Modified carboxyl-containing polyphenylene ether resins
Assignee: BASF SE
•
Filing: 1986-11-12
•
Granted: 1988-06-14
•
Expires: 2006-11-12
Abstract
Abstract A process for the preparation of modified polyphenylene ether resins by grafting fumaric acid, preferably at from 270° to 350° C., onto polyphenylene ethers which are mixed with vinylaromatic polymers, and modified polyphenylene ether resins consisting of from 4.95 to 95 parts by weight of polyphenylene ether, from 95 to 4.95 parts by weight of vinylaromatic polymer and from 0.05 to 10 parts by weight of grafted fumaric acid.
Inventors
- 👤 Christof Taubitz
- 👤 Erhard Seiler
- 👤 Lothar Schlemmer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 01:35
CPC Classifications
C; C08; C08F; C08F283/00; C08F283/06; C08F283/08; Y; Y10; Y10S; Y10S525/00; Y10S525/905
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
59 words
In a process for the preparation of a modified polyphenylene ether resin by grafting an olefinically unsaturated compound onto a polyphenylene ether which is mixed with a vinylaromatic polymer, the improvement which consists essentially of using fumaric acid as the olefinically unsaturated compound, which is subjected to graft polymerization in the presence or absence of a free radical initiator.
Claim 2
Dependent Claim
59 words
In a process for the preparation of a modified polyphenylene ether resin by grafting an olefinically unsaturated compound onto a polyphenylene ether which is mixed with a vinylaromatic polymer, the improvement which consists essentially of using fumaric acid as the olefinically unsaturated compound, which is subjected to graft polymerization in the presence or absence of a free radical initiator.
Claim 3
Dependent Claim
16 words
The process of claim 1, wherein graft polymerization is carried out at from 170°to 350° C.
Claim 4
Dependent Claim
29 words
The process of claim 1, wherein graft polymerization is carried out at a polymer melt temperature of above 200° C. and without the addition of a free radical initiator.
Claim 5
Dependent Claim
26 words
The process of claim 1, wherein the graft polymerization ia carried out in a reaction zone of an extruder, which zone is provided with kneading elements.
Claim 6
Dependent Claim
49 words
A modified polyphenlene ether resin prepared by the process of claim 1, and which consists of from 4.95 to 95 parts by weight of polyphenylene ether, from 95 to 4.95 parts by weight of a vinylaromatic polymer and from 0.05 to 10 parts by weight of grafted fumaric acid.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-06-14 | 1991-12-14 | 1992-06-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-06-14 | 1995-12-14 | 1996-06-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-06-14 | 1999-12-14 | 2000-06-14 | $7700.00 | Window Closed / Lapsed |