Curable organosiloxane compositions
Assignee: Dow Silicones Corp
•
Filing: 1987-08-25
•
Granted: 1988-06-28
•
Expires: 2007-08-25
Abstract
Abstract The tear strength of cured organosiloxane elastomers can be increased without adversely affecting other physical properties if the composition used to prepare the elastomer is curable by a platinum-catalyzed hydrosilation reaction and contains a mixture of two liquid diorganovinylsiloxy terminated polydiorganosiloxanes, one of which constitutes from 70 to 95 percent by weight of said mixture and contains vinyl or other ethylenically unsaturated hydrocarbon radicals only at the terminal positions. The second polydiorganosiloxane contains both terminal vinyl radicals and from 1 to 5 mole percent of vinyl radicals on non-terminal repeating units.
Inventors
- 👤 Jary D. Jensen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 18:06
CPC Classifications
C; C08; C08L; C08L83/00; C08L83/04; C08G; C08G77/00; C08G77/04; C08G77/12; C08G77/20; C08G77/22; C08G77/24; C08G77/70
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
198 words
A curable organosiloxane composition comprising the product obtained by mixing to homogeniety A. from 70 to 95 weight percent, based on the total weight of (A) and (B), of a first diorganovinylsiloxy terminated polydiorganosiloxane exhibiting a viscosity of from 20 to 200 Pa.s at 25° C. and containing essentially no ethylenically unsaturated hydrocarbon radicals bonded to non-terminal silicon atoms, B. from 5 to 30 weight percent, based on the total weight of (A) and (B), of a second diorganovinylsiloxy terminated polydiorganosiloxane that is miscible with said first polydiorganosiloxane and exhibits a viscosity of from 0.1 to 200 Pa.s at 25° C., where from 1 to 5 percent of the non-terminal repeating units of said second diorganovinylsiloxy-terminated polydiorganosiloxane contain a vinyl radical C. an amount sufficient to cure said composition of an organohydrogensiloxane that is miscible with (A) and (B), and contains an average of more than two silicon bonded hydrogen atoms per molecule, D. a platinum hydrosilation catalyst in an amount sufficient to promote curing of said composition at a temperature of from ambient to 250° C., and E. from 10 to 60 weight percent, based on the weight of said composition, of a treated reinforcing silica filler.
Claim 2
Dependent Claim
198 words
A curable organosiloxane composition comprising the product obtained by mixing to homogeniety A. from 70 to 95 weight percent, based on the total weight of (A) and (B), of a first diorganovinylsiloxy terminated polydiorganosiloxane exhibiting a viscosity of from 20 to 200 Pa.s at 25° C. and containing essentially no ethylenically unsaturated hydrocarbon radicals bonded to non-terminal silicon atoms, B. from 5 to 30 weight percent, based on the total weight of (A) and (B), of a second diorganovinylsiloxy terminated polydiorganosiloxane that is miscible with said first polydiorganosiloxane and exhibits a viscosity of from 0.1 to 200 Pa.s at 25° C., where from 1 to 5 percent of the non-terminal repeating units of said second diorganovinylsiloxy-terminated polydiorganosiloxane contain a vinyl radical C. an amount sufficient to cure said composition of an organohydrogensiloxane that is miscible with (A) and (B), and contains an average of more than two silicon bonded hydrogen atoms per molecule, D. a platinum hydrosilation catalyst in an amount sufficient to promote curing of said composition at a temperature of from ambient to 250° C., and E. from 10 to 60 weight percent, based on the weight of said composition, of a treated reinforcing silica filler.
Claim 3
Dependent Claim
162 words
A composition according to claim 1 where said first diorganovinylsiloxy terminated polydiorganosiloxane (A) is represented by the average general formula ViR.sub.2 SiO(R'.sub.2 SiO).sub.x SiR.sub.2 Vi where Vi represents a vinyl radical, R and R' are individually monovalent hydrocarbon radicals or substituted monovalent hydrocarbon radicals, and contain from 1 to 20 carbon atoms R and R' are substantially free of ethylenic unsaturation, and x represents a degree of polymerization equivalent to a viscosity of from 20 to 200 Pa.s at 25° C. and said second diorganovinylsiloxy terminated polydiorganosiloxane is represented by the average general formula ViR".sub.2 SiO(R"'.sub.2 SiO).sub.y (R"'ViSiO).sub.z SiR".sub.2 Vi where Vi represents a vinyl radical and R" and R"' are selected from the same group of monovalent hydrocarbon radicals and substituted monovalent substituted hydrocarbon radicals as R and R', the degree of polymerization represented by the sum of y and z is equivalent to a viscosity of from 0.1 to 200 Pa.s, and the ratio z/(y+z) is from 0.01 to 0.05.
Claim 4
Dependent Claim
37 words
A composition according to claim 2 where at least 50 percent of the radicals represented by R, R', R" and R"' are methyl and any remaining radicals are selected from the group consisting of phenyl and 3,3,3-trifluoropropyl.
Claim 5
Dependent Claim
75 words
A composition according to claim 3 where R, R', R" and R"' are methyl, the viscosity of said first polydiorganosiloxane (A) is from 40 to 70 Pa.s at 25° C., the viscosity of said second polydiorganosiloxane (B) is from 0.1 to 20 Pa.s at 25° C., said first polydiorganosiloxane constitutes from 85 to 95 percent of the combined weight of said first and second polydiorganosiloxanes, and said organohydrogensiloxane (C) is a trimethylsiloxy terminated dimethylsiloxane/methylhydrogensiloxane copolymer.
Claim 6
Dependent Claim
55 words
A composition according to claim 4 where the molar ratio of the silicon bonded hydrogen atoms present in said organohydrogensiloxane and all of the vinyl or other ethylenically unsaturated hydrocarbon radicals present in said composition is from 1 to 2 and said reinforcing filler is treated with an anti-creping agent during preparation of said composition.
Claim 7
Dependent Claim
23 words
A composition according to claim 1 where said composition is extrudable and exhibits a viscosity of less than 10 Pa.s at 25° C.
References Cited (Backward Citations)
US3671480A
Cited
GB1269007A
Cited
US3884866A
Cited
US4057596A
Cited
US4162243A
Cited
US4539357A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-06-28 | 1991-12-28 | 1992-06-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-06-28 | 1995-12-28 | 1996-06-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-06-28 | 1999-12-28 | 2000-06-28 | $7700.00 | Window Closed / Lapsed |