Method for producing silicone rubber powder
Assignee: DuPont Toray Specialty Materials KK
•
Filing: 1987-09-14
•
Granted: 1988-05-10
•
Expires: 2007-09-14
Abstract
Abstract Cured silicone rubber in the form of a finely divided powder is prepared by (1) dispersing a heat-curable liquid silicone rubber composition in water maintained at a temperature of from 0° to 25° C., (2) dispersing the resultant dispersion in a liquid heated to a temperature of at least 50° C., and (3) recovering the resultant cured powder. The liquid silicone rubber composition is preferably maintained at a temperature of from -60° to 0° C. before being emulsified and said liquid is preferably water.
Inventors
- 👤 Keiji Yoshida
- 👤 Koji Shimizu
- 👤 Mitsuo Hamada
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 11:24
CPC Classifications
C; C08; C08J; C08J3/00; C08J3/02; C08J3/03; C08J3/12; C08J3/16; C08J3/24; C08J3/26; C08J2383/00; C08J2383/04
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
91 words
A method for preparing a finely divided cured silicone rubber powder exhibiting a volume resistivity greater than 10 13 ohm-cm, said method comprising (1) forming a dispersion of a heat-curable liquid silicone rubber composition in water maintained at a temperature of from 0° to 25° C. and in the absence of surfactants, (2) dispersing the resultant dispersion into a liquid maintained at a temperature of at least 50° C. to obtain said cured silicone rubber in the form of said finely divided powder, and (3) isolating said powder from said liquid.
Claim 2
Independent Claim
91 words
A method for preparing a finely divided cured silicone rubber powder exhibiting a volume resistivity greater than 10 13 ohm-cm, said method comprising (1) forming a dispersion of a heat-curable liquid silicone rubber composition in water maintained at a temperature of from 0° to 25° C. and in the absence of surfactants, (2) dispersing the resultant dispersion into a liquid maintained at a temperature of at least 50° C. to obtain said cured silicone rubber in the form of said finely divided powder, and (3) isolating said powder from said liquid.
Claim 3
Dependent Claim
68 words
A method according to claim 1 where said composition cures by either (1) a platinum catalyzed addition reaction between an organopolysiloxane containing at least two lower alkenyl radicals per molecule and an organohydrogenpolysiloxane containing at least two silicon bonded hydrogen atoms per molecule, or (2) a free radical initiated polymerization of an organopolysiloxane containing at least two vinyl radicals per molecule in the presence of an organic peroxide.
Claim 4
Dependent Claim
57 words
A method according to claim 2 where said composition cures by said platinum catalyzed addition reaction, the sum of the number of silicon bonded hydrogen atoms and the number of silicon bonded lower alkenyl radicals present in said curable composition is at least 5, said organopolysiloxane is a dimethylvinylsiloxy terminated dimethylpolysiloxane and said organohydrogenpolysiloxane is a methylhydrogenpolysiloxane.
Claim 5
Dependent Claim
42 words
A method according to claim 1 where the curable liquid silicone rubber composition is maintained at a temperature of from -30° to 0° C. before being dispersed in said water and the temperature of said water is from 0° to +5° .
Claim 6
Dependent Claim
40 words
A method according to claim 1 where the liquid into which said dispersion is dispersed is water at a temperature of at least 80° C. and the volume of said liquid is at least twice the volume of said dispersion.
References Cited (Backward Citations)
US4594134A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-05-10 | 1991-11-09 | 1992-05-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-05-10 | 1995-11-09 | 1996-05-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-05-10 | 1999-11-09 | 2000-05-10 | $7700.00 | Window Closed / Lapsed |