Assignee: Webco Ltd
•
Filing: 1987-07-06
•
Granted: 1988-05-17
•
Expires: 2007-07-06
Abstract
Abstract A method for producing pipeline having a thermally insulating coating in which a continuous matrix of water-impermeable material has dispersed throughout it hollow microspheres or cellular particles which improve on heat insulating properties of the basic matrix.
Inventors
- 👤 George A. Webster
- 👤 Steven A. Burton
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 07:30
CPC Classifications
F; F16; F16L; F16L59/00; F16L59/02; F16L59/028; F16L58/00; F16L58/02; F16L58/04; F16L58/10; F16L58/1054; F16L58/1063; F16L59/06; F16L59/14; F16L59/143; Y; Y10; Y10S; Y10S138/00; Y10S138/09; Y10T; Y10T428/00; Y10T428/13; Y10T428/1352; Y10T428/1355; Y10T428/1359; Y10T428/1379; Y10T428/249921; Y10T428/249953; Y10T428/249971; Y10T428/249972
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
109 words
A method for producing a conduit having a thermally insulating, resilient, water impermeable coating comprising the steps of: providing a mould around a conduit; supplying to said mould a mixture of chemicals which are capable of reacting chemically together to form a thermally insulating, resilient, water impermeable material, said mixture having dispersed therein a plurality of discrete units of which at least a portion is hollow; providing conditions in said mould to cause chemical reaction between said chemicals throughout said mould thereby to form said thermally insulating, resilient, water impermeable material containing said discrete units dispersed therein; removing said thermally insulating, resilient, water impermeable covered conduit from said mould.
Claim 2
Independent Claim
109 words
A method for producing a conduit having a thermally insulating, resilient, water impermeable coating comprising the steps of: providing a mould around a conduit; supplying to said mould a mixture of chemicals which are capable of reacting chemically together to form a thermally insulating, resilient, water impermeable material, said mixture having dispersed therein a plurality of discrete units of which at least a portion is hollow; providing conditions in said mould to cause chemical reaction between said chemicals throughout said mould thereby to form said thermally insulating, resilient, water impermeable material containing said discrete units dispersed therein; removing said thermally insulating, resilient, water impermeable covered conduit from said mould.
Claim 3
Dependent Claim
27 words
The method as set forth in claim 1 wherein said chemicals adapted to react together to form said thermally insulating, resilient, water impermeable material are polyurethane monomers.
Claim 4
Dependent Claim
16 words
The method as set forth in claim 2 wherein said polyurethane monomers are isocyanate and polyol.
Claim 5
Dependent Claim
22 words
The method as set forth in claim 1 wherein said discrete hollow units are microspheres approximately 10 to 100 microns in size.
Claim 6
Dependent Claim
14 words
The method as set forth in claim 4 wherein said microsphere walls are polyvinylidiene.
Claim 7
Dependent Claim
21 words
The method as set forth in claim 1 further including the step of thermosetting said thermally insulating, resilient, water impermeable material.
Claim 8
Dependent Claim
26 words
The method as set forth in claim 1 wherein said conduit is provided with a corrosion resistant coating prior to providing said mould around said conduit.
Claim 9
Dependent Claim
16 words
The method as set forth in claim 7 wherein said corrosion resistant coating is thermoset neoprene.
Claim 10
Independent Claim
212 words
A method for producing a conduit having a thermally insulating, resilient, water impermeable coating comprising the steps of: preparing the surface of said conduit comprising the steps of cleaning the surface of said conduit by shotblasting and applying a coat of primer to said surface; applying to said prepared conduit surface a continuous layer of polychloroprene spirally wrapped around the surface of said conduit and securing said material firmly in place about said conduit surface by tightly winding nylon tape over said material; heating said conduit and its wrappings at 150° C. and 60 psi sufficient to vulcanize said polychloroprene onto said conduit surface; removing said nylon tape; placing said cured polychloroprene conduit into an injection mould; injecting a mixture of polyol and isocyanate monomers into said mould, wherein at least one of said monomers contains dispersed therein a plurality of hollow, gas filled microspheres and wherein said monomers are adapted to react together to form a thermally insulating, resilient polyurethane coating on the surface of said cured polychloroprene covered conduit; allowing said chemicals to react in said injection mould and to form said thermally insulating, resilient coating; allowing said thermally insulating, resilient coating to cure for a predetermined period of time; removing said resilient, water impermeable covered conduit from said mould.
Claim 11
Independent Claim
212 words
A method for producing a conduit having a thermally insulating, resilient, water impermeable coating comprising the steps of: preparing the surface of said conduit comprising the steps of cleaning the surface of said conduit by shotblasting and applying a coat of primer to said surface; applying to said prepared conduit surface a continuous layer of polychloroprene spirally wrapped around the surface of said conduit and securing said material firmly in place about said conduit surface by tightly winding nylon tape over said material; heating said conduit and its wrappings at 150° C. and 60 psi sufficient to vulcanize said polychloroprene onto said conduit surface; removing said nylon tape; placing said cured polychloroprene conduit into an injection mould; injecting a mixture of polyol and isocyanate monomers into said mould, wherein at least one of said monomers contains dispersed therein a plurality of hollow, gas filled microspheres and wherein said monomers are adapted to react together to form a thermally insulating, resilient polyurethane coating on the surface of said cured polychloroprene covered conduit; allowing said chemicals to react in said injection mould and to form said thermally insulating, resilient coating; allowing said thermally insulating, resilient coating to cure for a predetermined period of time; removing said resilient, water impermeable covered conduit from said mould.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-05-17 | 1991-11-16 | 1992-05-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-05-17 | 1995-11-16 | 1996-05-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-05-17 | 1999-11-16 | 2000-05-17 | $7700.00 | Window Closed / Lapsed |