Process for shrink-fit locking a cylindrical ceramic part into a flange made of a ferrous material, and ceramic-metal composite bodies
Assignee: METOXIT AG A CORP OF SWITZERLAND
•
Filing: 1986-04-07
•
Granted: 1988-07-26
•
Expires: 2006-04-07
Abstract
Abstract The tensile loading of a ceramic-metal joint, made by shrink-fit locking a cylindrical ceramic component into a flange of ferrous material in the axial direction of the ceramic component can be improved by undersizing the diameter D of the bore of the flange by 13-27 mu m making it, at room temperature, this much smaller than the diameter d of that part of the ceramic component to be attached to the flange by shrink-fit locking, by preparing the cylindrical surface of the said part of the ceramic component with a surface roughness Ra of 0.05-0.2 mu m and the surface of the bore in the flange with a roughness Ra of 0.4-0.8 rho m, and by heating the flange, before fitting it to the ceramic part, to a temperature such that, after fitting together the ceramic component and the flange, the resultant stresses produced on cooling the assembly to room temperature are below the yield strength Rpo.2 of the ferrous material, and the said temperature of heating is below the Wöhler temperature of the ceramic material.
Inventors
- 👤 Wolfhart Rieger
- 👤 Jakob Widrig
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 20:54
CPC Classifications
B; B23; B23P; B23P11/00; B23P11/02; B23P11/025; F; F16; F16B; F16B4/00; F16B4/006; F16B2200/00; F16B2200/85; Y; Y10; Y10S; Y10S29/00; Y10S29/035; Y10T; Y10T29/00; Y10T29/49; Y10T29/49229; Y10T29/49249; Y10T29/49256; Y10T29/49826; Y10T29/49863; Y10T29/49865; Y10T403/00; Y10T403/48
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
134 words
A process for shrink-fit locking a cylindrical ceramic component into a flange component of ferrous material comprising: providing a flange component having a bore of diameter D at substantially room temperature; roughening the inside surface of said bore; providing a cylindrical ceramic component having an outside diameter d at substantially room temperature wherein d is greater than D; roughening the outside surface of a portion of said cylindrical ceramic component; heating said flange component to a temperature such that diameter D is greater than or equal to diameter d; placing said roughened portion of said cylindrical ceramic component within said bore having said roughened inside surface of said flange component so as to form an assembly; and cooling said assembly to room temperature such that said flange component shrink-fits about said cylindrical ceramic component.
Claim 2
Dependent Claim
134 words
A process for shrink-fit locking a cylindrical ceramic component into a flange component of ferrous material comprising: providing a flange component having a bore of diameter D at substantially room temperature; roughening the inside surface of said bore; providing a cylindrical ceramic component having an outside diameter d at substantially room temperature wherein d is greater than D; roughening the outside surface of a portion of said cylindrical ceramic component; heating said flange component to a temperature such that diameter D is greater than or equal to diameter d; placing said roughened portion of said cylindrical ceramic component within said bore having said roughened inside surface of said flange component so as to form an assembly; and cooling said assembly to room temperature such that said flange component shrink-fits about said cylindrical ceramic component.
Claim 3
Dependent Claim
29 words
A process according to claim 1 wherein said bore roughening step includes roughening the inside surface of said bore to a roughness of between Ra 0.4 to 0.8 μm.
Claim 4
Dependent Claim
36 words
A process according to claim 2 wherein said outside surface portion roughening step includes roughening the outside surface of said portion of said cylindrical ceramic component to a roughness of between Ra 0.05 to 0.2 μm.
Claim 5
Dependent Claim
25 words
A process according to claim 1 including providing the diameter D at room temperature of between d minus 27 μm and d minus 13 μm.
Claim 6
Dependent Claim
9 words
An assembly produced by the process of claim 1.
Claim 7
Dependent Claim
14 words
An assembly according to claim 5 wherein said flange component is made of steel.
Claim 8
Dependent Claim
19 words
A process according to claim 1 including providing the diameter D at room temperature of d minus 20 μm.
Claim 9
Dependent Claim
108 words
A process for shrink-fit locking a cylindrical ceramic component into a flange component of ferrous material comprising: providing a flange component having a bore of diameter D at substantially room temperature; providing a cylindrical ceramic component having an outside diameter d at substantially room temperature wherein d is greater than D; heating said flange component to a temperature of less than the Wohler temperature of the cylindrical ceramic component; placing a portion of said cylindrical ceramic component within said bore of said flange component so as to form an assembly; and cooling said assembly to room temperature such that said flange component shrink-fits about said cylindrical ceramic component.
Claim 10
Dependent Claim
108 words
A process for shrink-fit locking a cylindrical ceramic component into a flange component of ferrous material comprising: providing a flange component having a bore of diameter D at substantially room temperature; providing a cylindrical ceramic component having an outside diameter d at substantially room temperature wherein d is greater than D; heating said flange component to a temperature of less than the Wohler temperature of the cylindrical ceramic component; placing a portion of said cylindrical ceramic component within said bore of said flange component so as to form an assembly; and cooling said assembly to room temperature such that said flange component shrink-fits about said cylindrical ceramic component.
Claim 11
Dependent Claim
145 words
An assembly which includes: a flange component made of steel; said flange component having a bore of diameter D at substantially room temperature and a relief notch; and said assembly being produced by a process for shrink-fit locking a cylindrical ceramic component into said flange component which comprises (a) providing said flange component having said bore of diameter D at substantially room temperature; (b) providing a cylindrical ceramic component having an outside diameter d at substantially room temperature wherein d is greater than D; (c) heating said flange component to a temperature such that diameter D is greater than or equal to diameter d; (d) placing a portion of said cylindrical ceramic component within said bore of said flange component so as to form an assembly; and (e) cooling said assembly to room temperature such that said flange component shrink-fits about said cylindrical ceramic component.
Claim 12
Dependent Claim
145 words
An assembly which includes: a flange component made of steel; said flange component having a bore of diameter D at substantially room temperature and a relief notch; and said assembly being produced by a process for shrink-fit locking a cylindrical ceramic component into said flange component which comprises (a) providing said flange component having said bore of diameter D at substantially room temperature; (b) providing a cylindrical ceramic component having an outside diameter d at substantially room temperature wherein d is greater than D; (c) heating said flange component to a temperature such that diameter D is greater than or equal to diameter d; (d) placing a portion of said cylindrical ceramic component within said bore of said flange component so as to form an assembly; and (e) cooling said assembly to room temperature such that said flange component shrink-fits about said cylindrical ceramic component.
Claim 13
Dependent Claim
18 words
An assembly according to claim 9 wherein said ceramic component is made at least in part of corundum.
References Cited (Backward Citations)
DE372153C
Cited
DE2734747A1
Cited
US4297779A
Cited
US4531269A
Cited
US4573250A
Cited
US4624484A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-07-26 | 1992-01-25 | 1992-07-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-07-26 | 1996-01-25 | 1996-07-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-07-26 | 2000-01-25 | 2000-07-26 | $7700.00 | Window Closed / Lapsed |