than said steel body through a temperature range; (d) placing said plug in said opening; (e) heat treating said steel body through said temperature range with said plug in said opening to significantly increase the hardness of said steel body; and thereafter, (f) removing said plug.
Claim 3
Dependent Claim
15 words
The method as defined in claim 1 wherein said plug is press-fitted in said opening.
Claim 4
Dependent Claim
18 words
The method as defined in claim 1 wherein said steel body is tempered prior to removing said plug.
Claim 5
Dependent Claim
36 words
The method as defined in claim 3 wherein said plug is removed while said steel body is at a temperature above the temperature at which it was when said plug was originally fitted in said opening.
Claim 6
Dependent Claim
50 words
The method as defined in claim 1 wherein said steel body with the plug in said opening is heat treated by raising the temperature of said steel body and said plug to a level at or above the transformation range of said steel body and thereafter quenching said steel body.
Claim 7
Dependent Claim
16 words
The method as defined in claim 1 wherein said plug is formed from sintered tungsten carbide.
Claim 8
Dependent Claim
29 words
The method as defined in claim 1 wherein said plug is formed of a material which will not metallurgically react with said steel body during said heat treating step.
Claim 9
Independent Claim
153 words
The method of making a tool bit for rock drilling comprising the steps of: (a) providing a tool bit body formed from a steel capable of being heat treated to raise its hardness to a relatively high level, said bit body having a cutting face surface; (b) while said bit body is in a soft condition forming a plurality of openings extending into said cutting face surface; (c) placing a plug formed from a material different than the steel forming said bit body into each said openings with each plug having a coefficient of thermal expansion different than the bit body; (d) heat treating said bit body with said plugs therein to significantly raise the level of hardness of said bit body; and thereafter, (e) removing said plugs and press-fitting hard cutting inserts into said openings, each such insert being sized to have a cutting end portion extending outwardly of said cutting face.
Claim 10
Independent Claim
153 words
The method of making a tool bit for rock drilling comprising the steps of: (a) providing a tool bit body formed from a steel capable of being heat treated to raise its hardness to a relatively high level, said bit body having a cutting face surface; (b) while said bit body is in a soft condition forming a plurality of openings extending into said cutting face surface; (c) placing a plug formed from a material different than the steel forming said bit body into each said openings with each plug having a coefficient of thermal expansion different than the bit body; (d) heat treating said bit body with said plugs therein to significantly raise the level of hardness of said bit body; and thereafter, (e) removing said plugs and press-fitting hard cutting inserts into said openings, each such insert being sized to have a cutting end portion extending outwardly of said cutting face.
Claim 11
Dependent Claim
45 words
The method as defined in claim 8 wherein said plugs are inserted into said bit body at a first relatively low temperature and are removed from said body at a temperature above said first temperature but below the maximum temperature of said heat treating step.
Claim 12
Dependent Claim
28 words
The method as defined in claim 8 wherein said openings are cylindrical and wherein said plugs have a uniform diameter slightly greater than the diameters of said openings.
Claim 13
Dependent Claim
29 words
The method as defined in claim 10 wherein said plugs are formed from a material having a coefficient of thermal expansion lower than the steel forming said bit body.
Claim 14
Dependent Claim
28 words
The method as defined in claim 8 wherein said openings are cylindrical and wherein said plugs have a uniform diameter slightly less than the diameter of said openings.
Claim 15
Dependent Claim
29 words
The method as defined in claim 12 wherein said plugs are formed from a material having a coefficient of thermal expansion greater than the steel forming said bit body.
Claim 16
Dependent Claim
19 words
The method as defined in claim 8 wherein said plugs are a rigid material when inserted into said openings.
Claim 17
Dependent Claim
42 words
The method as defined in claim 8 wherein said plugs have a strength less than the steel forming the bit body at room temperature and a strength greater than the steel forming the bit body at an elevated bit body hardening temperature.
References Cited (Backward Citations)
US3190380A
Cited
JPS6056425A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-08-02 | 1992-02-01 | 1992-08-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-08-02 | 1996-02-01 | 1996-08-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-08-02 | 2000-02-01 | 2000-08-02 | $7700.00 | Window Closed / Lapsed |