Assignee: Dainippon Screen Manufacturing Co Ltd
•
Filing: 1987-04-06
•
Granted: 1988-07-05
•
Expires: 2007-04-06
Abstract
Abstract A photoetching method for processing a thin metal sheet to produce apertured shadow masks. The disclosed method utilizes a supporting layer for supporting a metal sheet. A photoresist layer is formed on the metal sheet for defining pattern images. An etching solution is supplied to metal sheet surfaces exposed through voids of the photoresist layer defining the pattern images to etch the metal surfaces. Then the photoresist layer is removed from the metal sheet, and the metal sheet is removed from the supporting sheet. The resulting metal sheet constitutes a shadow mask having a multiplicity of apertures. Productivity may be doubled by applying two metal sheets to opposite faces of the supporting sheet, respectively, and processing both metal sheets simultaneously.
Inventors
- 👤 Toshio Yamamoto
- 👤 Masaru Kawasaki
- 👤 Takefumi Kandori
- 👤 Ryoichi Ando
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 05:50
CPC Classifications
C; C23; C23F; C23F1/00; H; H01; H01J; H01J9/00; H01J9/02; H01J9/14; H01J9/142; C23F1/02; C23F1/10; C23F1/14; C23F1/16; C23F1/28; H05; H05K; H05K3/00; H05K3/02; H05K3/06; H05K3/061; H05K3/064; H05K3/10; H05K3/20; H05K3/202
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
126 words
A method of patterning a thin metal sheet, comprising the steps of: providing a thin metal sheet of less than about 0.5 mm thickness; fixedly applying a supporting sheet to one surface of said metal sheet; applying a photoresist material to the other surface of said metal sheet to form a photoresist layer therein; exposing desired pattern images onto said photoresist layer; supplying a developing solution to said photoresist layer to develop said pattern images on said photoresist layer and thereby bare a metal sheet surface having desired pattern images; supplying an etching solution to said metal sheet surface to etch said metal sheet surface thus bared; removing said photoresist layer from said metal sheet; and removing said supporting sheet from said metal sheet by peeling.
Claim 2
Independent Claim
126 words
A method of patterning a thin metal sheet, comprising the steps of: providing a thin metal sheet of less than about 0.5 mm thickness; fixedly applying a supporting sheet to one surface of said metal sheet; applying a photoresist material to the other surface of said metal sheet to form a photoresist layer therein; exposing desired pattern images onto said photoresist layer; supplying a developing solution to said photoresist layer to develop said pattern images on said photoresist layer and thereby bare a metal sheet surface having desired pattern images; supplying an etching solution to said metal sheet surface to etch said metal sheet surface thus bared; removing said photoresist layer from said metal sheet; and removing said supporting sheet from said metal sheet by peeling.
Claim 3
Independent Claim
117 words
A method fo patterning thin metal sheets, comprising the steps of: providing a pair of thin metal sheets each of less than about 0.05 mm thickness; fixedly applying said metal sheets to respective of opposite faces of a supporting sheet; applying a photoresist material to said metal sheets to form photoresist layers thereon, respectively; exposing desired pattern images onto said photoresist layers; supplying a developing solution to said photoresist layers to develop said pattern images on said photoresist layer and thereby bare metal sheet surfaces having desired pattern images; supplying an etching solution to said metal sheet surface to etch said metal sheet surface thus bared; and removing said metal sheets from said supporting sheet by peeling.
Claim 4
Independent Claim
117 words
A method fo patterning thin metal sheets, comprising the steps of: providing a pair of thin metal sheets each of less than about 0.05 mm thickness; fixedly applying said metal sheets to respective of opposite faces of a supporting sheet; applying a photoresist material to said metal sheets to form photoresist layers thereon, respectively; exposing desired pattern images onto said photoresist layers; supplying a developing solution to said photoresist layers to develop said pattern images on said photoresist layer and thereby bare metal sheet surfaces having desired pattern images; supplying an etching solution to said metal sheet surface to etch said metal sheet surface thus bared; and removing said metal sheets from said supporting sheet by peeling.
Claim 5
Dependent Claim
15 words
A method according to claim 1, wherein the resulting metal sheet constitutes a shadow mask.
Claim 6
Dependent Claim
19 words
A method according to claim 2, wherein the resulting pair of metal sheets constitute a pair of shadow masks.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-07-05 | 1992-01-04 | 1992-07-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-07-05 | 1996-01-04 | 1996-07-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-07-05 | 2000-01-04 | 2000-07-05 | $7700.00 | Window Closed / Lapsed |