Preparation of composites
Assignee: BP PLC
•
Filing: 1987-03-26
•
Granted: 1988-06-07
•
Expires: 2007-03-26
Abstract
Abstract This invention relates to metal matrix composites containing at least 40% v/v of a hard material such as SiC and a matrix of aluminium, magnesium or alloys of either. The invention also covers a method of making such composites by ball milling powders of the respective components. Other mixing techniques do not enable such a high proportion of hard material to be incorporated into the composite. The composites are useful to produce components resistant to wear.
Inventors
- 👤 Alan R. Begg
- 👤 Andrew D. Tarrant
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 20:18
CPC Classifications
C; C22; C22C; C22C29/00; C22C29/02; C22C29/06; C22C29/067; C22C1/00; C22C1/04; C22C1/05; C22C47/00; C22C47/14
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
83 words
A method for preparing metal matrix composites comprising at least 40% v/v of a hard material selected from silicon carbides, silicon nitrides, silicon oxides, boron carbides, boron nitrides and boron oxides, and a lightweight component selected from aluminum, magnesium and alloys of either, the method comprising intimately mixing using a high energy milling technique a powder of the hard material and either aluminum or magnesium in its powder form to produce a uniform powder mixture and compacting the powder mixture at elevated temperatures.
Claim 2
Independent Claim
83 words
A method for preparing metal matrix composites comprising at least 40% v/v of a hard material selected from silicon carbides, silicon nitrides, silicon oxides, boron carbides, boron nitrides and boron oxides, and a lightweight component selected from aluminum, magnesium and alloys of either, the method comprising intimately mixing using a high energy milling technique a powder of the hard material and either aluminum or magnesium in its powder form to produce a uniform powder mixture and compacting the powder mixture at elevated temperatures.
Claim 3
Dependent Claim
31 words
A method according to claim 1 wherein the lightweight component is either a pure aluminium or magnesium metal or an alloy containing at least 70% by weight of aluminium or magnesium.
Claim 4
Dependent Claim
33 words
A method according to claim 1 wherein the composites are prepared from a powder of the hard material which contains less than about 20% by weight of fibres or whiskers of that material.
Claim 5
Dependent Claim
44 words
A method according to claim 1 wherein the powders of the hard material and aluminium, magnesium or alloys of either are intimately mixed in a high energy milling apparatus selected from a ball mill, a swing grinding mill (teamer mill) and an attritor mill.
Claim 6
Dependent Claim
42 words
A method according to claim 1 wherein the hard material powder has an average particle size of less than 50 microns and the powder of aluminium, magnesium or an alloy of either has an average particle size of less than 100 microns.
Claim 7
Dependent Claim
22 words
A method according to claim 1 wherein the powder mix contains the hard material in concentrations from 45% to 80% by volume.
Claim 8
Dependent Claim
21 words
A method according to claim 1 wherein the intimately mixed powder is uniformly compacted at elevated temperatures by hot isostatic pressing.
Claim 9
Dependent Claim
17 words
A method according to claim 7 wherein the hot isostatic pressing is used after degassing the system.
Claim 10
Dependent Claim
41 words
A method according to claim 8 wherein the degassed material is subjected to hot isostatic pressing at a temperature from 500°-560° C. and a pressure of at least 15,000 psi e.g. 30,000 psi for a duration of at least 1 hour.
References Cited (Backward Citations)
US2568157A
Cited
US2793949A
Cited
US2894319A
Cited
US3239319A
Cited
US3725015A
Cited
US3828417A
Cited
US3877884A
Cited
JPS5083207A
Cited
US4012204A
Cited
US4060412A
Cited
US4557893A
Cited
US4664704A
Cited
US4624705A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-06-07 | 1991-12-07 | 1992-06-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-06-07 | 1995-12-07 | 1996-06-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-06-07 | 1999-12-07 | 2000-06-07 | $7700.00 | Window Closed / Lapsed |