Non destructive testing for creep damage of a ferromagnetic workpiece
Assignee: Siemens Energy Inc
•
Filing: 1987-01-12
•
Granted: 1988-05-24
•
Expires: 2007-01-12
Abstract
Abstract Rapid nondestructive testing of a ferromagnetic workpiece for creep damage is carried out by placing an eddy current coil adjacent to the workpiece, passing an alternating current through the coil, measuring the eddy current response as influenced by the workpiece, and comparing the current measurement to a current calibrated to known creep damage for the given ferromagnetic material. Correlations of the eddy current response to creep rate and time to failure are generated from creep rupture tests performed on specimens of the given material subjected to varying conditions of time, temperature and stress. Qualitative tests can also be performed to identify the point of greatest creep damage by passing the eddy current coil over the workpiece to find the location of the lowest eddy current response. Conventional creep damage tests can then be performed at that location if desired.
Inventors
- 👤 Michael J. Metala
- 👤 William G. Clark, Jr.
- 👤 Warren R. Junker
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 11:49
CPC Classifications
G; G01; G01N; G01N27/00; G01N27/60; G01N27/72; G01N27/82; G01N27/90; G01N27/9046
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
88 words
A method of determining creep damage in a ferromagnetic workpiece, said method comprising the steps of: placing an eddy current coil adjacent to the ferromagnetic workpiece which has been previously subjected to a prolonged period of stress at elevated temperature; applying an alternating current signal to said eddy current coil to induce eddy currents in the ferromagnetic workpiece; measuring the current passing through said coil as influenced by said workpiece; and comparing said current measurement with a current calibrated to known creep damage to determine the creep damage.
Claim 2
Independent Claim
88 words
A method of determining creep damage in a ferromagnetic workpiece, said method comprising the steps of: placing an eddy current coil adjacent to the ferromagnetic workpiece which has been previously subjected to a prolonged period of stress at elevated temperature; applying an alternating current signal to said eddy current coil to induce eddy currents in the ferromagnetic workpiece; measuring the current passing through said coil as influenced by said workpiece; and comparing said current measurement with a current calibrated to known creep damage to determine the creep damage.
Claim 3
Dependent Claim
25 words
The method of claim 1 including the step of applying a magnetic bias to said workpiece while the current in said coil is being measured.
Claim 4
Independent Claim
210 words
A method of non-destructive testing of a workpiece composed of a selected ferromagnetic material for creep damage comprising the steps of: (a) successively placing an eddy current coil adjacent a selected location on the surface of calibration specimens composed of said selected ferromagnetic material each of which specimen has been previously subjected to different conditions of mechanical stress and elevated temperature; (b) supplying an alternating current to the eddy current coil to induce eddy currents in the specimens; (c) measuring the current passing through said eddy current coil as influenced by said specimens; (d) independently determining the amount of creep damage to each specimen at the selected locations; (e) generating correlations for said selected ferromagnetic material between measured current through the eddy current coil and creep damage; (f) placing said eddy current coil adjacent a selected location on the surface of said workpiece; (g) supplying an alternating current to said eddy current coil to induce eddy currents in said workpiece; (h) measuring the current passing through said eddy current coil as influenced by said workpiece; and (i) determining the measure of creep damage at the selected location on the workpiece from the measurement of the current in the eddy current coil as influenced by said workpiece and from said correlations.
Claim 5
Independent Claim
210 words
A method of non-destructive testing of a workpiece composed of a selected ferromagnetic material for creep damage comprising the steps of: (a) successively placing an eddy current coil adjacent a selected location on the surface of calibration specimens composed of said selected ferromagnetic material each of which specimen has been previously subjected to different conditions of mechanical stress and elevated temperature; (b) supplying an alternating current to the eddy current coil to induce eddy currents in the specimens; (c) measuring the current passing through said eddy current coil as influenced by said specimens; (d) independently determining the amount of creep damage to each specimen at the selected locations; (e) generating correlations for said selected ferromagnetic material between measured current through the eddy current coil and creep damage; (f) placing said eddy current coil adjacent a selected location on the surface of said workpiece; (g) supplying an alternating current to said eddy current coil to induce eddy currents in said workpiece; (h) measuring the current passing through said eddy current coil as influenced by said workpiece; and (i) determining the measure of creep damage at the selected location on the workpiece from the measurement of the current in the eddy current coil as influenced by said workpiece and from said correlations.
Claim 6
Dependent Claim
26 words
The method of claim 3 including the steps of: applying a constant biasing magnetic field to said selected locations on said specimens and on said workpiece.
Claim 7
Dependent Claim
62 words
The method of claim 3 wherein said step of independently determining the amount of creep damage to each specimen comprises; performing a creep rupture test on the specimen and calculating therefrom the creep damage in terms of the creep rate, and wherein the step of generating said correlations comprises correlating the eddy current measurements with the calculated creep rate for each specimen.
Claim 8
Dependent Claim
60 words
The method of claim 3 wherein said step of independently determining the amount of creep damage to each specimen comprises; performing a creep rupture test on the specimen; and calculating therefrom the time to failure of said specimen, and wherein the step of generating said correlations comprises correlating the eddy current measurement with the time to failure for each specimen.
Claim 9
Independent Claim
120 words
A method of determining the location of greatest creep damage in a ferromagnetic workpiece comprising the steps of: (a) placing an eddy current coil adjacent a selected location on the surface of a ferromagnetic workpiece which has been previously subjected to stress during prolonged periods of elevated temperature; (b) applying an alternating current to said eddy current coil to induce eddy currents in said workpiece; (c) measuring the current in said eddy current coil influenced by said workpiece; (d) repeating steps a, b, and c for at least one other selected location on the surface of the workpiece; (e) identifying the selected location at which the lowest eddy current response is measured as the location of the greatest creep damage.
Claim 10
Independent Claim
120 words
A method of determining the location of greatest creep damage in a ferromagnetic workpiece comprising the steps of: (a) placing an eddy current coil adjacent a selected location on the surface of a ferromagnetic workpiece which has been previously subjected to stress during prolonged periods of elevated temperature; (b) applying an alternating current to said eddy current coil to induce eddy currents in said workpiece; (c) measuring the current in said eddy current coil influenced by said workpiece; (d) repeating steps a, b, and c for at least one other selected location on the surface of the workpiece; (e) identifying the selected location at which the lowest eddy current response is measured as the location of the greatest creep damage.
Claim 11
Independent Claim
18 words
The method of 7 including the step of performing a quantitive creep damage test at said identified location.
Claim 12
Independent Claim
18 words
The method of 7 including the step of performing a quantitive creep damage test at said identified location.
Claim 13
Dependent Claim
29 words
The method of claim 8 including the additional step of applying a biasing magnetic field to said workpiece at said selected locations while said current measurements are being made.
References Cited (Backward Citations)
US3427872A
Cited
US4460869A
Cited
US4418315A
Cited
US4533095A
Cited
US4599563A
Cited
US4528856A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-05-24 | 1991-11-23 | 1992-05-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-05-24 | 1995-11-23 | 1996-05-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-05-24 | 1999-11-23 | 2000-05-24 | $7700.00 | Window Closed / Lapsed |