Polyimide modified epoxy resins in aqueous emulsions for lamination and electrodeposition
Assignee: Westinghouse Electric Corp
•
Filing: 1985-10-09
•
Granted: 1988-07-26
•
Expires: 2005-10-09
Abstract
Abstract Disclosed in an emulsion having a discontinuous phase that consists of a water dispersed or water emulsified epoxy resin in water having at least two epoxide groups, a water soluble salt of an imide compound having at least one carboxyl group, and a crosslinking agent; the discontinuous phase has excess epoxide functionality. The continuous phase is water. A method of forming a coating on a conductive substrate is also disclosed. The substrate and an electrode are immersed into the emulsion and a direct current is applied between the substrate and the electrode to electrophoretically deposit a coating on the substrate of the epoxy resin, the imide compound, and the crosslinking agent. The substrate is removed from the emulsion and is heated to a temperature sufficient to cure the coating.
Inventors
- 👤 Timothy J. Fuller
- 👤 Joseph R. Marchetti
- 👤 Zal N. Sanjana
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 19:41
CPC Classifications
B; B32; B32B; B32B5/00; B32B5/22; B32B5/24; B32B5/26; B32B5/02; B32B5/024; C; C07; C07D; C07D209/00; C07D209/02; C07D209/44; C07D209/48; C08; C08G; C08G59/00; C08G59/18; C08G59/40; C08G59/62; C08G59/625; C08J; C08J3/00; C08J3/02; C08J3/03; C08J5/00; C08J5/24; C08J5/241; C08J5/244; C09; C09D; C09D5/00; C09D5/44; C09D5/4419; C09D5/443; C09D5/4434; B32B38/00; B32B2038/0052; B32B2038/0076; B32B2260/00; B32B2260/02; B32B2260/021; B32B2260/04; B32B2260/046; B32B2305/00; B32B2305/07; B32B2305/076; C08J2363/00
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
89 words
An emulsion made by the process of mixing: (1) an epoxy resin composition selected from the group consisting of water dispersed epoxy resin and water emulsified epoxy resin, where the epoxy resin has at least two epoxide groups and itself is not soluble in water; (2) a solution of a water soluble salt of a di or multifunctional imide compound, which imide compound contains at least one imide group and at least one free carboxyl group; and (3) when the imide compound is non-multifunctional, a water compatible crosslinking agent.
Claim 2
Dependent Claim
89 words
An emulsion made by the process of mixing: (1) an epoxy resin composition selected from the group consisting of water dispersed epoxy resin and water emulsified epoxy resin, where the epoxy resin has at least two epoxide groups and itself is not soluble in water; (2) a solution of a water soluble salt of a di or multifunctional imide compound, which imide compound contains at least one imide group and at least one free carboxyl group; and (3) when the imide compound is non-multifunctional, a water compatible crosslinking agent.
Claim 3
Dependent Claim
36 words
An emulsion according to claim 1 wherein the equivalent ratio of reactive epoxide functionality on the epoxy resin, to the functional groups on the imide compound that are reactive therewith, is about 1.5 to about 2.5.
Claim 4
Dependent Claim
12 words
An emulsion according to claim 1 wherein said imide compound is aromatic.
Claim 5
Dependent Claim
22 words
An emulsion according to claim 1 wherein said imide compound has an acid number of at least 60 mg KOH per gram.
Claim 6
Dependent Claim
29 words
An emulsion according to claim 1 wherein said imide compound is the reaction product of an anhydride, or a compound having vicinal carboxylic acid groups, and a primary amine.
Claim 7
Dependent Claim
51 words
An emulsion according to claim 5 wherein said anhydride or compound having vicinal carboxylic acid groups is selected from the group consisting of trimellitic anhydride, trimellitic acid, 3,3',4,4'-benzophenone tetracarboxylic dianhydride, pyromellitic dianhydride, tetrahydrofuran tetracarboxylic dianhydride, polyazelaic polyanhydride, 2,3,6-napthalene tricarboxylic-2,3-monoanhydride, maleinized vegetable oils, maleinized polybutadienes, and laser polymerized maleic anhydride oligomeric homopolymers.
Claim 8
Dependent Claim
30 words
An emulsion according to claim 5 wherein said primary amine is selected from the groups consisting of m-phenylene diamine, methylene diamine, methylene diamylamine, diamyl diphenyl ether, diaminobenzanilide, and p-amino phenol.
Claim 9
Dependent Claim
36 words
An emulsion according to claim 1 wherein said epoxy resin is selected from the group consisting of novolac epoxies, diglycidyl ethers of bisphenol A, hydantoin epoxies, high performance multifunctional epoxies, and diglycidyl ethers of bisphenol S.
Claim 10
Dependent Claim
27 words
An emulsion according to claim 1 wherein said crosslinking agent is selected from the group consisting of dicyandiamide, trimellitic acid, water soluble multi-carboxyl polyesters, and diphenolic acid.
Claim 11
Dependent Claim
136 words
An emulsion made by the process of mixing: (1) an aromatic epoxy resin composition selected from the group consisting of water dispersed epoxy resin and water emulsified epoxy resin, where the epoxy resin has at least two epoxide groups; (2) a solution of a water soluble tertiary amine salt of an aromatic imide having at least one imide group, and at least two groups that are reactive with said epoxide groups, at least one of which is a carboxyl group, where the equivalent ratio of reactive epoxide functionality on said epoxy resin to said functional groups on said aromatic imide that are reactive therewith is about 1.5 to about 2.5; and (3) a water compatible crosslinking agent, said emulsion having a solids content of about 5% to about 60% by weight, based on total emulsion weight.
Claim 12
Dependent Claim
136 words
An emulsion made by the process of mixing: (1) an aromatic epoxy resin composition selected from the group consisting of water dispersed epoxy resin and water emulsified epoxy resin, where the epoxy resin has at least two epoxide groups; (2) a solution of a water soluble tertiary amine salt of an aromatic imide having at least one imide group, and at least two groups that are reactive with said epoxide groups, at least one of which is a carboxyl group, where the equivalent ratio of reactive epoxide functionality on said epoxy resin to said functional groups on said aromatic imide that are reactive therewith is about 1.5 to about 2.5; and (3) a water compatible crosslinking agent, said emulsion having a solids content of about 5% to about 60% by weight, based on total emulsion weight.
Claim 13
Dependent Claim
44 words
An emulsion according to claim 10 wherein said epoxy resin includes about 1 to about 15% by weight, based on epoxy resin weight, of an emulsifying agent, and up to about 15% by weight, based on epoxy resin weight, of a water-dispersible organic solvent.
References Cited (Backward Citations)
JPS4867394A
Cited
JPS4938119A
Cited
JPS4944957A
Cited
JPS4997898A
Cited
US4130469A
Cited
US4384946A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-07-26 | 1992-01-25 | 1992-07-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-07-26 | 1996-01-25 | 1996-07-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-07-26 | 2000-01-25 | 2000-07-26 | $7700.00 | Window Closed / Lapsed |