Alloy having variable spectral reflectance and information recording material making use of the same
Assignee: Hitachi Ltd
•
Filing: 1985-12-02
•
Granted: 1988-05-10
•
Expires: 2005-12-02
Abstract
Abstract An alloy having variable spectral reflectance having a composition which essentially consists of Ag, 30 to 46 wt % of Zn and 0.1 to 15 wt % in total of at least one element selected from elements of groups Ia, IIa, Iva, Va, VIa, VIIa, VIII, Ib to Vb and rare earth elements, the alloy being able to have different crystal structures, one of which is obtained when it is held in solid state at a first temperature above the room temperature, another of which is obtained when the same is held in the solid state at a second temperture lower than said first temperature. Disclosed also is an information recording medium made of the alloy. The alloy exhibits a reversible change in color or spectral reflectance as a result of change between two crystal phases, so that the information recording medium produced from this alloy can be used effectively as the medium for recording, regeneration and erasion of the informations.
Inventors
- 👤 Hisashi Ando
- 👤 Tetsuro Minemura
- 👤 Isao Ikuta
- 👤 Yosimi Katou
- 👤 Mituo Nakamura
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 18:24
CPC Classifications
C; C22; C22C; C22C30/00; C22C30/06; C22C5/00; C22C5/06; G; G11; G11B; G11B7/00; G11B7/24; G11B7/241; G11B7/242; G11B7/243; G11B2007/24302; G11B2007/24304; G11B2007/24308; G11B7/004; G11B7/0045; G11B7/00454; Y; Y10; Y10S; Y10S430/00; Y10S430/146; Y10S430/165
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
131 words
An information recording medium made of an alloy with variable spectral reflectance having a composition which consists essentially of 30 to 46 wt % of Zn, not greater than 15 wt % in total of at least one element selected from the group consisting of Mg, Ti, V, Cr, Fe, Al, Sn, Y, In, Cu, Sm and Ga, and the balance Ag and incidental impurities, said alloy being able to have different crystal structures at room temperature, one of said different crystal structures being obtained at room temperature after being held in the solid state at a first temperature above the room temperature, and another of said different crystal structures being obtained at room temperature after being held in the solid state at a second temperature lower than said first temperature.
Claim 2
Dependent Claim
131 words
An information recording medium made of an alloy with variable spectral reflectance having a composition which consists essentially of 30 to 46 wt % of Zn, not greater than 15 wt % in total of at least one element selected from the group consisting of Mg, Ti, V, Cr, Fe, Al, Sn, Y, In, Cu, Sm and Ga, and the balance Ag and incidental impurities, said alloy being able to have different crystal structures at room temperature, one of said different crystal structures being obtained at room temperature after being held in the solid state at a first temperature above the room temperature, and another of said different crystal structures being obtained at room temperature after being held in the solid state at a second temperature lower than said first temperature.
Claim 3
Dependent Claim
40 words
An information recording medium according to claim 1, wherein said alloy has a composition which consists essentially of 30 to 46 wt % of Zn, not greater than 10 wt % of In, and the balance Ag and incidental impurities.
Claim 4
Dependent Claim
39 words
An information recording medium according to claim 1, wherein said alloy has a composition which consists essentially of 30 to 46 wt % of Zn, 0.5 to 2.0 wt % of Cu, and the balance Ag and incidental impurities.
Claim 5
Dependent Claim
40 words
An information recording medium according to claim 1, wherein said alloy has a composition which consists essentially of 30 to 46 wt % of Zn, 0.1 to 3.0 wt % of Ga, and the balance of Ag and incidental impurities.
Claim 6
Dependent Claim
24 words
An information recording medium according to claim 11, wherein said alloy has the form of a thin film, foil, strip, powder or thin wire.
Claim 7
Dependent Claim
58 words
An information recording medium according to claim 1, wherein said composition consists essentially of 30 to 46 wt % of Zn, 0.1 to 15 wt % total of at least one element selected from the group consisting of Mg, Ti, V, Cr, Fe, Al, Sn, Y, In, Cu, Sm and Ga, and the balance Ag and incidental impurities.
Claim 8
Dependent Claim
21 words
An information recording medium according to claim 1 wherein said alloy has a crystal grain size not greater than 0.1 μm.
Claim 9
Dependent Claim
39 words
An information recording medium according to claim 1 wherein said alloy has a composition which consists essentially of 30 to 46 wt % of Zn, 0.5 to 8.0 wt % of Sm, and the balance Ag and incidental impurities.
References Cited (Backward Citations)
JPS5352084A
Cited
JPS57140845A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-05-10 | 1991-11-09 | 1992-05-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-05-10 | 1995-11-09 | 1996-05-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-05-10 | 1999-11-09 | 2000-05-10 | $7700.00 | Window Closed / Lapsed |