Hydrolytic process for the preparation of a melt stable polycaprolactam
Assignee: Stamicarbon BV
•
Filing: 1986-06-16
•
Granted: 1988-05-24
•
Expires: 2006-06-16
Abstract
Abstract The invention relates to a process for the preparation of a caprolactam that is not appreciably subject to re-equilibration during melt spinning of textile fibres. In the process such an amount of chain length regulating agent is used that the relative viscosity of the polyamide increases by not more than 0.5 units after 20 hour heat treatment in the solid phase in an inert gas atmosphere at between 110 DEG C. and 190 DEG C., after extraction.
Inventors
- 👤 Christiaan Nap
- 👤 Robert Kirschbaum
- 👤 Pierre J. Franssen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 13:29
CPC Classifications
C; C08; C08L; C08L77/00; C08L77/02; C08G; C08G69/00; C08G69/02; C08G69/08; C08G69/14; C08G69/16
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
139 words
A process for the preparation of a melt-stable polyamide for the melt spinning of textile yarn comprising, polymerizing E-caprolactam monomer in the presence of water and a chain length regulating agent, to form a polycaprolactam; solidifying said polycaprolactam, then extracting and drying said polycaprolactam; and subjecting the dried polycaprolactam to a heat treatment wherein said heat treatment is conducted at a temperature from about 110° to about 190° C., and in an inert gas atmosphere or under a vacuum for a period between about 2 and about 20 hours; and wherein said chain length regulating agent is present in an amount whereby the relative viscosity of the polyamide, measured on a solution of 1 g polymer in 100 ml 96 wt% sulphuric acid in water at 25° C., increases by not more than 0.5 unit during said heat treatment.
Claim 2
Dependent Claim
139 words
A process for the preparation of a melt-stable polyamide for the melt spinning of textile yarn comprising, polymerizing E-caprolactam monomer in the presence of water and a chain length regulating agent, to form a polycaprolactam; solidifying said polycaprolactam, then extracting and drying said polycaprolactam; and subjecting the dried polycaprolactam to a heat treatment wherein said heat treatment is conducted at a temperature from about 110° to about 190° C., and in an inert gas atmosphere or under a vacuum for a period between about 2 and about 20 hours; and wherein said chain length regulating agent is present in an amount whereby the relative viscosity of the polyamide, measured on a solution of 1 g polymer in 100 ml 96 wt% sulphuric acid in water at 25° C., increases by not more than 0.5 unit during said heat treatment.
Claim 3
Dependent Claim
19 words
The process of claim 1, wherein the relative viscosity of the polycaprolactam increases by not more than 0.4 unit.
Claim 4
Dependent Claim
19 words
The process of claim 1, wherein the relative viscosity of the polycaprolactam increases by not more than 0.3 unit.
Claim 5
Dependent Claim
19 words
The process of claim 1, wherein the heat treatment is continued until the relative viscosity reaches a constant value.
Claim 6
Dependent Claim
23 words
The process of claim 1, wherein the relative viscosity of the polycaprolactam after the heat treatment is from about 2.1 to about 2.65.
Claim 7
Dependent Claim
24 words
The process according to claim 5, wherein the relative viscosity of the polycaprolactam after the heat treatment is from about 2.2 to about 2.5.
Claim 8
Dependent Claim
19 words
The process of claim 1, wherein the chain length regulating agent is a monocarboxylic acid or a monofunctional amine.
Claim 9
Dependent Claim
16 words
The process according to claim 7, wherein the chain length regulating agent is a monocarboxylic acid.
Claim 10
Dependent Claim
16 words
The process according to claim 8, wherein the monocarboxylic acid is benzoic acid or acetic acid.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-05-24 | 1991-11-23 | 1992-05-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-05-24 | 1995-11-23 | 1996-05-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-05-24 | 1999-11-23 | 2000-05-24 | $7700.00 | Window Closed / Lapsed |