Absorbent, protective nonwoven fabric
Assignee: Kimberly Clark Corp
•
Filing: 1986-05-01
•
Granted: 1988-06-28
•
Expires: 2006-05-01
Abstract
Abstract There is disclosed a multi-layered absorbent, protective nonwoven web which has one or more center layers of melt-blown polypropylene microfibers which are naturally hydrophobic. The center layers are sandwiched between one or more melt-blown surface layers on each side which surface layers are composed of melt-blown polypropylene microfibers which have been rendered hydrophilic by addition of a nonionic surfactant during formation of the surface layer microfibers.
Inventors
- 👤 Ronald F. Cook
- 👤 Monica C. Cunningham
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 16:54
CPC Classifications
D; D04; D04H; D04H1/00; D04H1/70; D04H1/72; D04H1/724; D04H1/40; D04H1/54; D04H1/56; D04H1/42; D04H1/4282; D04H1/4291; Y; Y10; Y10S; Y10S428/00; Y10S428/903; Y10S428/913; Y10T; Y10T442/00; Y10T442/60; Y10T442/603; Y10T442/607; Y10T442/608; Y10T442/614; Y10T442/626; Y10T442/659; Y10T442/671; Y10T442/68
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
70 words
An integral nonwoven, melt-blown web comprising one or more surface layers and one or more center layers bonded to each other wherein the center layers consist of discontinuous, thermoplastic fibers formed by melt-blowing, which center layer fibers are hydrophobic and wherein the surface layers consist of discontinuous, thermoplastic fibers formed by melt-blowing, which surface layer fibers are rendered hydrophilic during formation by introducing a surfactant onto the surface layer fibers.
Claim 2
Dependent Claim
70 words
An integral nonwoven, melt-blown web comprising one or more surface layers and one or more center layers bonded to each other wherein the center layers consist of discontinuous, thermoplastic fibers formed by melt-blowing, which center layer fibers are hydrophobic and wherein the surface layers consist of discontinuous, thermoplastic fibers formed by melt-blowing, which surface layer fibers are rendered hydrophilic during formation by introducing a surfactant onto the surface layer fibers.
Claim 3
Dependent Claim
20 words
The web of claim 1, wherein the center layer fibers and surface layer fibers are produced from a single polymer.
Claim 4
Dependent Claim
10 words
The web of claim 2, wherein the polymer is polypropylene.
Claim 5
Dependent Claim
19 words
The web of claim 2, wherein the fibers on average range between 1.5 microns and 7.5 microns in diameter.
Claim 6
Dependent Claim
47 words
The web of claim 2, wherein the web comprises two surface layers on each side of the web and four center layers and wherein the web has a total basis weight between 0.75 and 1.5 ounces per square yard and all layers have essentially equal basis weights.
Claim 7
Independent Claim
153 words
A method of producing a nonwoven layered web having one or more wettable surface layers and one or more nonwettable center layers, the method comprising: (a) serially depositing by means of melt-blowing one or more first surface layers of discontinuous, thermoplastic fibers onto a collection surface, wherein a surfactant is added to the first surface layer fibers as the first surface layer fibers are formed to render the surface layers hydrophilic; (b) serially depositing by means of melt-blowing one or more center layers of discontinuous, thermoplastic fibers on top of the first surface layers, wherein the center layer fibers are naturally hydrophobic; and (c) serially depositing by means of melt-blowing one or more second surface layers of discontinuous, thermoplastic fibers on top of the first center layers, wherein a surfactant is added to the second surface layer fibers as the second surface layer fibers are formed to render the second surface layers hydrophilic.
Claim 8
Independent Claim
153 words
A method of producing a nonwoven layered web having one or more wettable surface layers and one or more nonwettable center layers, the method comprising: (a) serially depositing by means of melt-blowing one or more first surface layers of discontinuous, thermoplastic fibers onto a collection surface, wherein a surfactant is added to the first surface layer fibers as the first surface layer fibers are formed to render the surface layers hydrophilic; (b) serially depositing by means of melt-blowing one or more center layers of discontinuous, thermoplastic fibers on top of the first surface layers, wherein the center layer fibers are naturally hydrophobic; and (c) serially depositing by means of melt-blowing one or more second surface layers of discontinuous, thermoplastic fibers on top of the first center layers, wherein a surfactant is added to the second surface layer fibers as the second surface layer fibers are formed to render the second surface layers hydrophilic.
Claim 9
Dependent Claim
45 words
The method of claim 6, wherein the surfactant is a nonionic surfactant and is added to the first and second surface layer fibers by spraying the surfactant onto the fibers after formation and before they are deposited on the collection surface and center layers respectively.
Claim 10
Dependent Claim
25 words
The method of claim 7, wherein a 1% solution of the surfactant is added at a rate of between 0.9 and 0.35 gallons per minute.
Claim 11
Dependent Claim
25 words
The method of claim 8, wherein the first and second surface layer fibers and the center layer fibers are all produced from a single polymer.
Claim 12
Dependent Claim
10 words
The method of claim 9, wherein the polymer is polypropylene.
Claim 13
Dependent Claim
127 words
The method of claim 10, wherein the first and second surface layer fibers and the center layers are formed by means of a melt-blowing process having the following process parameters: (a) a peroxide prodegradant is added to the polypropylene resin. (b) through-put is between 2.5 and 5.5 pih; (c) during extrusion through an extruder barrel divided into temperature zones from input to output, temperatures of the polymer is maintained below its melting point for several zones to facilitate mixing of the polymer and peroxide prodegradant in the barrel; (d) pressure in the extruder barrel is maintained above 500 psi to facilitate mixing of the polymer and peroxide prodegradant; (e) primary air flow is between 1600 and 2000 scfm; (f) forming distance is between 10 and 14 inches.
Claim 14
Dependent Claim
10 words
A nonwoven web formed by the process of claim 6.
References Cited (Backward Citations)
US3916447A
Cited
US4041203A
Cited
US4075382A
Cited
US4165352A
Cited
US4307143A
Cited
US4196245A
Cited
US4328279A
Cited
US4468428A
Cited
US4379192A
Cited
US4426417A
Cited
US4508113A
Cited
US4555811A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-06-28 | 1991-12-28 | 1992-06-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-06-28 | 1995-12-28 | 1996-06-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-06-28 | 1999-12-28 | 2000-06-28 | $7700.00 | Window Closed / Lapsed |