Flexible carbon material
Assignee: Kureha Corp
•
Filing: 1986-08-20
•
Granted: 1988-07-26
•
Expires: 2006-08-20
Abstract
Abstract A flexible carbon material is produced by carbonizing a composite material comprising carbon fibers having an average length of 6 to 50 mm and a binding agent. Carbon lumps are derived from the binding agent and are dispersed in a matrix of the carbon fibers so as to restrain a plurality of the carbon fibers while yet permitting relative slippage to occur as between the carbon fibers and carbon lumps such that the carbon fiber material exhibits a flexibility ratio D/d of not greater than 200 (where D is the diameter of curvature of the carbon material, when bent, just before breakage, and d is the thickness of the carbon material). The carbon fibers and lumps are preferrably present in an amount of from 5 to 50%, and 5 to 70% by volume, respectively, based upon the total volume of the carbon material.
Inventors
- 👤 Hiroyuki Fukuda
- 👤 Yukihiro Shibuya
- 👤 Kiyomi Ohuchi
- 👤 Masumi Sagi
- 👤 Naohiro Murayama
- 👤 Masatomo Shigeta
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 07:43
CPC Classifications
D; D21; D21H; D21H25/00; D21H25/04; D21H25/06; C; C04; C04B; C04B35/00; C04B35/71; C04B35/78; C04B35/80; C04B35/83; D21H13/00; D21H13/36; D21H13/46; D21H13/50; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24479; Y10T428/24612; Y10T428/249921; Y10T428/249924; Y10T428/24994; Y10T428/30; Y10T442/00; Y10T442/20; Y10T442/2418; Y10T442/2426; Y10T442/2475; Y10T442/2631; Y10T442/60; Y10T442/699
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
178 words
A flexible carbon material produced by carbonizing a composite material comprising carbon fibers having an average length of 6 to 50 mm which have been treated at a temperature of not less than 1500° C. and a binding agent, wherein carbon lumps derived from said binding agent are dispersed in a matrix of said carbon fibers and restrain a plurality of said carbon fibers while yet permitting relative slippage to occur as between said carbon fibers and said carbon lumps, so as to provide a flexibility ratio D/d of said carbon material of not more than 200, where D is the diameter of said flexible carbon material, when bent, just prior to breakage, and d is the thickness of said carbon material, and wherein said carbon material exhibits tensile strength, electrical resistance, and apparent density values, respectively, of not less than 0.05 kgf/mm 2 , not more than 900 mΩ·cm and 0.2 to 1.3 g/cc, and wherein not less than 80% by volume of pores in said flexible carbon material has a diameter of 10 to 400 μm.
Claim 2
Dependent Claim
178 words
A flexible carbon material produced by carbonizing a composite material comprising carbon fibers having an average length of 6 to 50 mm which have been treated at a temperature of not less than 1500° C. and a binding agent, wherein carbon lumps derived from said binding agent are dispersed in a matrix of said carbon fibers and restrain a plurality of said carbon fibers while yet permitting relative slippage to occur as between said carbon fibers and said carbon lumps, so as to provide a flexibility ratio D/d of said carbon material of not more than 200, where D is the diameter of said flexible carbon material, when bent, just prior to breakage, and d is the thickness of said carbon material, and wherein said carbon material exhibits tensile strength, electrical resistance, and apparent density values, respectively, of not less than 0.05 kgf/mm 2 , not more than 900 mΩ·cm and 0.2 to 1.3 g/cc, and wherein not less than 80% by volume of pores in said flexible carbon material has a diameter of 10 to 400 μm.
Claim 3
Dependent Claim
20 words
A flexible carbon material according to claim 1, wherein the diameter of said carbon fibers is 4 to 25 μm.
Claim 4
Dependent Claim
29 words
A flexible carbon material according to claim 1, wherein said carbon fibers are present in an amount of 5 to 50% of the total volume of said carbon material.
Claim 5
Dependent Claim
23 words
A flexible carbon material according to claim 3, wherein said carbon fibers are present in an amount of 10 to 40% by volume.
Claim 6
Dependent Claim
63 words
A flexible carbon material according to claim 1, wherein when in the form of said lumps derived from said binding agent is regarded as a sphere, said lumps have a diameter of 2 to 200 times the diameter of said carbon fibers, and wherein said lumps are present in an amount of 5 to 70% of the total volume of said carbon material.
Claim 7
Dependent Claim
40 words
A flexible carbon material according to claim 5, wherein the diameter of said lumps is 3 to 100 times the diameter of said carbon fibers, and wherein the lumps are present in an amount of 10 to 60% by volume.
Claim 8
Dependent Claim
181 words
A flexible carbon sheet comprised of (a) a matrix of carbon fibers having a mean length of not less than 6 mm and not greater than 50 mm and a diameter of between 4 to 25 μm, and (b) an organic binding agent having a carbonizing yield of not less than 10% dispersed throughout said matrix in the form of carbonized lumps having diameters of between 2 to 200 times the diameter of said carbon fibers, wherein said lumps retain said carbon fibers in said matrix yet are physically and chemically unattached thereto so as to allow relative slippage to occur as between said lumps and said carbon fibers such that said carbon sheet exhibits a flexibility ratio D/d of not greater than 200, wherein D is the diameter of curvature of said sheet, when bent, just before breakage, and d is the thickness of said carbon sheet, and wherein said carbon fibers and lumps are present in an amount of from 5 to 50%, and 5 to 70% by volume, respectively, based upon the total volume of said carbon sheet.
Claim 9
Dependent Claim
181 words
A flexible carbon sheet comprised of (a) a matrix of carbon fibers having a mean length of not less than 6 mm and not greater than 50 mm and a diameter of between 4 to 25 μm, and (b) an organic binding agent having a carbonizing yield of not less than 10% dispersed throughout said matrix in the form of carbonized lumps having diameters of between 2 to 200 times the diameter of said carbon fibers, wherein said lumps retain said carbon fibers in said matrix yet are physically and chemically unattached thereto so as to allow relative slippage to occur as between said lumps and said carbon fibers such that said carbon sheet exhibits a flexibility ratio D/d of not greater than 200, wherein D is the diameter of curvature of said sheet, when bent, just before breakage, and d is the thickness of said carbon sheet, and wherein said carbon fibers and lumps are present in an amount of from 5 to 50%, and 5 to 70% by volume, respectively, based upon the total volume of said carbon sheet.
References Cited (Backward Citations)
US3998689A
Cited
US4064207A
Cited
US4115528A
Cited
WO1980002818A1
Cited
US4365008A
Cited
US4426340A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-07-26 | 1992-01-25 | 1992-07-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-07-26 | 1996-01-25 | 1996-07-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-07-26 | 2000-01-25 | 2000-07-26 | $7700.00 | Window Closed / Lapsed |