US4752626A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of making low compression set urethane foams
Assignee: Motors Liquidation Co
•
Filing: 1987-08-27
•
Granted: 1988-06-21
•
Expires: 2007-08-27
Abstract
Abstract This invention generally relates to a high resilience urethane foam (HR foam) having low compression set at a wide range of isocyanate index for use in small void filling in integrated foam parts. The small voids formed in the molding process of integrated foam parts can be filled without penetration of foaming liquids into existing foam cells. In addition, resulting foams have very low compression set values at a wide range of isocyanate index. The foaming system of the present invention is composed of two components, i.e., thixotropic polyisocyanate component and thixotropic polyol component. Their thixotropicity is obtained by adding benzal sorbitol into respective components. The polyisocyanate is selected from organic polyisocyanates and the polyol component is prepared by mixing a polyol blend composed of a polyolefinic polyol and a polyoxyalkylene polyol in a weight ratio between 95/5 to 50/50, a blowing agent, a surfactant and a catalyst.
Inventors
- 👤 Robert J. Hoye
- 👤 Vabilisetti S. Murty
- 👤 Kaneyoshi Ashida
- 👤 Chin-Jui Chang
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 07:39
CPC Classifications
B; B29; B29C; B29C73/00; B29C73/02; C; C08; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/40; C08G18/4009; C08G18/4063; C08G18/67; C08G18/69; C08G18/698; C08G18/70; B29K; B29K2075/00; B29K2105/00; B29K2105/04; B29K2105/045; C08G2110/00; C08G2110/0008; C08G2110/0041; C08G2110/005; C08G2110/0058
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
92 words
A method of making high resilience urethane foams having superior compression set properties by intimately mixing the component of an organic isocyanate having at least two isocyanate groups with a polyol blend consisting of (a) a polyolefinic polyol having at least two hydroxyl groups selected from the group consisting of polybutadiene, polyisoprene and hydrogenated products thereof, and (b) a polyether polyol in a weight ratio of a/b being from 95/5 to 50/50, in the presence of a blowing agent, a surfactant, a urethane catalyst and optionally a benzal sorbitol and other additives.
Claim 2
Independent Claim
92 words
A method of making high resilience urethane foams having superior compression set properties by intimately mixing the component of an organic isocyanate having at least two isocyanate groups with a polyol blend consisting of (a) a polyolefinic polyol having at least two hydroxyl groups selected from the group consisting of polybutadiene, polyisoprene and hydrogenated products thereof, and (b) a polyether polyol in a weight ratio of a/b being from 95/5 to 50/50, in the presence of a blowing agent, a surfactant, a urethane catalyst and optionally a benzal sorbitol and other additives.
Claim 3
Independent Claim
106 words
A method of making high resilience urethane foams having superior compression set properties by intimately mixing the component of an organic isocyanate having at least two isocyanate groups, with a polyol blend consisting of (a) at least one polyolefinic polyol having at least two hydroxyl groups and a molecular weight of about 1,000-5,000 selected from the group consisting of polybutadiene, polyisoprene and hydrogenated products thereof, and (b) at least one polyether polyol having a molecular weight of about 3,000-6,000 in a weight ratio of a/b being from 95/5 to 50/50, in the presence of a blowing agent, a surfactant, a urethane catalyst and optionally an additive.
Claim 4
Independent Claim
106 words
A method of making high resilience urethane foams having superior compression set properties by intimately mixing the component of an organic isocyanate having at least two isocyanate groups, with a polyol blend consisting of (a) at least one polyolefinic polyol having at least two hydroxyl groups and a molecular weight of about 1,000-5,000 selected from the group consisting of polybutadiene, polyisoprene and hydrogenated products thereof, and (b) at least one polyether polyol having a molecular weight of about 3,000-6,000 in a weight ratio of a/b being from 95/5 to 50/50, in the presence of a blowing agent, a surfactant, a urethane catalyst and optionally an additive.
Claim 5
Dependent Claim
41 words
A method of making high resilience urethane foams according to claim 1, wherein a benzal sorbitol is added to both the polyisocyanate component and the polyol component, respectively, as a thixotropic agent in an amount of 0.1 to 5.0 weight percent.
Claim 6
Dependent Claim
41 words
A method of making high resilience urethane foams according to claim 1, wherein a dibenzal sorbitol is added to both the polyisocyanate component and the polyol component, respectively, as a thixotropic agent in an amount of 0.1 to 5.0 weight percent.
Claim 7
Dependent Claim
30 words
A method of making flexible urethane foams according to claim 2, wherein the blend ratio of polyolefinic polyol to polyoxyalkylene polyether polyol being in the range between 80/20 to 70/30.
Claim 8
Dependent Claim
26 words
A method of making flexible urethane foams according to claim 2, wherein the polyolefinic polyol is polybutadiene, having a molecular weight of about 1,000 to 5,000.
Claim 9
Dependent Claim
27 words
A method of making flexible urethane foam according to claim 2, wherein the polyolefinic polyol is hydrogenated polybutadiene having a molecular weight of about 1,000 to 5,000.
Claim 10
Dependent Claim
29 words
A method of making flexible urethane foam according to claim 2, wherein the polyisocyanate is a liquefied 4, 4'-diphenylmethane diisocyanate having an isocyanate equivalent of about 130 to 190.
Claim 11
Dependent Claim
17 words
A method of making flexible urethane foams according to claim 2, wherein the blowing agent is water.
References Cited (Backward Citations)
US4067759A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-06-21 | 1991-12-21 | 1992-06-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-06-21 | 1995-12-21 | 1996-06-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-06-21 | 1999-12-21 | 2000-06-21 | $7700.00 | Window Closed / Lapsed |